|本期目录/Table of Contents|

[1]张亚,陈维国,王成龙,等.数码印花用涤纶非织造布聚丙烯酸酯涂层的制备及其性能[J].浙江理工大学学报,2020,43-44(自科四):464-471.
　ZHANG Ya,CHEN Weiguo,WANG Chenglong,et al.Preparation and performance of polyester nonwoven polyacrylate coating for digital printing[J].Journal of Zhejiang Sci-Tech University,2020,43-44(自科四):464-471.
点击复制

数码印花用涤纶非织造布聚丙烯酸酯涂层的制备及其性能()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第43-44卷
期数:
2020年自科四期
页码:
464-471
栏目:
出版日期:
2020-07-10

文章信息/Info

Title:
Preparation and performance of polyester nonwoven polyacrylate coating for digital printing
文章编号:
1673-3851 (2020) 07-0464-08
作者:
张亚; 陈维国; 王成龙; 崔志华; 郑今欢
浙江理工大学，a. 生态染整技术教育部工程研究中心；b. 先进纺织材料与制备技术教育部重点实验室，杭州 310018
Author(s):
ZHANG Ya;  CHEN Weiguo;  WANG Chenglong;  CUI Zhihua;  ZHENG Jinhuan
a. Engineering Research Center for EcoDyeing and Finishing of Textiles, Ministry of Education; b. Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
涤纶; 非织造布; 聚丙烯酸酯; 涂层; 数码印花
分类号:
TS193-5
文献标志码:
A
摘要:
在聚丙烯酸酯乳液中加入具有增白效果的高岭土填料制成涂层用浆料，然后对涤纶针刺基布进行涂层整理，通过研究涂层浆体系各组分用量及涂层工艺对涂层材料耐折力、附着力、断裂强力及表面性能等的影响，确定最佳涂层浆配方及涂层工艺，从而制备适用于数码喷墨印花的涤纶非织造布涂层材料。结果表明：当分散剂CF10用量为03 wt%，交联剂SAC100用量为03 wt%，聚丙烯酸酯涂层剂用量为200 wt%，涂层剂与高岭土质量比为1∶4时，可以制备得到性能优良的涂层浆；将所制涂层浆用于非织造布涂层，当后处理焙烘温度为160 ℃，焙烘时间为90 s时，可以制备得到耐折力和附着力好、手感较佳的涂层材料；对制备的涂层材料进行UV数码喷印，所得图案的干摩擦色牢度为4～5级、湿摩擦色牢度为3～4级，图案颜色鲜艳且边缘清晰。该涤纶针刺非织造布涂层材料对于拓展非织造布应用领域具有重要意义。

参考文献/References:

［1］ 陈曙光,孙新增,徐广标. 后整理对丙纶针刺非织造材料表观与孔隙结构的影响［J］. 东华大学学报(自然科学版), 2017, 43(3): 359-363.
［2］ 刘文月,邓炳耀. 数码印花纺粘非织造装饰材料的应用前景探讨［J］. 产业用纺织品, 2010, 28(1): 37-40.
［3］ 王莉,闫新,孙静,等. 非织造布装饰材料喷墨印花技术探析［J］. 纺织导报, 2018(10): 97-99.
［4］ 张红阳,任煜,徐林,等. 常压等离子体辅助涤纶非织造材料表面拒水拒油整理研究［J］. 纺织导报, 2019(4): 26-29.
［5］ 刘太东, 徐长如, 李齐红, 等. 棉/仪纶织物的染整加工［J］. 印染, 2018, 44(13): 32-35.
［6］ 杨西江. 表面活性剂对水性油墨用色浆制备和性能的影响［J］. 染料与染色, 2018, 55(4): 39-42.
［7］ 陈益人. 篷用全棉涂层织物制备及性能研究［D］.上海：东华大学, 2009：43-47.
［8］ 刘金花, 杨斌. 用于墙纸的水刺非织造布涂层工艺的研究［J］. 浙江理工大学学报, 2013, 30(6): 834-837.
［9］ 汤锡铨. 干法涂层技术简介［J］. 塑料科技, 1994, 22(1): 25-26.
［10］ 张剑飞, 王进忠, 李斌, 等. 环氧涂层在金属基材上附着力影响因素探讨［J］. 现代涂料与涂装, 2018, 21(2): 1-4.

