[1]郑洋,孙辉,于斌.Cu-MOF/PP/纤维素水刺非织造材料的制备及其性能[J].浙江理工大学学报,2019,41-42(自科六):769-775.
　ZHENG Yang,SUN Hui,YU Bin.Preparation and properties of CuMOF/PP/cellulose spunlaced nonwovens[J].Journal of Zhejiang Sci-Tech University,2019,41-42(自科六):769-775.
点击复制

Cu-MOF/PP/纤维素水刺非织造材料的制备及其性能()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第41-42卷
期数:
2019年自科六期
页码:
769-775
栏目:
出版日期:
2019-10-31

文章信息/Info

Title:
Preparation and properties of CuMOF/PP/cellulose spunlaced nonwovens
文章编号:
1673-3851 (2019) 11-0769-07
作者:
郑洋;  孙辉;  于斌
浙江理工大学材料与纺织学院，杭州 310018
Author(s):
ZHENG Yang;  SUN Hui;  YU Bin
College of Materials and Textiles, Zhejiang Sci-Tech University, Hangzhou 310081, China
关键词:
金属有机框架材料; 非织造材料; 溶剂热; 染料去除
分类号:
O643-36
文献标志码:
A
摘要:
以1,2二溴乙烷、4,4联吡啶、醋酸铜为原料，聚丙烯（PP）和纤维素组成的双层水刺非织造材料为基底，通过溶剂热法制得CuMOF（铜基金属有机框架材料）/PP/纤维素复合水刺非织造材料。利用扫描电镜、X射线衍射、红外光谱仪等对复合材料的形貌和结构进行表征，并研究了其对水溶液中酸性橙7的去除能力。结果表明：CuMOF主要负载于非织造材料的纤维素表面上，且呈现花朵状；改性后，复合材料的拉伸强度断裂伸长率略有下降，拉伸模量基本没有变化；在60 min内，对浓度为5 mg/L的酸性橙7的去除率达到90%，经5次循环后的去除率仍在60%以上。

参考文献/References:

［1］ Petit C. Present and future of MOF research in the field of adsorption and molecular separation［J］. Current Opinion in Chemical Engineering, 2018, 20: 132-142.
［2］ Li H, Wang K C, Sun Y J, et al. Recent advances in gas storage and separation using metalorganic frameworks［J］. Materials Today, 2018, 21(2): 108-121.
［3］ AlJadir T M, Siperstein F R. The influence of the pore size in MetalOrganic Frameworks in adsorption and separation of hydrogen sulphide: A molecular simulation study［J］. Microporous and Mesoporous Materials, 2018, 271: 160-168.
［4］ 李庆, 张莹, 樊增禄, 等. Cu有机骨架对染料废水的吸附和可见光降解［J］. 纺织学报, 2018, 39(2): 112-118.
［5］ 高霞, 张国春, 乔成芳. CuMOFs固定化酶制备及染料降解应用研究［J］. 商洛学院学报, 2018, 137(4): 30-36.
［6］ Han L J, Kong Y J, Yan T J, et al. A new fivecoordinated copper compound for efficient degradation of methyl orange and Congo red in the absence of UVvisible radiation［J］. Dalton Transactions, 2016, 45(46): 1856618571.
［7］ Liu K, Zhou N Y, Xie C X, et al. Design dopaminemodified polypropylene fibers towards removal of heavy metal ions from water［J］. Aip Advances, 2017, 7(4): 898-906.
［8］ Lee D T, Zhao J, Peterson G W, et al. Catalytic “MOFCloth” formed via directed supramolecular assembly of UiO66NH2 crystals on atomic layer depositioncoated textiles for rapid degradation of chemical warfare agent simulants［J］. Chemistry of Materials, 2017, 29(11): 4894-4903.
［9］ Lu A X, Ploskonka A M, Tovar T M, et al. Direct surface growth of UIO66NH2 on polyacrylonitrile nanofibers for efficient toxic chemical removal［J］. Industrial & Engineering Chemistry Research, 2017, 56(49): 14502-14506
［10］ Silva Pinto M, SierraAvila C A, Hinestroza J P. In situ synthesis of a CuBTC metalorganic framework (MOF 199) onto cellulosic fibrous substrates: cotton［J］. Cellulose, 2012, 19(5): 1771-1779.

相似文献/References:

[1]张子洁,吴超,朱为康,等.Mg掺杂对［NH-2(CH-3)-2］Mn 1-x-Mg-x-(HCOO)-3单晶性能的影响[J].浙江理工大学学报,2017,37-38(自科6):823.
　ZHANG Zijie,WU Chao,ZHU Weikang,et al.Doping Effect of Mg on the Physics Properties of ［NH-2(CH-3)-2］Mn-1-xMg-x-(HCOO)3 Single Crystals[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科六):823.

备注/Memo

备注/Memo:
基金项目：浙江省自然科学基金项目（LY19E030011）;国家自然科学基金项目（51203141）；浙江省公益技术应用研究项目（2017C33077）
作者简介：郑洋（1993-），男，浙江台州人，硕士研究生，主要从事非织造材料改性方面的研究
通信作者：于斌，E-mail：yubin7712@163.com
更新日期/Last Update: 2019-11-25