[1]郭银涛,王勇军,吕汪洋.单体和低聚物的含量对聚酰胺6切片性能的影响[J].浙江理工大学学报,2024,51-52(自科二):174-179.
　GUO Yintao,WANG Yongjun,L  Wangyang.Effects of monomer and oligomer content in  polyamide 6 pellets on their properties[J].Journal of Zhejiang Sci-Tech University,2024,51-52(自科二):174-179.
点击复制

单体和低聚物的含量对聚酰胺6切片性能的影响()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第51-52卷
期数:
2024年自科第二期
页码:
174-179
栏目:
出版日期:
2024-03-10

文章信息/Info

Title:
Effects of monomer and oligomer content in  polyamide 6 pellets on their properties
文章编号:
1673-3851 (2024) 03-0174-06
作者:
郭银涛; 王勇军; 吕汪洋
浙江理工大学纺织纤维材料与加工技术国家工程实验室，杭州 310018
Author(s):
GUO Yintao;  WANG Yongjun;  L  Wangyang
National Engineering Laboratory for Textile Fiber Materials and Processing Technology, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
PA6切片; 单体; 低聚物; 液相色谱/飞行时间质谱/二极管阵列检测器; 结晶
分类号:
TQ317-2
文献标志码:
A
摘要:
采用溶解/沉淀法对聚酰胺6（PA6）中的单体及低聚物进行提取，利用液相色谱/飞行时间质谱/二极管阵列检测器（LC-TOF-MS-PDA）和聚合物色谱/多角度激光散射/示差折光检测器（APC- MALLS-RID）联用方法测定PA6中单体和低聚物含量、低聚物组成及PA6的分子量和分布；通过热重分析仪、差示扫描量热仪和二维广角X射线衍射仪分析PA6切片中单体低聚物含量对切片热性能和结晶性能的影响。结果表明：物理再生PA6（pr-PA6）和化学再生PA6（cr-PA6）中单体及环状低聚物含量分别为2.079%和1.578%，比原生PA6（PA6）分别高0.683%和0.182%，其中再生PA6切片中单体、环状二聚体和环状三聚体含量高于原生PA6切片。PA6、pr-PA6和cr-PA6的分子量分别为19620、20840 g/mol和22210 g/mol，分子量分布系数分别为1.47、1.56和1.49；三种PA6切片的最大分解温度无明显变化。与原生PA6切片相比，再生PA6切片的结晶峰温度向高温区偏移，结晶温度从PA6的176 ℃增加至pr--PA6的 185 ℃，且pr-PA6和cr-PA6切片中α晶型的相对含量增加。该研究可为提高PA6材料的热性能及结晶性能提供理论基础。

参考文献/References:

［1］Peng C, Tang X J, Gong X Y, et al. Development and application of a mass spectrometry method for quantifying nylon microplastics in environment［J］. Analytical Chemistry, 2020, 92(20): 13930-13935.
［2］Mondragon G, Kortaberria G, Mendiburu E, et al. Thermomechanical recycling of polyamide 6 from fishing nets waste［J］. Journal of Applied Polymer Science, 2020, 137(10): 48442.
［3］Banerjee S S, Bhowmick A K. Novel nanostructured polyamide 6/fluoroelastomer thermoplastic elastomeric blends: Influence of interaction and morphology on physical properties［J］. Polymer, 2013, 54(24): 6561-6571.
［4］Esmizadeh E, Vahidifar A, Shojaie S, et al. Tailoring the properties of PA6 into high-performance thermoplastic elastomer: Simultaneous reinforcement and impact property modification［J］. Materials Today Communications, 2021, 26: 102027.
［5］ehi Aｃ＇1 A, VasiljeviAｃ＇1  J, Jordanov I, et al. Influence of N-, P- and Si-based flame retardant mixtures on flammability, thermal behavior and mechanical properties of PA6 composite fibers［J］. Fibers and Polymers, 2018, 19(6): 1194-1206.
［6］李文武. 基于热裂解色谱的PA6和PA66纤维鉴别及定量分析研究［D］. 杭州：浙江理工大学, 2017：1-3.
［7］Chen J Y, Li Z, Jin L J, et al. Catalytic hydrothermal depolymerization of nylon 6［J］. Journal of Material Cycles and Waste Management, 2010, 12(4): 321-325.
［8］Alberti C, Figueira R, Hofmann M, et al. Chemical recycling of end-of-life polyamide 6 via ring closing depolymerization［J］. ChemistrySelect, 2019, 4(43): 12638-12642.
［9］黄梅. 聚酰胺类材料化学解聚反应研究［D］. 青岛：青岛科技大学, 2018：6-10.
［10agar E, ACˇGearek U, Drin?iAｃ＇1 A  Zagar E，Cesarek U， Drincic A, et al. Quantitative determination of PA6 and/or PA66 content in polyamide-containing wastes［J］. ACS Sustainable Chemistry & Engineering, 2020, 8(31): 11818-11826.

相似文献/References:

[1]黄益,张海东,孟一丁,等.纺织品数码喷印用蓝光固化颜料墨水之柔性聚合体系研究[J].浙江理工大学学报,2016,35-36(自科1):9.
　HUANG Yi,ZHANG Haidong,MENG Yiding,et al.Study on Fleixble Polymerization System of Blue Light Curing Ink for Textile Digital Inkjet Printing[J].Journal of Zhejiang Sci-Tech University,2016,35-36(自科二):9.
[2]王东海,许丹,陈建勇.单体和低聚物对UV固化涂料稳定性的影响[J].浙江理工大学学报,2017,37-38(自科2):220.
　WANG Donghai,XU Dan,CHEN Jianyong.Effects of Monomers and Oligomers on the Stability of UV Curing Coatings[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科二):220.

备注/Memo

备注/Memo:
收稿日期： 2023-04-06
网络出版日期：2023-07-07
基金项目： 浙江省自然科学基金项目(LDQ23E030001)
作者简介： 郭银涛(1997-)，男，安徽阜阳人，硕士研究生，主要从事再生PA6性能分析方面的研究
通信作者： 吕汪洋，E-mail: luwy@zstu.edu.cn
更新日期/Last Update: 2024-03-08