[1]杜文浩,王一帆,史伊媛,等.水热时间和低温热处理对 δ MnO 2电容性能的影响[J].浙江理工大学学报,2018,39-40(自科3):259-267.
　DU Wenhao,WANG Yifan,SHI Yiyuan,et al.Effects of hydrothermal time and lowtemperature heat treatment on supercapacitor properties of  δ MnO 2[J].Journal of Zhejiang Sci-Tech University,2018,39-40(自科3):259-267.
点击复制

水热时间和低温热处理对 δ MnO 2电容性能的影响()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第39-40卷
期数:
2018年自科3期
页码:
259-267
栏目:
出版日期:
2018-05-19

文章信息/Info

Title:
Effects of hydrothermal time and lowtemperature heat treatment on supercapacitor properties of  δ MnO 2
文章编号:
1673-3851 (2018) 05-0259-09
作者:
杜文浩; 王一帆; 史伊媛; 粟晨; 胡益彰; 王騊
浙江理工大学先进纺织材料与制备技术教育部重点实验室，杭州 310018
Author(s):
DU Wenhao;  WANG Yifan;  SHI Yiyuan;  SU Chen;  HU Yizhang;  WANG Tao
Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
超级电容器; 水热法; 低温热处理; 结晶性; 物理吸附水; 电化学性能
分类号:
O649.1
文献标志码:
A
摘要:
以高锰酸钾（KMnO 4）为原料，在不同反应时间下水热法制备δ MnO 2，同时对不同反应时间制备的 δ MnO 2进行300 ℃低温热处理。通过SEM揭示 δ MnO2的生长机理，采用SEM、TEM和XRD对 δ MnO2的形貌和结晶度进行表征，利用N 2吸附脱附法表征δ MnO2的比表面积，通过恒电流充放电、循环伏安法和交流阻抗法对δ MnO 2的电化学性能进行测试。实验结果表明：随着水热时间的延长， δ MnO2的结晶度依次增加，比电容逐渐增大；当电流密度为0.1 A/g时，10 h的样品在1 M Na 2SO 4电解液中比电容高达264 F/g，展现出最优的比电容。进一步对水热样品进行300 ℃低温热处理，结晶度进一步提高的同时物理吸附水大量丢失，导致比电容均出现下降。结果证实了δ MnO 2的结晶度和表面的物理吸附水对电容性能都具有贡献作用，二者缺一不可。 δ MnO 2随着结晶度的提高，层状结构越趋稳定，存储离子电荷的能力不断增强，同时材料表面的物理吸附水有助于提高电解液与电极材料之间的浸润性，降低电荷转移电阻，产生较大的赝电容。

参考文献/References:

［1］ Lu X, Yu H, M H, et al. Flexible solidstate  supercapacitors: design, fabrication and applications［J］. Energy & Environmental Science,2014,7(7):2160-2181.
［2］ Yang P, Mai W. Flexible solidstate electrochemical supercapacitors［J］. Nano Energy,2014,8(6):274-290.
［3］ 邱照远.赝电容材料用作超级电容器电极材料的研究［D］.厦门:华侨大学,2013:2-87.
［4］ 余丽丽,朱俊杰,赵景泰.超级电容器的现状及发展趋势［J］.自然杂志,2015,37(3):188-196.
［5］ 胡传跃,郭军,汪形艳.锂离子电池Li(Ni  (3/8)Co (3/8)Mn (2/8))O 2层状正极材料的制备与电化学性能［J］.中国有色金属学报,2008,18(9):1721-1726.
［6］ Zhu B, Tang S, Vonehr S. Hierarchically MnO2nanosheet covered submcrometerFeCo2O4tube forest as binderfree electrodes for high energy density allsolidstate supercapacitors［J］. Applied Materials & Interfaces,2016,8(7):4762-4770.
［7］ 王旭珍,周泉,任素贞.溶剂热法制备Fe3O4/氧化石墨烯复合材料及其性能研究［J］.功能材料,2015,46(3):3045-3049.
［8］ Radhamani A V, Shareef K M, Rao M S R. ZnO@MnO2 coreshell nanofiber cathodes for high performance  asymmetric supercapacitors［J］. Applied Materials & Interfaces,2016,8(44):30531.
［9］ 庞旭,马正青,左列.Sn掺杂二氧化锰超级电容器电极材料［J］.物理化学学报,2009,25(12):2433-2437.
［10］ Simon P, Gogotsi Y. Materials for electrochemical capacitors［J］. Nature Materials,2008,7(11):845-854.

