[1]周文翠,马佳慧,杨静,等.间苯二酚 甲醛树脂基碳球的可控制备与应用[J].浙江理工大学学报,2018,39-40(自科2):163-170.
　ZHOU Wencui,MA Jiahui,YANG Jing,et al.Controllable preparation and application of carbon spheres based on resorcinolformaldehyde resin[J].Journal of Zhejiang Sci-Tech University,2018,39-40(自科2):163-170.
点击复制

间苯二酚 甲醛树脂基碳球的可控制备与应用()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第39-40卷
期数:
2018年自科2期
页码:
163-170
栏目:
出版日期:
2018-03-31

文章信息/Info

Title:
Controllable preparation and application of carbon spheres based on resorcinolformaldehyde resin
文章编号:
1673-3851 (2018) 03-0163-08
作者:
周文翠; 马佳慧; 杨静; 贾亚茹; 蔡玉荣
浙江理工大学材料与纺织学院、丝绸学院，杭州 310018
Author(s):
ZHOU Wencui;  MA Jiahui;  YANG Jing;  JIA Yaru;  CAI Yurong
Silk Institute, College of Materials and Textiles, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
水热法; 单分散; RF树脂微球; 碳球
分类号:
TB383
文献标志码:
A
摘要:
以间苯二酚和甲醛为原料，利用预聚合水热处理的两步法制备苯二酚/甲醛树脂（resorcinolformaldehyde resin，RF）微球，考察各反应参数对树脂微球尺寸的影响，并将所制得的树脂微球经高温碳化制得碳球，将碳球用作牺牲模板制备其他中空材料。结果表明：以间苯二酚和甲醛为原材料可制备出单分散且尺寸均匀的树脂微球，其中催化剂的浓度、间苯二酚添加量、预聚合温度、乙醇/水的体积比等均会对所制得的树脂微球的尺寸产生影响；通过选择反应参数，可以使得树脂微球直径在255~1500 nm范围内调整；碳化后的RF树脂微球尺寸略有减小，球形度好，可以用作牺牲模板来制备二氧化锰和氧化锌等中空材料。通过该研究可开发出制备尺寸跨度大且单分散的RF树脂微球的简便方法，所得到的微球可以被转变成单分散碳球，在牺牲模板等领域具有广泛的应用前景。

参考文献/References:

［1］ 任斌.基于碳球模板法的功能型纳米材料的合成与应用［D］.重庆:重庆大学,2016.
［2］ 徐伟,杜芳林.二氧化锰空心微球的制备及表征［J］.青岛科技大学学报,2014,35(1):30-33.
［3］ Wen Z H, Wang Q, Zhang Q, et al. Hollow  carbon spheres with wide size distribution as anode catalyst support for direct methanol fuel cells［J］. Electrochemistry Communications,2007,9(8):1867-1872.
［4］ 罗雯,黄磊,关豆豆,等.空心碳球负载二硫化硒复合材料作为锂离子电池正极材料［J］.物理化学学报,2016,32(8):1999-2006.
［5］ 杨维佳,郝亚敏,闫翊鹏,等.多孔碳微球负载纳米银的制备及抗菌性能［J］.太原理工大学学报,2014,45(3):285-290.
［6］ 林茜颉,吕荣文,曹安民.介孔碳球的制备及其催化性能研究［J］.中国科学:化学,2016,46(10):1126-1130.
［7］ Cheng K, Zhou Y M, Sun Z Y, et al. Synthesis of  carboncoated, porous and waterdispersive Fe3O4 nanocapsules  and their excellent performance for heavy metal removal applications［J］. Dalton Trans,2012,41(1):5854-5861.
［8］ 李雪娜.空心碳球的可控制备及其在CO2吸附领域的研究［D］.北京:北京工业大学,2016.
［9］ 郭燕川,徐海涛,张兵,等.新型酞著高温热解沉积法制备燃料电池专用纳米碳球载铂催化剂［J］.科学通报,2003,48(22):2338-2342.