相似文献/References:

[1]赵许亮,赵奇才,陈维国.应用有机/无机复合糊料的涤纶分散染料印花热固色研究[J].浙江理工大学学报,2016,35-36(自科4):504.
　ZHAO Xuliang,ZHAO Qicai,CHEN Weiguo.Study on Thermal Fixation of Polyester with Disperse Dye by Applying Organic/Inorganic Composite Paste[J].Journal of Zhejiang Sci-Tech University,2016,35-36(自科四):504.
[2]孟娇,刘妮萍,崔志华,等.可碱洗羧酸异丙酯分散染料AC 1的合成及应用[J].浙江理工大学学报,2017,37-38(自科2):159.
　MENG Jiao,LIU Niping,CUI Zhihua,et al.Synthesis and Application of AlkaliCleaningCarboxylic Acid Isopropyl Ester Disperse Dye[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科四):159.
[3]张丽,江华,崔志华,等.双亚芴基醌式噻吩染料对涤纶的染色性能研究[J].浙江理工大学学报,2018,39-40(自科2):139.
　ZHANG Li,JIANG Hua,CUI Zhihua,et al.Dyeing property of difluorenylidene quinoidal thiophene on polyester[J].Journal of Zhejiang Sci-Tech University,2018,39-40(自科四):139.
[4]张向阳,李成才,朱海霖,等.基于二氧化硅溶胶的聚丙烯非织造布亲水后整理[J].浙江理工大学学报,2020,43-44(自科四):457.
　ZHANG Xiangyang,LI Chengcai,ZHU Hailin,et al.ZHANG Xiangyang, LI Chengcai, ZHU Hailin, HE Yuping, LIU Guojin[J].Journal of Zhejiang Sci-Tech University,2020,43-44(自科四):457.
[5]高雅芳,张耘箫,刘国金,等.光子晶体结构生色纺织品的快速制备及其性能表征[J].浙江理工大学学报,2021,45-46(自科二):157.
　GAO Yafanga,ZHANG Yunxiaoa,LIU Guojina,et al.Rapid preparation and characterization of chromogenic textiles with photonic crystal structure[J].Journal of Zhejiang Sci-Tech University,2021,45-46(自科四):157.
[6]樊莎,李成才,朱海霖,等.防水防油剂的制备及其在非织造布后整理中的应用[J].浙江理工大学学报,2022,47-48(自科二):153.
　FAN Sha,LI Chengcai,ZHU Hailin,et al.Preparation of a water and oil repellent agent and its application in non woven fabric finishing[J].Journal of Zhejiang Sci-Tech University,2022,47-48(自科四):153.
[7]万慧,余培泽,钱涛,等.分散蓝354和分散彩蓝QS-B匀染性的影响因素分析[J].浙江理工大学学报,2023,49-50(自科四):449.
　WAN Hui,YU Peize,QIAN Tao,et al.Analysis of influencing factors on levelness of  Disperse Blue 354 and Disperse Blue QS-B[J].Journal of Zhejiang Sci-Tech University,2023,49-50(自科四):449.
[8]郭丽雪,王成龙,黄俊峰,等.高耐晒染料C.I.分散蓝77与C.I.分散黄54的复配性能分析[J].浙江理工大学学报,2023,49-50(自科四):465.
　GUO Lixue,WANG Chenglong,HUANG Junfeng,et al.Analysis on the compatibility of high light fastness dyes C.I. Disperse Blue 77 and C.I. Disperse Yellow 54[J].Journal of Zhejiang Sci-Tech University,2023,49-50(自科四):465.
[9]潘毕成,张佳文,杨孝全,等.被动式日间辐射制冷超疏水涤纶织物的制备及其性能[J].浙江理工大学学报,2024,51-52(自科一):55.
　PAN Bicheng,ZHANG Jiawen,YANG Xiaoquan,et al.Preparation and performance of superhydrophobic polyester  fabrics for passive daytime radiative cooling[J].Journal of Zhejiang Sci-Tech University,2024,51-52(自科四):55.
[10]段银河,蒋付良,董慧娴,等.交联型氟硅改性聚丙烯酸酯乳胶及其在涤纶织物染色中的应用研究[J].浙江理工大学学报,2024,51-52(自科三):329.
　DUAN Yinhe,JIANG Fuliang,DONG Huixian,et al.Preparation of cross linked fluorosilicone modified polyacrylate latex and its application in dyeing of polyester fabrics[J].Journal of Zhejiang Sci-Tech University,2024,51-52(自科四):329.

备注/Memo

备注/Memo:
收稿日期：2019-10-02
网络出版日期：2020-01-02
基金项目：国家自然科学基金项目（21808210，51673176）
作者简介：张亚（1993-），男，河南周口人，硕士研究生，主要从事织物涂层整理方面的研究
通信作者：陈维国，E-mail：wgchen_62@126.com
更新日期/Last Update: 2020-07-06