[1]董青青a,吴明华a,b,等. 聚醚聚硅氧烷二元醇改性水性聚氨酯涂层剂的研制[J].浙江理工大学学报,2011,28(05):658-662.
　DONG Qing qinga,WU Ming huaa,b,et al. Preparation of the Coating Agent on the Fabric with Polyurethane Modified by Polyethersiloxanediol[J].Journal of Zhejiang Sci-Tech University,2011,28(05):658-662.
点击复制

 聚醚聚硅氧烷二元醇改性水性聚氨酯涂层剂的研制()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第28卷
期数:
2011年05期
页码:
658-662
栏目:
出版日期:
2011-10-30

文章信息/Info

Title:
 Preparation of the Coating Agent on the Fabric with Polyurethane Modified by Polyethersiloxanediol
文章编号:
16733851 (2011) 05 065805
作者:
 董青青1a;  吴明华1a; b;  刘爱莲2;  鲍进跃2;  柴红梅2
 1. 浙江理工大学, a. 先进纺织材料与制备技术教育部重点实验室, b. 生态染整技术教育部工程研究中心, 杭州 310018; 2. 浪莎控股集团有限公司, 浙江 义乌 322000
Author(s):
 DONG Qingqing1a;  WU Minghua1a; b;  LIU Ailian2;  BAO Jinyue2;  CHAI Hongmei2
 1. Zhejiang SciTech University, a. The Key Laboratory of Advanced Textile Material and Manufacturing Technology; b. Engineering Research Center for EcoDyeing & Finishing of Textiles, Ministry of Education, Hangzhou 310018, China; 2. Langsha Group Co., Ltd, Yiwu 322000, China
关键词:
 ; 水性聚氨酯;  聚醚聚硅氧烷二元醇;  耐水性;  织物涂层
分类号:
TS195.5
文献标志码:
A
摘要:
    采用聚氧化丙烯二醇和聚醚聚硅氧烷二元醇为混合软段，异佛尔酮二异氰酸酯为硬段合成了有机硅改性水性聚氨酯(SiWPU)乳液, 研究聚醚聚硅氧烷二元醇的用量对改性水性聚氨酯乳液及其胶膜性能的影响，并将其应用于棉织物的涂层整理，测试了改性水性聚氨酯涂层织物的静水压、透湿量、耐洗性、撕破强度以及硬挺度。研究结果表明：聚醚聚硅氧烷二元醇用量为2%~8%，改性聚氨酯乳液具有良好的乳液稳定性和较小的粒径，胶膜能保持聚氨酯原有的拉伸强度，且具有较好的耐水性和滑爽的手感；采用聚醚聚硅氧烷二元醇改性聚氨酯，可以明显提高涂层织物的耐水性和透湿性。

参考文献/References:

 ［1］ 许戈文. 水性聚氨酯材料［M］. 北京: 化学工业出版社, 2006: 12.
［2］ Janusz Kozakiewicz. Polysiloxaneurethanes: new polymers for potential coating applications［J］. Progress in Organic Coatings, 1996, 27(6): 123131.
［3］ Dou Q Z, Wang C C, Cheng C. PDMSmodified polyurethane films with low water contact angle hysteresis［J］. Macromolecular Chemistry and Physics, 2006, 20(7): 21702179.
［4］ Majumdar P, Webster D C. Surface microtopography in siloxanepolyurethan ethermosets: the influence of siloxane and extent of reaction［J］. Polymer, 2007, 26(3): 74997509.
［5］ 傅荣兴, 饶文亮. 水性聚氨酯预聚硅氧烷共混改性的研究［J］. 皮革科技, 1989, 18(10): 1517.
［6］ 吴小峰, 朱传方, 张丽, 等. 二羟基硅油改性水性聚氨酯树脂的合成及性能［J］. 应用化学, 2007, 24(9): 10231026.
［7］ 姚明, 李伯耿, 朱春凤. 烷羟基硅油改性水性聚氨酯的制备和性能［J］. 科技通报, 2007, 23(4): 574577.
［8］ 宋海相, 罗运军, 罗巨涛, 等. 聚醚硅氧烷二元醇改性水性聚氨酯的合成及性能［J］. 上海交通大学学报, 2006, 40(7): 12491256.
［9］ 伍胜利, 吴晓波, 李晓萱. 聚醚型硅油改性水性聚氨酯的制备与性能研究［J］. 热固型树脂, 2009, 24(3): 3638.
［10］ 周成, 张兴元, 戴家兵, 等. 硅氧烷改性水性聚氨酯的制备及性能［J］. 化学物理学报, 2005, 18(3): 448452.
［11］ 陈红, 范曲立, 余学海. 氨基硅油扩链改性水性聚氨酯的研究［J］. 功能高分子学报, 1999, 12(9): 297301.
［12］ 罗振寰. 有机硅改性聚氨酯涂层聚合物的合成及其表面性能［D］. 杭州: 浙江大学, 2010: 16.

