纳米Fe-3O-4/超支化聚合物制备及性能()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第37-38卷
期数:
2017年自科4期
页码:
491-496
栏目:
出版日期:
2017-07-10

文章信息/Info

Title:
Preparation and Properties of Fe-3O-4/Hyperbranched Polymer Nanoparticles
文章编号:
1673-3851 (2017) 04-0491-06
作者:
杨晓苏; 吴明华; 余德游; 田丽
浙江理工大学，a.先进纺织材料与制备技术教育部重点实验室;b.生态染整技术教育部工程研究中心，杭州 310018
Author(s):
YANG Xiaosu; WU Minghu; YU Deyou; TIAN Li
a. Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministryof Education; b. Engineering Research Center for EcoDyeing ＆ Finishing of Textiles, Ministry of Education, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
超支化聚合物; 纳米Fe-3O-4; 粒径; 催化降解
分类号:
TS190.3
文献标志码:
A
摘要:
为了提高纳米Fe-3O-4的分散性，以马来酸酐改性超支化聚合物（简称超支化物）为模板，采用原位共沉淀法制备纳米Fe-3O-4/超支化物(Fe-3O-4/HB)，并将Fe-3O-4/HB应用于催化双氧水降解染料。分析了铁盐比例（ n Fe2+∶n Fe3+）、超支化物与FeCl2质量比（m-HB∶m-FeCl2）、吸附配位反应时间和共沉淀反应pH值对纳米Fe-3O4粒径的影响，并对纳米Fe-3O4/HB催化降解性能进行了测试。结果表明：纳米Fe-3O-4/HB制备的优化条件为：n-Fe2+∶n-Fe3+为1∶1.8，m-HB∶m-FeCl2为7.5∶1，吸附配位反应时间4 h，共沉淀反应pH值为11，所得纳米Fe-3O-4平均粒径为116.3 nm。Fe-3O-4/HB在中性条件下催化双氧水降解活性KN-G 60 min，其降解率可达到99.8%。相比于无超支化物为模板制备的纳米Fe-3O-4，实验所得纳米Fe-3O-4粒径小，分散性和催化降解性能明显提高。

参考文献/References:

［1］ GAO L, ZHUANG J, NIE L, et al. Intrinsic peroxidaselike activity of ferromagnetic nanoparticles［J］. Nature Nanotechnology,2007,2(9）:577-583.
［2］ SUGIMOTO T, MATIJEVIC〖DD（〗′〖DD)〗 E. Formation of uniform spherical magnetite particles by crystallization from ferrous hydroxide gels［J］. Journal of Colloid and Interface Science,1980,74(1）:227-243.
［3］ XU J, YANG H, FU W, et al. Preparation and magnetic properties of magnetite nanoparticles by solgel method［J］. Journal of Magnetism and magnetic Materials,2007,309(2）:307-311.
［4］ DENG H, LI X, PENG Q, et al. Monodisperse magnetic singlecrystal ferrite microspheres［J］. Angewandte Chemie,2005,117(18）:2842-2845.
［5］ FELTIN N, PILENI M P. New technique for synthesizing iron ferrite magnetic nanosized particles［J］. Langmuir,1997,13(15）:3927-3933.
［6］ LIN F, CHEN W, LIAO Y H, et al. Effective approach for the synthesis of monodisperse magnetic nanocrystals and MFe3O4 (M= Ag, Au, Pt, Pd) heterostructures［J］. Nano Research,2011,4(12）:1223-1232.
［7］ BALOGH L, SWANSON D R, TOMALIAO D A, et al. Dendrimersilver complexes and nanocomposites as antimicrobial agents［J］. Nano Letters,2001,1(1）:18-21.
［8］ 朱广谦,何青科,刘长庚,等.Fe3O4磁性纳米粒子的制备及其表面修饰［J］.湖南师范大学自然科学学报,2016,39(3）:46-55.
［9］ 袁文俊,周勇敏.纳米颗粒团聚的原因及解决措施［J］.材料导报:纳米与新材料专辑,2008,22(3）:59-61.

备注/Memo

备注/Memo:
收稿日期： 2016-10-12
网络出版日期： 2017-01-19
作者简介： 杨晓苏(1991-)，女，湖北荆州人，硕士研究生，主要从事生态染整废水处理方面的研究
通信作者： 吴明华，E-mail : wmh@zstu.edu.cn
更新日期/Last Update: 2017-09-25