|本期目录/Table of Contents|

[1]陈航,林萍,王朋,等.氯化甲胺对甲胺铅溴钙钛矿单晶的钝化[J].浙江理工大学学报,2023,49-50(自科一):69-77.
　CHEN Hang,LIN Ping,WANG Peng,et al.Passivation of methylamine lead bromide perovskite single crystal by methylamine chloride[J].Journal of Zhejiang Sci-Tech University,2023,49-50(自科一):69-77.
点击复制

氯化甲胺对甲胺铅溴钙钛矿单晶的钝化()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第49-50卷
期数:
2023年自科第一期
页码:
69-77
栏目:
出版日期:
2023-03-10

文章信息/Info

Title:
Passivation of methylamine lead bromide perovskite single crystal by methylamine chloride
文章编号:
1673-3851 (2023) 01-0069-09
作者:
陈航; 林萍; 王朋; 崔灿
浙江理工大学理学院，杭州 310018
Author(s):
CHEN Hang;  LIN Ping;  WANG Peng;  CUI Can
School of Science, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
甲胺铅溴; 钙钛矿单晶; 氯化甲胺; 钝化; 光电探测器
分类号:
TB33
文献标志码:
A
摘要:
为了减少甲胺铅溴(MAPbBr3)钙钛矿单晶的表面缺陷以提高其光电性能，采用氯化甲胺(MACl)的异丙醇溶液对机械打磨后的MAPbBr3单晶进行钝化。通过扫描电子显微镜(SEM)、光致发光谱（PL）、时间分辨光致发光衰减谱(TRPL)、X射线衍射图谱（XRD）、X射线光电子能谱（XPS）和紫外光电子能谱（UPS）对MACl钝化后的MAPbBr3单晶的结构与形貌进行表征和分析；采用钝化后的单晶制备光电探测器，考察MACl钝化对MAPbBr3单晶的光电性能的影响。结果表明：经MACl钝化，机械打磨后的MAPbBr3单晶表面重新结晶，载流子寿命增大约4-5倍，在形貌优化的同时有效减少了单晶的表面缺陷。氯离子的引入改变了单晶表面的晶格间距与能带结构，增大了单晶与电极之间的势垒，可使暗电流减少2个数量级，光暗电流比提高1个数量级，探测率提高近5倍。MACl钝化法简易高效，成本低廉，为MAPbBr3钙钛矿单晶高性能光电探测器的开发应用提供了可行性方案。

参考文献/References:

［ 1 ］ Kojima A, Teshima K, Shirai Y, et al. Organometal halide perovskites as visible - light sensitizers for photovoltaic cells ［ J ］ . Journal of the American Chemical Society, 2009, 131(17): 6050 - 6051.

［ 2 ］ Kim M, Jeong J, Lu H Z, et al. Conformal quantum dot - SnO   2 layers as electron transporters for efficient perovskite solar cells ［ J ］ . Science, 2022, 375(6578): 302 - 306.

［ 3 ］沈典典 , 张翔晖 . 有机无机杂化型钙钛矿材料光电探测器研究进展［ J ］ . 电子元件与材料 , 2018, 37(2): 7 - 18.

［ 4 ］ Saidaminov M I, Abdelhady A L, Murali B, et al. High - quality bulk hybrid perovskite single crystals within minutes by inverse temperature crystallization ［ J ］ . Nature Communications, 2015, 6: 7586.

［ 5 ］ Jeon N J, Noh J H, Yang W S, et al. Compositional engineering of perovskite materials for high - performance solar cells ［ J ］ . Nature, 2015, 517(7535): 476 - 480.

［ 6 ］ Hodes G. Applied physics. Perovskite - based solar cells ［ J ］ . Science, 2013, 342(6156): 317 - 318.

［ 7 ］ Stranks S D, Eperon G E, Grancini G, et al. Electron - hole diffusion lengths exceeding 1 micrometer in an organometal trihalide perovskite absorber ［ J ］ . Science, 2013, 342(6156): 341 - 344.

［ 8 ］ Zhumekenov A A, Saidaminov M I, Haque M A, et al. Formamidinium lead halide perovskite crystals with unprecedented long carrier dynamics and diffusion length ［ J ］ . ACS Energy Letters, 2016, 1(1): 32 - 37.

［ 9 ］ Dong Q F, Fang Y J, Shao Y C, et al. Electron - hole diffusion lengths > 175 μ m in solution - grown CH   3 NH   3 PbI   3 single crystals ［ J ］ . Science, 2015, 347(6225): 967 - 970.

［ 10 ］ Shi D, Adinolfi V, Comin R, et al. Low trap - state density and long carrier diffusion in organolead trihalide perovskite single crystals ［ J ］ . Science, 2015, 347(6221): 519 - 522.

undefined

备注/Memo

备注/Memo:
收稿日期： 2022-04-29
网络出版日期：2022-06-02
基金项目： 国家自然科学基金项目（11804300）
作者简介： 陈航（1997-），男，江苏扬州人，硕士研究生，主要从事光电探测器方面的研究
通信作者： 林萍，E-mail：pinglin@zstu.edu.cn
更新日期/Last Update: 2023-04-03