[1]闫爱丽,王晟,俞烨,等.碳化纳米纤维负载TiO-2的制备及其光催化性能研究[J].浙江理工大学学报,2017,37-38(自科1):8-13.
　YAN Aili,WANG Sheng,YU Ye,et al.Preparation of TiO-2 Loaded by Carbon Nanofiber and Investigation of Its Photocatalytic Performance[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科1):8-13.
点击复制

碳化纳米纤维负载TiO-2的制备及其光催化性能研究()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第37-38卷
期数:
2017年自科1期
页码:
8-13
栏目:
出版日期:
2017-01-10

文章信息/Info

Title:
Preparation of TiO-2 Loaded by Carbon Nanofiber and Investigation of Its Photocatalytic Performance
文章编号:
1673-3851 (2017) 01-0008-06
作者:
闫爱丽; 王晟; 俞烨; 王騊
1.浙江理工大学先进纺织材料与制备技术教育部重点实验室，杭州 310018；2. 浙江宁波维科精华人丰家纺有限公司，宁波 315821
Author(s):
YAN Aili;  WANG Sheng; YU Ye; WANG Tao
1.Key Laboratory of Advanced Textile Materials and Manufacturing Technology,Ministry of Education, Zhejiang Sci-Tech University, Hangzhou 310018, China；2.Ningbo Weike Jinghua Renfeng Home Textile Co., Ltd., Ningbo 315821, China
关键词:
水热法; 碳化纤维; TiO-2; 光催化
分类号:
O649.1
文献标志码:
A
摘要:
以Te纳米线为模板，葡萄糖为碳源，硫酸氧钛为钛源，采用两步水热法，通过煅烧制备出碳化纳米纤维负载TiO2光催化剂。采用SEM、TEM、EDS、XRD、TG等测试方法对其形貌、结构、晶型、负载量进行表征。TiO2的负载量是通过调节硫酸氧钛的添加量来控制，并以甲基橙为目标污染物，探索TiO2的负载量对光降解甲基橙性能的影响。实验结果表明：随着硫酸氧钛添加量的增加，TiO2负载量先增大，当添加量高于20 mL后负载量几乎不变；碳化纳米纤维负载TiO2光催化剂对甲基橙的光降解随着负载量升高先逐渐增大然后趋于稳定，且负载量在57.63%时降解甲基橙效果最好。

参考文献/References:

［1］ PALMISANO G, AUGUGLIARO V, PAGLIARO M, et al. Photocatalysis：a promising route for 21st century organic chemistry［J］. Chemical Communications,2007(33)：3425-3437.
［2］ 董业硕.微米级负载型TiO2催化剂的制备及其光催化降解特性［D］.天津：天津城建大学,2012：1-38.
［3］ 田维,张洪林,蒋林时.纳米TiO2光催化材料的制备及研究进展［J］.四川有色金属,2007(4)：15-20.
［4］ 沈毅,张青龙,吴国友,等.纳米TiO2光催化材料研究新进展［J］.矿业研究与开发,2006,26(4)：39-43.
［5］ 贺飞,唐怀军.纳米TiO2光催化剂负载技术研究［J］.环境污染治理技术与设备,2001,2(2)：47-58.
［6］ 廖振华,陈建军,姚可夫,等.纳米TiO2光催化剂负载化的研究进展［J］.无机材料学报,2004,19(1)：17-24.
［7］ KIM S, HWANG S J, CHOI W. Visible light active platinumiondoped TiO2 photocatalyst［J］. The Journal of Physical Chemistry B,2005,109(51)：24260-24267.
［8］ 王积森,冯忠彬,孙金全,等.纳米TiO2的光催化机理及其影响因素分析［J］.微纳电子技术,2008,45(1)：28-32.
［9］ 田维,张洪林,蒋林时.纳米TiO2光催化材料的制备及研究进展［J］.四川有色金属,2007(4)：15-20.
［10］ PUMA G L, BONO A, KRISHNAIAH D, et al. Preparation of titanium dioxide photocatalyst loaded onto activated carbon support using chemical vapor deposition：A review paper［J］. Journal of Hazardous Materials,2008,157(2)：209-219.
［11］ VIGIL E, DIXON D, HAMILTON J W J, et al. Deposition of TiO2 thin films on steel using a microwave activated chemical bath［J］. Surface and Coatings Technology,2009,203(23)：3614-3617.
［12］ AAL A A, BARAKAT M A, MOHAMED R M. Electrophoreted ZnTiO 2ZnO nanocomposite coating films for photocatalytic degradation of 2chlorophenol［J］. Applied Surface Science,2008,254(15)：4577-4583.

