Effect of Hybrid Coating on the Interfacial Property of GlassFiber/Epoxy Composite Processed at High Temperature
文章编号:
1673-3851 (2017) 06-0785-05
作者:
赵永振水兴瑶董余兵傅雅琴
浙江理工大学材料与纺织学院,杭州 310018
Author(s):
ZHAO Yongzhen SHUI Xingyao DONG YubingFU Yaqin
College of Materials and Textiles, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
杂化涂层玻璃纤维环氧树脂界面剪切强度耐热性能
分类号:
TB332
文献标志码:
A
摘要:
以杂化涂层处理后的玻璃纤维(GF)为增强材料,以环氧树脂(EP)为基体,制备出单根GF/EP复合材料。利用扫描电镜(SEM)观察和单纤维复合材料断裂试验,对高温热处理后的复合材料断面形貌和界面剪切强度进行分析。结果表明:杂化涂层的存在降低了GF与EP基体间热线性膨胀系数不匹配性,使GF/EP复合材料的耐热性能得到有效提高,其界面剪切强度较未改性前提高了68.9%。

参考文献/References:

[1] LIU Z, ZHANG L, YU E, et al. Modification of glass fiber surface and glass fiber reinforced polymer composites[J]. Current Organic Chemistry,2015,19(11):991-1010.
[2] KECHAOU B, SALVIA M, BENZARTI K, et al. Role of fiber/matrix interphases on dielectric, friction, and mechanical properties of glass fiberreinforced epoxy composites[J]. Journal of Composite Materials,2011,-46(2):131-144.
[3] WU H F, DWIGHT D W, HUFF N T. Effects of silane coupling agents on the interphase and performance of glassfiberreinforced polymer composites[J]. Composites Science and Technology,1997,57(8):975-983.
[4] DIBENEDETTO A T. Tailoring of interfaces in glass fiber reinforced polymer composites: a review[J]. Materials Science and Engineering: A,2001,302(1):74-82.
[5] YANG L, THOMASON J L. Effect of silane coupling agent on mechanical performance of glass fibre[J]. Journal of Materials Science,2012,48(5):1947-1954.
[6] PARK S J, JIN J S. Effect of silane coupling agent on interphase and performance of glass fibers/unsaturated polyester composites[J]. Journal of Colloid and Interface Science,2001,242(1):174-179.
[7] WANG W, DIBENEDETTO A T. A modified silane treatment for superior hydrolytic stability of glass reinforced composites[J]. The Journal of Adhesion,1998,68(3/4):183-201.
[8] KECHAOU B, SALVIA M, BENZARTI K, et al. Role of fiber/matrix interphases on dielectric, friction, and mechanical properties of glass fiberreinforced epoxy composites[J]. Journal of Composite Materials,2011,46(2):131-144.

相似文献/References:

[1]边晓川,方园,居婷婷,等. 玻璃纤维字型三维立体织物的设计和织造[J].浙江理工大学学报,2011,28(05):705.
 BIAN Xiao chuan,FANG Yuan,JU Ting ting,et al. The Designing and Weaving of ThreeDimensionalShape of Glass Fiber Fabric[J].Journal of Zhejiang Sci-Tech University,2011,28(自科6):705.
[2]孔春凤,田伟,翁浦莹,等.高性能纤维层叠复合材料的抗冲击性能研究[J].浙江理工大学学报,2016,35-36(自科3):367.
 KONG Chunfeng,TIAN Wei,WENG Puying,et al.Impact Resistance of High Performance  Fiber Laminated Composite Materials[J].Journal of Zhejiang Sci-Tech University,2016,35-36(自科6):367.

备注/Memo

备注/Memo:
收稿日期: 2017-01-03
网络出版日期: 2017-03-28
基金项目: 国家自然科学基金项目(51473147)
作者简介: 赵永振(1989-),男,河南商丘人,硕士研究生,主要从事纤维复合材料界面性能方面研究
通信作者: 傅雅琴,E-mail: fyq01@zstu.edu.cn
更新日期/Last Update: 2017-11-16