[1]戴霄霞,殷英,周青,等.有机硅改性聚丙烯酸酯预处理对涤棉织物喷墨印花性能的影响[J].浙江理工大学学报,2024,51-52(自科五):681-690.
　DAI Xiaoxia,YIN Ying,ZHOU Qing,et al.Influence of silicone modified polyacrylate pretreatment on the digital printing performance of polyester cotton fabrics[J].Journal of Zhejiang Sci-Tech University,2024,51-52(自科五):681-690.
点击复制

有机硅改性聚丙烯酸酯预处理对涤棉织物喷墨印花性能的影响()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第51-52卷
期数:
2024年自科第五期
页码:
681-690
栏目:
出版日期:
2024-09-20

文章信息/Info

Title:
Influence of silicone modified polyacrylate pretreatment on the digital printing performance of polyester cotton fabrics
作者:
戴霄霞; 殷英; 周青; 沈一峰
1.浙江理工大学纺织科学与工程学院（国际丝绸学院），杭州 310018；2.浙江省现代纺织技术创新中心，浙江绍兴 312000；3.浙江理工大学绍兴柯桥研究院，浙江绍兴 312000
Author(s):
DAI Xiaoxia;  YIN Ying;  ZHOU Qing;  SHEN Yifeng
1.College of Textiles Science and Engineering (International Institute of Silk), Zhejiang Sci-Tech  University, Hangzhou 310018, China; 2.Zhejiang Provincial Innovation Center of Advanced  Textile Technology, Shaoxing 312000, China; 3.Shaoxing Keqiao Research Institute of Zhejiang SciTech University, Shaoxing 312000, China
关键词:
涂料喷墨印花; 硅烷偶联剂; 聚丙烯酸酯乳液; 预处理; 印花性能
分类号:
TS195-6
文献标志码:
A
摘要:
为提升涤棉织物涂料喷墨印花工艺的印花性能，采用半连续种子乳液聚合法，以醋酸乙烯酯（VA）、丙烯酸丁酯（BA）和丙烯酸异辛酯（EHA）为共聚单体，丙烯酸羟乙酯（HEA）为功能单体，引入硅烷偶联剂（KH 1706），制备得到有机硅改性聚丙烯酸酯乳液（KH1706/PVAc），并将其作为预处理液应用于涤棉织物；探究引入不同质量分数的KH 1706对乳液烘干后所得乳胶膜性能的影响，并分析以KH 1706/PVAc为预处理液对涤棉织物涂料喷墨印花性能的影响。结果表明：当引入KH 1706的质量分数为2%时，乳胶膜具有较好的热稳定性和耐水性，吸水率为16.8%；乳液运用于涤棉织物预处理后，有效抑制了墨滴在织物上的渗化，墨滴渗化面积为20.8 mm2；预处理后印花织物耐湿摩擦牢度提高半级，印花精细度提升约13%，并且复杂图案打印后仍具有较好的印花效果，表现出良好的综合印花性能。该研究可为提升涤棉织物涂料喷墨印花的印花性能提供理论参考。

参考文献/References:

［1］AliShah M, Lee D G, Lee B Y, et al. Classifications and applications of inkjet printing technology: A review［J］. IEEE Access, 2021, 9: 140079-140102.
［2］张健军, 赵志慧, 陈为超. 墨水性能优化和预处理提高纺织品喷墨印花效果研究进展［J］. 分子科学学报, 2023, 39(5): 392-403.
［3］张鑫, 李羽佳, 杨柳, 等. 涤、棉及其混纺机织物颜料墨水扩散特性与数码印花质量研究［J］. 东华大学学报(自然科学版), 2022, 48(4): 20-27.
［4］AbdelHakeim O, Rashed S A, Diab H A. Influence of aminopropyl/vinyl/silsesquioxane post-treatment on the colour performance of pigment-based inks on ink-jet-printed polyester fabrics［J］. Coloration Technology, 2021, 137(6): 587-603.
［5］GaoC Y, Xing T L, Hou X N, et al. Clean production of polyester fabric inkjet printing process without fabric pretreatment and soaping［J］. Journal of Cleaner Production, 2021, 282: 124315.
［6］杨海贞, 房宽峻, 刘秀明, 等. 喷墨印花预处理对织物组织结构的影响［J］. 纺织学报, 2019, 40(5): 84-90.
［7］ZhangM, Qiao X R, Liu X M, et al. Environmental urea-free pretreatment process to form new surface on hemp for enhancing the inkjet printing performance［J］. Progress in Organic Coatings, 2023, 174: 107317.
［8］LiangY C, Liu X M, Fang K J, et al. Construction of new surface on linen fabric by hydroxyethyl cellulose for improving inkjet printing performance of reactive dyes［J］. Progress in Organic Coatings, 2021, 154: 106179.
［9］AnF F, Fang K J, Liu X M, et al. Rheological properties of carboxymethyl hydroxypropyl cellulose and its application in high quality reactive dye inkjet printing on wool fabrics［J］. International Journal of Biological Macromolecules, 2020, 164: 4173-4182.
［10］刘尊东. 棉织物的聚合物改性与喷墨印花效果［D］. 天津: 天津工业大学, 2017: 53-57.

相似文献/References:

[1]宋文敏,陈晨,江明明,等.硅烷偶联剂对咖啡渣的表面改性及其对咖啡渣/聚丙烯木塑复合材料性能的影响[J].浙江理工大学学报,2023,49-50(自科五):560.
　SONG Wenmin,CHEN Chen,JIANG Mingming,et al.Surface modification of spent coffee grounds by the silane coupling agent and its effect on the properties of spent coffee grounds/polypropylene wood plastic composites[J].Journal of Zhejiang Sci-Tech University,2023,49-50(自科五):560.

备注/Memo

备注/Memo:
收稿日期： 2024-01-24
网络出版日期：2024-05-22
基金项目： 浙江省基础公益研究计划项目（LQ21E030017）
作者简介： 戴霄霞（1997—），浙江平湖人，硕士研究生，主要从事织物涂层整理方面的研究
通信作者： 沈一峰，E-mail：shenyf66@sina.com
更新日期/Last Update: 2024-09-18