相似文献/References:

[1]郑贤火,马非凡,王龙成.K+掺杂对Y-2O- 3：Eu 3+粉末发光强度与量子效率的影响[J].浙江理工大学学报,2016,35-36(自科5):691.
　ZHENG Xianhuo,MA Feifan,WANG Longcheng.Effect of K+ Doping on Luminescent Intensity and Quantum Efficiency of Y 2O 3：Eu 3+  Powder[J].Journal of Zhejiang Sci-Tech University,2016,35-36(自科2):691.
[2]余大江,郭绍义,袁永锋,等.水热法高温煅烧处理制备Ni x Co - x MoO 4纳米片阵列/泡沫Ni复合材料及其赝电容性能研究[J].浙江理工大学学报,2016,35-36(自科6):855.
　YU Dajiang,GUO Shaoyi,YUAN Yongfeng,et al.Preparation of Ni xCo 1-x MoO4 Nanosheet Array/Nickel Foam  Composite by Hydrothermal Method and Hightemperature Calcination and Its Pseudocapacitance Performance[J].Journal of Zhejiang Sci-Tech University,2016,35-36(自科2):855.
[3]闫爱丽,王晟,俞烨,等.碳化纳米纤维负载TiO-2的制备及其光催化性能研究[J].浙江理工大学学报,2017,37-38(自科1):8.
　YAN Aili,WANG Sheng,YU Ye,et al.Preparation of TiO-2 Loaded by Carbon Nanofiber and Investigation of Its Photocatalytic Performance[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科2):8.
[4]江珍珍,郑晋生,王晟.核 壳光催化剂Cu-CdS@C-3N-4的制备及其性能研究[J].浙江理工大学学报,2017,37-38(自科1):24.
　JIANG Zhenzhen,ZHENG Jinsheng,WANG Sheng.Preparation of Core Shell Photocatalyst Cu-CdS@C-3N-4  and  Study on Its Performance[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科2):24.
[5]周伟杰,高林辉,王广发.Gd-2Zr-2O-7:Eu 3+ 红色荧光粉的制备及发光性能的研究[J].浙江理工大学学报,2017,37-38(自科2):197.
　ZHOU Weijie,GAO Linhui,WANG Guangfa.Preparation of Gd2Zr2O7:Eu3+ Red Phosphor and Stusy on Its Photoluminescence Property[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科2):197.
[6]杨术莉,邱琳琳,杜平凡.水热法制备TiO-2致密层及其在钙钛矿太阳电池中的应用[J].浙江理工大学学报,2017,37-38(自科4):475.
　YANG Shuli,QIU Linlin,DU Pingfan.Preparation of TiO-2 Compact Layer by Hydrothermal Methodand Its Application in Perovskite Solar Cells[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科2):475.
[7]马非凡,郑贤火,廖世才,等.钾离子对GdBO-3:Tb-3+ 发光性能的影响[J].浙江理工大学学报,2017,37-38(自科4):506.
　MA Feifan,ZHENG Xianhuo,LIAO Shicai,et al.Effect of K+ Doping on Luminescent Property of GdBO-3:Tb-3+ Powder[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科2):506.
[8]魏琦,周彬,杨帆,等.SiO-2/Ag复合微球的制备及光催化性能研究[J].浙江理工大学学报,2017,37-38(自科6):810.
　WEI Qi,ZHOU Bin,YANG Fan,et al.Preparation and Photocatalytic Performance ofSiO-2/Ag Composite Microsphere[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科2):810.
[9]杜文浩,王一帆,史伊媛,等.水热时间和低温热处理对 δ MnO 2电容性能的影响[J].浙江理工大学学报,2018,39-40(自科3):259.
　DU Wenhao,WANG Yifan,SHI Yiyuan,et al.Effects of hydrothermal time and lowtemperature heat treatment on supercapacitor properties of  δ MnO 2[J].Journal of Zhejiang Sci-Tech University,2018,39-40(自科2):259.
[10]端木佳杰,程睿珊,尹思敏,等.钙钛矿PbTiO3纳米片对金红石相TiO2微纳结构晶体生长的调控[J].浙江理工大学学报,2019,41-42(自科三):314.
　DUANMU Jiajie,CHENG Ruishan,YIN Simin,et al.Regulation of rutile TiO2 micro/nanostructures by the effect of Perovskite PbTiO3 Nanoplates[J].Journal of Zhejiang Sci-Tech University,2019,41-42(自科2):314.

备注/Memo

备注/Memo:
收稿日期： 2017-06-01
网络出版日期： 2017-11-09
基金项目： 国家自然科学基金项目（51372226）；浙江省自然科学基金项目（LY16E020013）
作者简介： 周文翠（1991-），山东东营人，硕士研究生，主要从事生物医用材料和生物传感器方面的研究
通信作者： 蔡玉荣，Email:caiyr@zstu.edu.cn
更新日期/Last Update: 2018-03-15