相似文献/References:

[1]郑贤火,马非凡,王龙成.K+掺杂对Y-2O- 3：Eu 3+粉末发光强度与量子效率的影响[J].浙江理工大学学报,2016,35-36(自科5):691.
　ZHENG Xianhuo,MA Feifan,WANG Longcheng.Effect of K+ Doping on Luminescent Intensity and Quantum Efficiency of Y 2O 3：Eu 3+  Powder[J].Journal of Zhejiang Sci-Tech University,2016,35-36(自科1):691.
[2]余大江,郭绍义,袁永锋,等.水热法高温煅烧处理制备Ni x Co - x MoO 4纳米片阵列/泡沫Ni复合材料及其赝电容性能研究[J].浙江理工大学学报,2016,35-36(自科6):855.
　YU Dajiang,GUO Shaoyi,YUAN Yongfeng,et al.Preparation of Ni xCo 1-x MoO4 Nanosheet Array/Nickel Foam  Composite by Hydrothermal Method and Hightemperature Calcination and Its Pseudocapacitance Performance[J].Journal of Zhejiang Sci-Tech University,2016,35-36(自科1):855.
[3]江珍珍,郑晋生,王晟.核 壳光催化剂Cu-CdS@C-3N-4的制备及其性能研究[J].浙江理工大学学报,2017,37-38(自科1):24.
　JIANG Zhenzhen,ZHENG Jinsheng,WANG Sheng.Preparation of Core Shell Photocatalyst Cu-CdS@C-3N-4  and  Study on Its Performance[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科1):24.
[4]周伟杰,高林辉,王广发.Gd-2Zr-2O-7:Eu 3+ 红色荧光粉的制备及发光性能的研究[J].浙江理工大学学报,2017,37-38(自科2):197.
　ZHOU Weijie,GAO Linhui,WANG Guangfa.Preparation of Gd2Zr2O7:Eu3+ Red Phosphor and Stusy on Its Photoluminescence Property[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科1):197.
[5]杨术莉,邱琳琳,杜平凡.水热法制备TiO-2致密层及其在钙钛矿太阳电池中的应用[J].浙江理工大学学报,2017,37-38(自科4):475.
　YANG Shuli,QIU Linlin,DU Pingfan.Preparation of TiO-2 Compact Layer by Hydrothermal Methodand Its Application in Perovskite Solar Cells[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科1):475.
[6]马非凡,郑贤火,廖世才,等.钾离子对GdBO-3:Tb-3+ 发光性能的影响[J].浙江理工大学学报,2017,37-38(自科4):506.
　MA Feifan,ZHENG Xianhuo,LIAO Shicai,et al.Effect of K+ Doping on Luminescent Property of GdBO-3:Tb-3+ Powder[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科1):506.
[7]魏琦,周彬,杨帆,等.SiO-2/Ag复合微球的制备及光催化性能研究[J].浙江理工大学学报,2017,37-38(自科6):810.
　WEI Qi,ZHOU Bin,YANG Fan,et al.Preparation and Photocatalytic Performance ofSiO-2/Ag Composite Microsphere[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科1):810.
[8]周文翠,马佳慧,杨静,等.间苯二酚 甲醛树脂基碳球的可控制备与应用[J].浙江理工大学学报,2018,39-40(自科2):163.
　ZHOU Wencui,MA Jiahui,YANG Jing,et al.Controllable preparation and application of carbon spheres based on resorcinolformaldehyde resin[J].Journal of Zhejiang Sci-Tech University,2018,39-40(自科1):163.
[9]杜文浩,王一帆,史伊媛,等.水热时间和低温热处理对 δ MnO 2电容性能的影响[J].浙江理工大学学报,2018,39-40(自科3):259.
　DU Wenhao,WANG Yifan,SHI Yiyuan,et al.Effects of hydrothermal time and lowtemperature heat treatment on supercapacitor properties of  δ MnO 2[J].Journal of Zhejiang Sci-Tech University,2018,39-40(自科1):259.
[10]端木佳杰,程睿珊,尹思敏,等.钙钛矿PbTiO3纳米片对金红石相TiO2微纳结构晶体生长的调控[J].浙江理工大学学报,2019,41-42(自科三):314.
　DUANMU Jiajie,CHENG Ruishan,YIN Simin,et al.Regulation of rutile TiO2 micro/nanostructures by the effect of Perovskite PbTiO3 Nanoplates[J].Journal of Zhejiang Sci-Tech University,2019,41-42(自科1):314.

备注/Memo

备注/Memo:
收稿日期： 2016-01-21
网络出版日期： 2016-12-09
基金项目： 国家自然科学基金项目（51372227，51471153）；浙江省自然科学基金项目（LY14E020011，2015C33008)；浙江理工大学“521人才工程”项目
作者简介： 闫爱丽（1989-），女，河南驻马店人，硕士研究生，主要从事纳米催化剂方面的研究
通信作者： 王騊，E-mail：taotao571@hotmail.com
更新日期/Last Update: 2017-02-28