|本期目录/Table of Contents|

[1]陈鼎,张亚飞,卢旦,等.大型木丝水泥墙板的力学性能试验研究[J].浙江理工大学学报,2023,49-50(自科三):396-403.
　CHEN Ding,ZHANG Yafei,LU Dan,et al.Experimental study on the mechanical properties of large scale wood wool cement wall panels[J].Journal of Zhejiang Sci-Tech University,2023,49-50(自科三):396-403.
点击复制

大型木丝水泥墙板的力学性能试验研究()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第49-50卷
期数:
2023年自科第三期
页码:
396-403
栏目:
出版日期:
2023-05-31

文章信息/Info

Title:
Experimental study on the mechanical properties of large scale wood wool cement wall panels
文章编号:
1673-3851 (2023) 05-0396-08
作者:
陈鼎; 张亚飞; 卢旦; 杨博
1.浙江交工集团股份有限公司地下工程分公司，杭州 311400；2.浙江理工大学建筑工程学院，杭州 310018；3.华东建筑设计研究院有限公司，上海 200041
Author(s):
CHEN Ding;  ZHANG Yafei;  LU Dan;  YANG Bo
1.Underground Branch, Zhejiang Communications Construction Group Co., Ltd., Hangzhou  311400, China; 2. School of Civil Engineering and Architecture, Zhejiang Sci-Tech University, Hangzhou 310018, China; 3. East China Architectural Design & Research  Institute Co., Ltd., Shanghai 200041, China
关键词:
大型木丝水泥墙板; 抗压性能; 抹灰效果; 抗折性能; 抗弯性能
分类号:
TB332
文献标志码:
A
摘要:
为了研究大型木丝水泥墙板的力学性能，以220 mm板厚的大型木丝水泥墙板上裁取的不同规格墙板为试验对象，进行了抗压性能、3点和4点抗折性能及抗弯性能试验研究。试验结果表明：木丝水泥复合墙板平行板面方向的抗压强度比垂直板面方向高，垂直板面方向的抗压强度按照行业标准《木丝水泥板》（JG/T 357—2012），以压缩10%的应力作为其抗压强度的表征；木丝水泥复合墙板表面抹灰能够提高其平行板面方向的抗压强度，其中钢筋增强抹灰层的效果最为明显。不同抗折试验引起不同的受力状态以及过高的含水率都会对木丝水泥复合墙板的抗折强度产生不利影响，导致3点抗折试验所得抗折强度高于4点抗折试验的强度；木丝水泥复合墙板的抗弯承载能力和挠度均满足相应规范要求，表现出了较好的韧性，但不能完全满足板表面抗开裂的要求。该研究结果可为大型木丝水泥墙板的工程应用提供理论指导。

参考文献/References:

［ 1 ］赵狄荣 , 赵彦 . 水泥木丝板［ J ］ . 新型建筑材料 , 2010, 37(11): 95 - 99.

［2］Ashori A, Tabarsa T, Azizi K, et al. Wood-wool cement board using mixture of eucalypt and poplar［J］. Industrial Crops and Products, 2011, 34(1): 1146-1149.

［3］徐学东, 段绪胜, 赵守杰, 等.木丝水泥板建造环保节能农村住房的试验研究［J］. 新型建筑材料, 2010, 37(5): 45-48.

［4］葛召深, 王静, 吴广彬, 等. 木丝水泥板在我国的研究进展及应用［J］. 建筑技术, 2018, 49(5): 499-502.

［5］战剑锋. 荷兰的木质水泥板新技术［J］. 林业机械与木工设备, 1999, 27(2): 30-32.

［6］Mattias R. Full wall element of cement stabilised wood wool, method to produce it and building method using it: EP1786988B1［P］. 2011-02-23.

［7］Elten G. Cement bonded particle board (CBPB) and wood strand cement board, production, properties and appications ［C］// 10th International Inorganic-Bonded Fiber Composites Conference (IIBCC). Sao Paulo: Idaho Press, 2006: 206-217.

［8］Elten G. New developed Eltomation plant capable to produce all Types of wood wool cement board (WWCB)-wood strand cement board (WSCB-Eltoboard) and-large WWCB wall elements ［C］//11th International Inorganic-Bonded Fiber Composites Conference (IIBCC). Madrid: Idaho Press, 2008: 188-197.

［9］涂平涛. 水泥木丝板及其生产技术解析［J］. 墙材革新与建筑节能, 2005(11): 28-31.

［10］Elten E. New developments in the field of wood cement products, applications and production technologies ［C］// 12th International Inorganic-Bonded Fiber Composites Conference (IIBCC), Aalborg, Idaho Press, 2010: 260-270.

undefined

备注/Memo

备注/Memo:
收稿日期： 2022-06-23
网络出版日期：2022-12-05
基金项目： 国家自然科学基金项目(51808499)；浙江省基础公益研究计划项目(LGG20E080002)
作者简介： 陈鼎（1993—），男，杭州人，硕士研究生，主要从事市政工程方面的研究
通信作者： 杨博，E-mail：youngbo@zstu.edu.cn
更新日期/Last Update: 2023-09-08