腰果酚基苯并噁嗪增韧二胺型苯并噁嗪及其性能()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第47-48卷
期数:
2022年自科第三期
页码:
348-356
栏目:
出版日期:
2022-05-10

文章信息/Info

Title:
Cardanol based benzoxazine toughen diamine benzoxazine and  properties of copolymer resins
文章编号:
1673-3851(2021)05-0348-09
作者:
孙浩然; 金子毅; 胡欣悦; 温小东; 付飞亚; 刘向东
浙江理工大学材料科学与工程学院，杭州310018
Author(s):
SUN Haoran;  JIN Ziyi;  HU Xinyue;  WEN Xiaodong;  FU Feiya;  LIU Xiangdong
School of Materials Science & Engineering, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
苯并噁嗪; 腰果酚; 共聚; 增韧; 自增塑作用
分类号:
TB324
文献标志码:
A
摘要:
以腰果酚与苯胺为原料合成了腰果酚-苯胺苯并噁嗪（C-A），然后将其与二胺型苯并噁嗪-4，4-二氨基二苯甲烷型苯并噁嗪（PH-DDM）进一步共聚，利用腰果酚间位长脂肪链的自增塑作用来改善共聚树脂韧性，从而改进传统聚苯并噁嗪脆性大的缺点。通过示差扫描量热法、动态热力学分析、热重分析以及拉伸测试等表征方法研究了共聚树脂的动态力学性能、热稳定性和机械性能，结果表明：当PH-DDM/C-A的摩尔比为2-5∶1时，1）聚苯并噁嗪树脂的玻璃化转变温度能保持在175℃以上，800℃下残炭率在39%以上,热稳定性保持稳定。2）聚苯并噁嗪树脂拉伸断裂应力达到57MPa，断裂伸长率增加到3-38%,相比于纯PH-DDM提高了20%。本文验证了腰果酚基苯并噁嗪对传统苯并噁嗪树脂增韧的有效性，对开拓苯并噁嗪的应用范围具有参考意义。以腰果酚与苯胺为原料合成腰果酚-苯胺苯并噁嗪（C-A），然后将其与二胺型苯并噁嗪-4，4-二氨基二苯甲烷型苯并噁嗪（PH-DDM）进一步共聚，利用腰果酚间位长脂肪链的自增塑作用来改善共聚树脂韧性，从而改进传统聚苯并噁嗪脆性大的缺点。通过示差扫描量热法、动态热力学分析、热重分析以及拉伸测试等表征方法研究共聚树脂的动态力学性能、热稳定性和机械性能。结果表明：当PH-DDM/C-A的摩尔比为2-5∶1时，聚苯并噁嗪共聚树脂的玻璃化转变温度能保持在175℃以上，800℃下残炭率在39%以上，表明聚苯并噁嗪共聚树脂的热稳定性较为稳定；聚苯并噁嗪共聚树脂拉伸断裂应力达到57MPa，断裂伸长率增加到3-38%，相比于纯PH-DDM提高了20%。本文验证了腰果酚基苯并噁嗪对传统苯并噁嗪树脂增韧的有效性，对开拓苯并噁嗪的应用范围具有参考意义。

参考文献/References:

［1］IshidaH,AgagT.HandbookofBenzoxazineResins［M］.Amsterdam:Elsevier,2011:3-30.
［2］ShaXL,YuanL,LiangGZ,etal.Preparationofhighperformancebio-basedbenzoxazineresinthroughagreensolvent-freestrategyforshapememoryapplication［J］.Polymer,2020,202:122673.
［3］DoganYE,SatilmisB,UyarT.Synthesisandcharacterizationofbio-basedbenzoxazinesderivedfromthymol［J］.JournalofAppliedPolymerScience,2019,136(17):47371.
［4］DumasL,BonnaudL,OlivierM,etal.Bio-basedhighperformancethermosets:Stabilizationandreinforcementofeugenol-basedbenzoxazinenetworkswithBMIandCNT［J］.EuropeanPolymerJournal,2015,67:494-502.
［5］LouYJ,ZhaoZX,ChenZW,etal.Processabilityimprovementofa4-vinlyguiacolderivedbenzoxazineusingreactivediluents［J］.Polymer,2019,160:316-324.
［6］WangCF,SunJQ,LiuXD,etal.Synthesisandcopolymerizationoffullybio-basedbenzoxazinesfromguaicol,furfurlamineandsteaylamine［J］.GreenChemistry,2012,14:2799-2806.
［7］YoshikawaT,YagiT,ShinoharaS,etal.Productionofphenolsfromligninviadepolymerizationandcatalyticcracking［J］.Fuelprocessingtechnology,2013,108:69-75.
［8］QianZZ,ZhengYL,LiQ,etal.Amidationwayofdiphenolicacidforpreparingbiopolybenzoxazineresinwithoutstandingthermalperformance［J］.ACSSustainableChemistryandEngineering,2021,9(12):4668-4680.
［9］YoshikawaT,ShinoharaS,YagiT,etal.Productionofphenolsfromlignin-derivedslurryliquidusingironoxidecatalyst［J］.AppliedCatalysisB,2014,146:289-297.
［10］LinCM,ChenCH,LinCH,etal.High-Performancebio-basedbenzoxazinesfromderivedfromphosphoratedbiphenolsandfurfurylamine［J］.EuropeanPolymerJournal,2018,108:48-56.

相似文献/References:

[1]周杰,徐豫松,张涛,等.苯并噁嗪与木质素磺酸钠协同阻燃聚酯复合材料的性能分析[J].浙江理工大学学报,2024,51-52(自科二):180.
　ZHOU Jie,XU Yusong,ZHANG Tao,et al.Performance analysis of the synergistic flame retardant polyester composite of benzoxazine and sodium lignosulfonate[J].Journal of Zhejiang Sci-Tech University,2024,51-52(自科三):180.
[2]王海青,曹万荣,李光旭,等.腰果酚基苯并噁嗪及其高生物质含量复合材料的制备和性能研究[J].浙江理工大学学报,2016,35-36(自科1):29.
　WANG Haiqing,CAO Wanrong,LI Guangxu,et al.Preparation and Properties of Cardanol based Benzoxazine and Its Composites with High Biomass Content[J].Journal of Zhejiang Sci-Tech University,2016,35-36(自科三):29.

备注/Memo

备注/Memo:
收稿日期：2021-07-12
网络出版日期：2021-11-17
基金项目：国家自然科学基金项目（51873195）
作者简介：孙浩然(1998-)，男，山东烟台人，硕士研究生，主要从事有机合成方面的研究
通信作者：刘向东，E-mail:liuxd@zstu.edu.cn
更新日期/Last Update: 2022-05-27