|本期目录/Table of Contents|

[1]孟晓美,易玲敏,陈睿文.退火对PMTFPS b PS电纺膜表面性质的影响[J].浙江理工大学学报,2014,31-32(自科6):641-646.
　MENG Xiao mei,YI Ling min,CHEN Rui wen.Effect of Annealing on Surface Properties of PMTFPS b PS Electro spinning Film[J].Journal of Zhejiang Sci-Tech University,2014,31-32(自科6):641-646.
点击复制

退火对PMTFPS b PS电纺膜表面性质的影响()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第31-32卷
期数:
2014年自科6期
页码:
641-646
栏目:
(自科)纺织与服装工程
出版日期:
2014-11-10

文章信息/Info

Title:
Effect of Annealing on Surface Properties of PMTFPS b PS Electro spinning Film
文章编号:
1673-3851 (2014) 06-0641-06
作者:
孟晓美;  易玲敏;  陈睿文
浙江理工大学, a. 先进纺织材料与制备技术教育部重点实验室; b. 生态染整技术教育部工程研究中心, 杭州 310018
Author(s):
MENG Xiaomei;  YI Lingmin;  CHEN Ruiwen
a. Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education; b. Engineering Research Center for Eco Dyeing & Finishing of Textiles, Ministry of Education,Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
氟硅;  嵌段共聚物;  退火;  静电纺丝;  表面性质
分类号:
O634.4
文献标志码:
A
摘要:
通过氟硅单体1,3,5 三甲基 1,3,5 三(3,3,3 三氟丙基)环三硅氧烷(简称F-3)的阴离子开环聚合(ROP)、苯乙烯(St)的原子转移自由基聚合(ATRP),合成了含氟硅嵌段共聚物PMTFPS b PS,并将其以四氢呋喃(THF)和N,N 二甲基甲酰胺(DMF)为溶剂进行静电纺丝。采用接触角测量仪(CAM)、扫描电镜(SEM)、X射线光电子能谱(XPS)研究PMTFPS b PS电纺膜退火前后的疏水性、微观形貌以及表面化学组成。结果表明：电纺纤维的水接触角可达152.6°,即达到超疏水的效果,经过120℃退火处理后电纺膜的表面光滑,接触角有所减小,但其水接触角仍远高于共聚物溶剂膜的接触角。

参考文献/References:

［1］ Yi L, Huang C, Zhou W. Synthesis, surface properties, and morphologies of poly［methyl(3,3,3trifluoropropyl) siloxane］ b polystyrene b poly(tert butylacrylate) triblock copolymers by a combination of anionic ROP and ATRP［J］. Journal of Polymer Science, Part A: Polymer Chemistry, 2012(50): 1728-1739.
［2］ Clarson S J, Owen M J, Smith S D, et al. Advances in Silicones and SiliconeModified Materials［M］. Washington, DC: American Chemical Society, 2010 : 99-108
［3］ 袁利兵, 刘海梁. 浅谈氟硅系列材料的性能及应用［J］. 有机氟工业, 2002, 30(2) : 31-33.
［4］ 赵宁, 卢晓英, 张晓艳, 等. 超疏水表面的研究进展［J］. 化学进展, 2007, 19( 6) : 860-871.
［5］ 倪华钢, 张伟, 王新平. 侧基含氟聚合物结构与表面性质研究进展［J］. 高分子材料科学与工程, 2007, 23(2) : 14-18.
［6］ 杜晨光, 夏帆, 王树涛, 等. 仿生智能浸润性表面研究的新进展［J］. 高等学校化学学报, 2010, 31(3) : 421-431.
［7］ 李小红. 静电纺纤维膜的疏水性能和拉伸性能的研究［D］. 上海: 东华大学, 2009: 5-11.
［8］ 郭志光, 刘维民. 仿生超疏水性表面的研究进展［J］. 化学进展, 2006, 18(6) : 721-726.
［9］ Feng L, Li S, Li Y, et al. Superhydropholic surfaces: from natural to artificial［J］. Advanced Materials, 2002, 14(15) : 1857-1860.
［10］ Lim J M, Yi G R, Moon J H, e t al. Superhydrophobic films of electrospun fibers with multiple scale surface morphology［J］. Langmuir, 2007, 23(15) : 7981-7985.
［11］ 高雪峰, 江雷. 天然超疏水生物表面研究的新进展［J］. 物理, 2006, 35(7) : 559-564.
［12］ Grange J D, Markham J L, Kurkjian C R. Effects of surface hydration on the deposition of silane monolayers on silica［J］. Langmuir. 1993, 9(7): 1749-1763.
［13］ Fadeev A Y, McCarthy T J. Selfassembly is not the only reaction possible between alkyltrichlorosilanes and surfaces: monomolecular and oligomeric covalently attached layers of dichloro and trichloroalkylsilanes on silicon［J］. Langmuir, 2000, 16(18): 7268-7274.
［14］ Van Oss C J. Interfacial Forces in Aqueous Media［M］. Boca Raton: Taylor & Francis, 2006: 213-226.

相似文献/References:

[1]田小平,易玲敏,孟晓美.聚醚改性氟硅表面活性剂的合成与溶液性质研究[J].浙江理工大学学报,2014,31-32(自科6):636.
　TIAN Xiao ping,YI Ling min,MENG Xiao mei.Research on Synthesis and Solution Properties of Polyether Modified Fluorosilicone Surfactant[J].Journal of Zhejiang Sci-Tech University,2014,31-32(自科6):636.
[2]张佳文,易玲敏,徐凯,等.PMTFPS-b-PMAA嵌段共聚物的合成与胶束化[J].浙江理工大学学报,2015,33-34(自科6):761.
　Zhang Jia wen,YI Ling min,Xu Kai,et al.Synthesis and Micellization of PMTFPS-b-PMAA Block Copolymers[J].Journal of Zhejiang Sci-Tech University,2015,33-34(自科6):761.
[3]王明乾,易玲敏,李静,等.涂层厚度对氟硅与甲基丙烯酸甲酯嵌段共聚物表面微观形貌和性质的影响[J].浙江理工大学学报,2017,37-38(自科1):31.
　WANG Mingqian,YI Lingmin,LI Jing,et al.The Influence of Film Thickness on Surface Microtopography and Properties  of Block Copolymers of Fluorosilicone and Methyl Methacrylate[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科6):31.
[4]王爱瑞,邵英,易玲敏,等.PMTFPS-b-PMMA/PMMA共混聚合物膜的表面性质[J].浙江理工大学学报,2017,37-38(自科6):804.
　WANG Airui,SHAO Ying,YI Lingmin,et al.Surface Properties of PMTFPS-b-PMMA/PMMA Polymer Blend Films[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科6):804.

备注/Memo

备注/Memo:
收稿日期： 2014-02-28
基金项目： 国家自然科学基金项目(21276243);浙江省重点科技创新团队项目(2012R10038-14)
作者简介： 孟晓美(1989-),女,安徽宿州人,硕士研究生,主要从事高分子方向的研究
通信作者： 易玲敏,E-mail:lmyi@zstu.edu.cn
更新日期/Last Update: 2014-11-19