相似文献/References:

[1]裴有斌,郭绍义,袁永锋,等. 液晶模板法制备Co3O4分级多孔结构薄膜和赝电容性能研究[J].浙江理工大学学报,2012,29(02):204.
　PEI You\|bin,GUO Shao\|yi,YUAN Yong\|feng,et al. Preparation and Pseudocapacitance Performances of HierarchicallyPorous Co3O4 Film by Lyotropic Liquid Crystalline Templates[J].Journal of Zhejiang Sci-Tech University,2012,29(自科3):204.
[2]郑贤火,马非凡,王龙成.K+掺杂对Y-2O- 3：Eu 3+粉末发光强度与量子效率的影响[J].浙江理工大学学报,2016,35-36(自科5):691.
　ZHENG Xianhuo,MA Feifan,WANG Longcheng.Effect of K+ Doping on Luminescent Intensity and Quantum Efficiency of Y 2O 3：Eu 3+  Powder[J].Journal of Zhejiang Sci-Tech University,2016,35-36(自科3):691.
[3]闫爱丽,王晟,俞烨,等.碳化纳米纤维负载TiO-2的制备及其光催化性能研究[J].浙江理工大学学报,2017,37-38(自科1):8.
　YAN Aili,WANG Sheng,YU Ye,et al.Preparation of TiO-2 Loaded by Carbon Nanofiber and Investigation of Its Photocatalytic Performance[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科3):8.
[4]张志强,袁永锋,郭绍义,等.聚吡咯包覆CoMoO-4纳米片自组装多孔柱阵列的制备及其赝电容性能研究[J].浙江理工大学学报,2017,37-38(自科1):18.
　ZHANG Zhiqiang,YUAN Yongfeng,GUO Shaoyi,et al.Preparation and Pseudocapacitance Performance of CoMoO-4 -NanoflakeAssembling Porous Pillar Array Coated by Polypyrrole[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科3):18.
[5]江珍珍,郑晋生,王晟.核 壳光催化剂Cu-CdS@C-3N-4的制备及其性能研究[J].浙江理工大学学报,2017,37-38(自科1):24.
　JIANG Zhenzhen,ZHENG Jinsheng,WANG Sheng.Preparation of Core Shell Photocatalyst Cu-CdS@C-3N-4  and  Study on Its Performance[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科3):24.
[6]周伟杰,高林辉,王广发.Gd-2Zr-2O-7:Eu 3+ 红色荧光粉的制备及发光性能的研究[J].浙江理工大学学报,2017,37-38(自科2):197.
　ZHOU Weijie,GAO Linhui,WANG Guangfa.Preparation of Gd2Zr2O7:Eu3+ Red Phosphor and Stusy on Its Photoluminescence Property[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科3):197.
[7]戎泽,袁永锋,郭绍义,等.C包覆CoMoO-4复合纳米片阵列材料的制备和赝电容性能的研究[J].浙江理工大学学报,2017,37-38(自科3):343.
　RONG Ze,YUAN Yongfeng,GUO Shaoyi,et al.Preparation of Carboncoated CoMoO4 Composite Nanosheet ArrayMaterial and Study on Its Supercapacitance Performances[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科3):343.
[8]杨术莉,邱琳琳,杜平凡.水热法制备TiO-2致密层及其在钙钛矿太阳电池中的应用[J].浙江理工大学学报,2017,37-38(自科4):475.
　YANG Shuli,QIU Linlin,DU Pingfan.Preparation of TiO-2 Compact Layer by Hydrothermal Methodand Its Application in Perovskite Solar Cells[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科3):475.
[9]马非凡,郑贤火,廖世才,等.钾离子对GdBO-3:Tb-3+ 发光性能的影响[J].浙江理工大学学报,2017,37-38(自科4):506.
　MA Feifan,ZHENG Xianhuo,LIAO Shicai,et al.Effect of K+ Doping on Luminescent Property of GdBO-3:Tb-3+ Powder[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科3):506.
[10]魏琦,周彬,杨帆,等.SiO-2/Ag复合微球的制备及光催化性能研究[J].浙江理工大学学报,2017,37-38(自科6):810.
　WEI Qi,ZHOU Bin,YANG Fan,et al.Preparation and Photocatalytic Performance ofSiO-2/Ag Composite Microsphere[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科3):810.
[11]余大江,郭绍义,袁永锋,等.水热法高温煅烧处理制备Ni x Co - x MoO 4纳米片阵列/泡沫Ni复合材料及其赝电容性能研究[J].浙江理工大学学报,2016,35-36(自科6):855.
　YU Dajiang,GUO Shaoyi,YUAN Yongfeng,et al.Preparation of Ni xCo 1-x MoO4 Nanosheet Array/Nickel Foam  Composite by Hydrothermal Method and Hightemperature Calcination and Its Pseudocapacitance Performance[J].Journal of Zhejiang Sci-Tech University,2016,35-36(自科3):855.
[12]谢宇,李赛赛,王龙成,等.碳布上负载的MnCo2O4纳米阵列的形貌、物相及电化学性能[J].浙江理工大学学报,2021,45-46(自科五):596.
　XIE Yu,LI Saisai,WANG Longcheng,et al.Morphology, physical phase and electrochemical properties of MnCo2O4nanoarrays loaded on carbon cloth[J].Journal of Zhejiang Sci-Tech University,2021,45-46(自科3):596.

备注/Memo

备注/Memo:
收稿日期： 2017-09-30
网络出版日期： 2017-12-11
基金项目： 国家自然科学基金项目（51471153）
作者简介： 杜文浩（1993-），男，安徽合肥人，硕士研究生，主要从事超级电容器赝电容材料方面的研究
通信作者： 王騊，E-mail:taotao571@hotmail.com
更新日期/Last Update: 2018-06-19