|本期目录/Table of Contents|

[1]楼恒屹,万军民.PVA-AgNWs@PVA水凝胶纤维制备及传感性能研究[J].浙江理工大学学报,2024,51-52(自科六):735-742.
 Hengyi,WAN Junmin.Preparation and sensing properties of  PVA-AgNWs@PVA hydrogel fibers[J].Journal of Zhejiang Sci-Tech University,2024,51-52(自科六):735-742.
点击复制

PVA-AgNWs@PVA水凝胶纤维制备及传感性能研究()
分享到:

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第51-52卷
期数:
2024年自科第六期
页码:
735-742
栏目:
出版日期:
2024-11-10

文章信息/Info

Title:
Preparation and sensing properties of  PVA-AgNWs@PVA hydrogel fibers
作者:
楼恒屹万军民
浙江理工大学材料科学与工程学院,杭州 310018
Author(s):
Hengyi WAN Junmin
School of Materials Science & Engineering, Zhejiang SciTech University, Hangzhou 310018, China
关键词:
水凝胶纤维同轴湿法纺丝高导电性温敏响应应变传感
分类号:
TQ342-83
文献标志码:
A
摘要:
为解决传统纤维基传感器功能单一与应变范围窄的缺点,以聚乙烯醇(PVA)为水凝胶基材、银纳米线为芯层填料、温敏粉末为皮层填料,采用同轴湿法纺丝技术制备PVA-AgNWs@PVA水凝胶初生纤维,将初生纤维置于4 mol/L氯化钠溶液中浸泡72 h制得PVA-AgNWs@PVA水凝胶传感纤维;对PVA-AgNWs@PVA水凝胶纤维的温度和拉伸传感性能进行测定。结果表明:PVA-AgNWs@PVA水凝胶纤维在环境温度小于17 ℃时呈深蓝色,18~27 ℃时呈蓝灰色,28~35 ℃时呈淡红色,大于36 ℃时呈灰白色;该水凝胶纤维断裂伸长率为374%,拉伸强度为3-65 MPa,电导率为5-12 S/m,应变灵敏度为3-57,在高频次运动状态下相对电阻变化一致。该文制备的PVAAgNWs@PVA水凝胶纤维具有优异的温度和拉伸传感性能,在柔性可穿戴设备领域具有潜在的应用价值。

参考文献/References:

[1]王思恒, 杨欣欣, 刘鹤, 等. 导电水凝胶的制备及应用研究进展[J]. 化工进展, 2021, 40(5): 2646-2664.
[2]鲁程程, 樊晓慧, 张玉红. 导电水凝胶的研究进展[J]. 胶体与聚合物, 2020, 38(2): 85-89.
[3]刘剑桥, 舒浩然, 王晓玲, 等. 导电水凝胶的构筑设计及应用[J]. 高分子材料科学与工程, 2019, 35(7): 182-190.
[4]Han L, Yan L W, Wang M H, et al. Transparent, adhesive, and conductive hydrogel for soft bioelectronics based on light-transmitting polydopamine-doped polypyrrole nanofibrils[J]. Chemistry of Materials, 2018, 30(16): 5561-5572.
[5]Liao M H, Liao H, Ye J J, et al. Polyvinyl alcohol-stabilized liquid metal hydrogel for wearable transient epidermal sensors[J]. ACS Applied Materials & Interfaces, 2019, 11(50): 47358-47364.
[6]Liu X F, Kim J C, Miller A L, et al. Electrically conductive nanocomposite hydrogels embedded with functionalized carbon nanotubes for spinal cord injury[J]. New Journal of Chemistry, 2018, 42(21): 17671-17681.
[7]Yang X L, Cao L Q, Wang J D, et al. Sandwich-like polypyrrole/reduced graphene oxide nanosheets integrated gelatin hydrogel as mechanically and thermally sensitive skinlike bioelectronics[J]. ACS Sustainable Chemistry & Engineering, 2020, 8(29): 10726-10739.
[8]Zhang Y Z, Wang Y, Cheng T, et al. Printed supercapacitors: materials, printing and applications[J]. Chemical Society Reviews, 2019, 48(12): 3229-3264.
[9]武慧. 基于同轴湿法纺丝导电复合纤维的制备及柔性传感器的应用研究[D]. 杭州: 浙江理工大学, 2023: 5.
[10]高辉. 基于聚丙烯酰胺离子水凝胶的柔性自供电电子皮肤研制[D]. 哈尔滨: 哈尔滨工业大学, 2020: 15-16.

备注/Memo

备注/Memo:
收稿日期: 2024-03-08
网络出版日期:2024-05-08
基金项目: 国家自然科学基金项目(52173274);浙江省自然科学基金项目(LY13B030009)
作者简介: 楼恒屹(1999—),男,浙江湖州人,硕士研究生,主要从事传感水凝胶纤维方面的研究
通信作者: 万军民,E-mail:wwjm2001@126.com
更新日期/Last Update: 2024-11-14