相似文献/References:

[1]陈智杰a,赵晓丽a,徐畅b,等. 有机颜料微胶囊在涂料染色中的应用及其染色效果分析[J].浙江理工大学学报,2013,30(01):1.
　CHEN Zhi jiea,ZHAO Xiao lia,XU Changb,et al. Application of Organic Pigment Microcapsule in Pigment Dyeingand Its Dyeing Results[J].Journal of Zhejiang Sci-Tech University,2013,30(05):1.
[2]詹永娟,谢维斌,姜晓云,等. 织物液态水传递性能的自动检测技术及应用[J].浙江理工大学学报,2013,30(01):6.
　ZHAN Yong juan,XIE Wei bin,JIANG Xiao yun,et al. Technology and Application of the Automatic Detection inTesting Liquid Transport Properties of Textiles[J].Journal of Zhejiang Sci-Tech University,2013,30(05):6.
[3]孙麒. 基于极大似然估计的织物图像分割[J].浙江理工大学学报,2013,30(01):12.
　SUN Qi. Textile Image Segmentation Based on theMaximum Likelihood Algorithm[J].Journal of Zhejiang Sci-Tech University,2013,30(05):12.
[4]巫静a,田彦杰b,汪澜a,等. 基于SVM理论的涤纶织物分散染料上染率模型研究[J].浙江理工大学学报,2013,30(01):21.
　WU Jinga,TIAN Yan jieb,WANG Lana,et al. Research on Modeling of DyeUptake Rate for Disperse Dyes onPolyester Fibers Based on SVM[J].Journal of Zhejiang Sci-Tech University,2013,30(05):21.
[5]周昊,徐英莲,齐素梅.微孔结构改性涤纶/棉混纺针织物服用性能的研究[J].浙江理工大学学报,2013,30(01):21.
　ZHAO Hao,XU Ying lian,QI Su mei. Research on Using Knitted Blend Fabric of Modified Polyesterby Cellular Structure and Cotton for Wearing[J].Journal of Zhejiang Sci-Tech University,2013,30(05):21.
[6]孙佳英,李艳清,章斐燕,等. 纺织结构复合材料铺层顺序设计与力学性能分析[J].浙江理工大学学报,2013,30(01):27.
　SUN Jia ying,LI Yan qing,ZHANG Fei yan,et al. Study on Layer Sequence Design and Mechanical Propertiesof Textile Structure Composites[J].Journal of Zhejiang Sci-Tech University,2013,30(05):27.
[7]丁源维,王騊,姚菊明,等. 静电纺制备TiO2/PVA复合纳米纤维及其光催化性能研究[J].浙江理工大学学报,2013,30(01):31.
　DING Yuan wei,WANG Tao,YAO Ju ming,et al. Photocatalytic Performance Investigation of TiO2/PVANanofibers Prepared by Electrospinning[J].Journal of Zhejiang Sci-Tech University,2013,30(05):31.
[8]章梦洁,伍仲,方园. 涤棉混纺织物阻燃性能的实验分析[J].浙江理工大学学报,2013,30(01):36.
　ZHANG Meng jie,WU Zhong,FANG Yang. Experimental Study on the PolyesterCotton BlendedFabrics Flame Retardancy[J].Journal of Zhejiang Sci-Tech University,2013,30(05):36.
[9]胡觉亮a,孔云鹏b,韩曙光a,等. 基于随机需求的服装供应链回购契约研究[J].浙江理工大学学报,2013,30(01):40.
　HU Jue lianga,KONG Yun pengb,HAN Shu guanga,et al. Study on Repurchase Contract in a Fashion Chainwith the Stochastic Demand[J].Journal of Zhejiang Sci-Tech University,2013,30(05):40.
[10]毛雯,阎玉秀. 针织服装供应商评价指标体系构建与权重确定[J].浙江理工大学学报,2013,30(01):46.
　MAO Wen,YAN Yu xiu. Building Evaluation Index System for Knitting Clothing Suppliersand Determining the Weight[J].Journal of Zhejiang Sci-Tech University,2013,30(05):46.

备注/Memo

备注/Memo:
 收稿日期： 2010-10-27
作者简介： 董青青（1986-），男，浙江宁波人，硕士研究生，主要从事纺织化学品助剂的研制及应用研究。
通讯作者： 吴明华，电子邮箱：wmh@zstu.edu.cn
更新日期/Last Update: