Title:
Preparation of PET Chips with Various Intrinsic Viscosity and Study on Processing Characteristics of PET Chips
文章编号:
1673-3851 (2017) 02-0208-06
作者:
袁效东; 马建平; 张先明; 陈文兴
浙江理工大学纺织纤维材料与加工技术国家地方联合工程实验室，杭州 310018
Author(s):
YUAN Xiaodong;  MA Jianping;  ZHANG Xianming;  CHEN Wenxing
National Engineering Laboratory for Textile Fiber Materials and Processing Technology,Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
聚苯二甲酸乙二醇酯(PET); 特性黏度; 流变性能; 加工特性
分类号:
TS102.5
文献标志码:
A
摘要:
以对苯二甲酸和乙二醇为原料，三氧化二锑(Sb2O3)作为催化剂，在1 L缩聚反应釜中制备不同特性黏度的聚对苯二甲酸乙二醇酯(PET)。利用旋转流变仪对样品的流变性能进行了对比，讨论特性黏度、剪切速率和温度对复数黏度、零切黏度、黏流活化能的影响。结果表明：4组样品均为假塑性流体，复数黏度随剪切速率和温度的增加而降低；随特性黏度的增加，样品零切黏度、黏流活化能也逐渐增大。

参考文献/References:

［1］ LIANGBIN L, RUI H, LING Z, et al. A new mechanism in the formation of PET extendedchain crystal［J］. Polymer,2001,42(5):2085-2089.
［2］ 韩亚东.PET树脂的生产现状及其发展趋势［J］.塑料工业,1988(6):4-8.
［3］ 张师民.聚酯的生产及应用［M］.北京:中国石化出版社,1997:295-296.
［4］ 王志远,陈福林,张兴华.国内PET改性研究的最新进展［J］.聚酯工业,2006,19(3):1-4.
［5］ 张义盛,吴德峰,曹健,等.PET/PP共混体系的熔融及非等温结晶行为［J］.塑料科技,2007,35(1):28-31.
［6］ COLIN X, VERDU J. Polymer degradation during processing［J］. Comptes Rendus Chimie,2006,9(11):1380-1395.
［7］ ASSADI R, COLIN X, VERDU J. Irreversible structural changes during PET recycling by extrusion［J］. Polymer,2004,45(13):4403-4412.
［8］ HARTH M, KASCHTA J, SCHUBERT D W. Shear and elongational flow properties of longchain branched poly (ethylene terephthalates) and correlations to their molecular structure［J］. Macromolecules,2014,47(13):4471-4478.［9］ SANCHEZSOLIS A, CALDERAS F, MANERO O. Influence of maleic anhydride grafting on the rheological properties of polyethylene terephthalatestyrene butadiene blends［J］. Polymer,2001,42(17):7335-7342.
［10］ CHEN S C, ZHANG X M, LIU M, et al. Rheological characterization and thermal stability of different intrinsic viscosity poly (ethylene terephthalate) in air and nitrogen［J］. International Polymer Processing,2016,31(3):292-300.

相似文献/References:

[1]孙亚芳,陈世昌,马建平,等.PET固相缩聚工艺与反应动力学机理研究[J].浙江理工大学学报,2017,37-38(自科2):226.
　SUN Yafang,CHEN Shichang,MA Jianping,et al.Studies on Solidstate Polymerization of PET and Reaction Kinetics Mechanism[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科2):226.
[2]赵梦肖,包建娜,王 滢,等.PET环状低聚物在高黏熔体中的开环聚合反应规律[J].浙江理工大学学报,2022,47-48(自科二):211.
　ZHAO Mengxiao,BAO Jianna,WANG Ying,et al.Reaction law of ring opening polymerization of PET cyclic oligomer in high viscosity melt[J].Journal of Zhejiang Sci-Tech University,2022,47-48(自科2):211.

备注/Memo

备注/Memo:
收稿日期： 2016-08-01
网络出版日期：2017-01-03
基金项目： 国家重点研发计划项目（2016YFB0303002）
作者简介： 袁效东（1993-），男，安徽阜阳人，硕士研究生，主要从事聚酯合成与加工方面的研究
通信作者： 张先明，E-mail：zhangxm@zstu.edu.cn
更新日期/Last Update: 2017-04-05