　WANG Airui,SHAO Ying,YI Lingmin,et al.Surface Properties of PMTFPS-b-PMMA/PMMA Polymer Blend Films[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科6):804-809.
点击复制

PMTFPS-b-PMMA/PMMA共混聚合物膜的表面性质()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第37-38卷
期数:
2017年自科6期
页码:
804-809
栏目:
出版日期:
2017-11-10

文章信息/Info

Title:
Surface Properties of PMTFPS-b-PMMA/PMMA Polymer Blend Films
文章编号:
1673-3851 (2017) 06-0804-06
作者:
王爱瑞; 邵英; 易玲敏; 李伟翔; 李家炜
1.浙江理工大学，a.材料与纺织学院；b.先进纺织材料与制备技术教育部重点实验室，杭州 310018；2.浙江工程设计有限公司,杭州 310002
Author(s):
WANG Airui;  SHAO Ying;  YI Lingmin;  LI Weixiang;  LI Jiawei
1a.College of Materials and Textiles; 1b.Key Laboratory of Advanced Textile Materials and Manufacturing  Technology, Ministry of Education, Zhejiang SciTech University, Hangzhou 310018, China;2.Zhejiang Engineering Design Co., Ltd., Hangzhou 310002, China
关键词:
氟硅; 聚甲基丙烯酸甲酯; 嵌段共聚物; 共混; 表面性质
分类号:
O634.4
文献标志码:
A
摘要:
将不同质量分数的氟硅与甲基丙烯酸甲酯嵌段共聚物（PMTFPS-b-PMMA）和甲基丙烯酸甲酯（PMMA）配制成2.00 wt%溶液，经旋涂、退火处理后得到共混聚合物膜。以水、二碘甲烷和甲酰胺为参比液，利用接触角测试仪测定了共混聚合物膜的表面能。研究结果表明：当共混聚合物中PMTFPS链段含量在由0.28 wt%增大至5.67 wt%时，表面能从26.90 mN/m降到14.49 mN/m，共混物涂膜表面氟元素的相对含量从0.93%急剧增加到14.27%；随PMTFPS链段含量的进一步增加，共混物膜表面能仅略有下降，表面氟含量增加也不明显，说明此时共混物膜的表面组成已趋于稳定。

参考文献/References:

［1］ MEDURI B, BOUTEVIN B, KOSTOV G. Fluoroelastomers: synthesis, properties and applications［J］. Progress in Polymer Science,2001,26(1):105-187.
［2］ JIANGJ, ZHANG G, WANG Q, et al. Novel fluorinated polymers containing short perfluorobutylside chains and their super wetting performance on diverse substrates［J］. ACS Applied Materials& Interfaces,2016,8(16):10513-10523.
［3］ JIANGW, GROZEA C M, SHI Z, et al. Fluorinated raspberrylike polymer particles for superamphiphobiccoatings［J］. ACS Applied Materials & Interfaces,2014,6(4):2629-2638.
［4］ POUGET E, TONNAR J, LUCAS P, et al. Well  architectured poly (dimethylsiloxane)containing copolymers obtained by radical chemistry［J］. Chemical Reviews,2010,110(3):1233-1277.

相似文献/References:

[1]田小平,易玲敏,孟晓美.聚醚改性氟硅表面活性剂的合成与溶液性质研究[J].浙江理工大学学报,2014,31-32(自科6):636.
　TIAN Xiao ping,YI Ling min,MENG Xiao mei.Research on Synthesis and Solution Properties of Polyether Modified Fluorosilicone Surfactant[J].Journal of Zhejiang Sci-Tech University,2014,31-32(自科6):636.
[2]孟晓美,易玲敏,陈睿文.退火对PMTFPS b PS电纺膜表面性质的影响[J].浙江理工大学学报,2014,31-32(自科6):641.
　MENG Xiao mei,YI Ling min,CHEN Rui wen.Effect of Annealing on Surface Properties of PMTFPS b PS Electro spinning Film[J].Journal of Zhejiang Sci-Tech University,2014,31-32(自科6):641.
[3]张佳文,易玲敏,徐凯,等.PMTFPS-b-PMAA嵌段共聚物的合成与胶束化[J].浙江理工大学学报,2015,33-34(自科6):761.
　Zhang Jia wen,YI Ling min,Xu Kai,et al.Synthesis and Micellization of PMTFPS-b-PMAA Block Copolymers[J].Journal of Zhejiang Sci-Tech University,2015,33-34(自科6):761.
[4]王明乾,易玲敏,李静,等.涂层厚度对氟硅与甲基丙烯酸甲酯嵌段共聚物表面微观形貌和性质的影响[J].浙江理工大学学报,2017,37-38(自科1):31.
　WANG Mingqian,YI Lingmin,LI Jing,et al.The Influence of Film Thickness on Surface Microtopography and Properties  of Block Copolymers of Fluorosilicone and Methyl Methacrylate[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科6):31.

备注/Memo

备注/Memo:
收稿日期： 2017-05-12
网络出版日期： 2017-08-07
基金项目： 国家自然科学基金项目（21276243）
作者简介： 王爱瑞（1990-），女，安徽蚌埠人，硕士研究生，主要从事有机氟硅功能材料方面的研究
通信作者： 易玲敏，教授，E-mail: lmyi@zstu.edu.cn
更新日期/Last Update: 2017-11-16