[1]蔡菲,杲爽,孙锦涛,等.沉淀法改性聚磷酸铵及其在水性环氧树脂中的阻燃性能[J].浙江理工大学学报,2022,47-48(自科一):1-8.
　CAI Fei,GAO Shuang,SUN Jintao,et al.Precipitationmodified ammonium polyphosphate and its flame retardant properties in waterborne epoxy resin[J].Journal of Zhejiang Sci-Tech University,2022,47-48(自科一):1-8.
点击复制

沉淀法改性聚磷酸铵及其在水性环氧树脂中的阻燃性能()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第47-48卷
期数:
2022年自科第一期
页码:
1-8
栏目:
出版日期:
2022-01-31

文章信息/Info

Title:
Precipitationmodified ammonium polyphosphate and its flame retardant properties in waterborne epoxy resin
文章编号:
1673-3851 (2022) 01-0001-08
作者:
蔡菲; 杲爽; 孙锦涛; 孙同同; 司银松; 傅雅琴
1.浙江理工大学材料科学与工程学院，杭州 310018；2.西安康本材料有限公司，西安 710089
Author(s):
CAI Fei; GAO Shuang; SUN Jintao; SUN Tongtong; SI Yinsong; FU Yaqin
1. School of Materials Science & Engineering, Zhejiang Sci-Tech University, Hangzhou 310018, China; 2. Xi′an Carbon Materials Co., Ltd., Xi′an 710089, China
关键词:
聚磷酸铵; 氢氧化铝; 沉淀法改性; 阻燃水性环氧树脂
分类号:
TB332
文献标志码:
A
摘要:
为了解决聚磷酸铵（Ammonium polyphosphate，APP）水溶度高以及与聚合物基体相容度差的问题，在APP表面原位合成超细氢氧化铝（Aluminium hydroxide，ATH）粒子，探讨反应时间、反应温度和无水氯化铝用量对反应结果的影响，并通过与水性环氧树脂（Waterborne epoxy，WEP）的结合验证改性方案的有效性。结果表明：当温度为60 ℃、无水氯化铝用量为2 g和反应时间为2 h时，APP的水溶度从0-95 g/（100 mL）降低到0-22 g/（100 mL），比表面积从1-24 m-2/g增大到15-36 m-2/g；SEM图显示APP表面由光滑变得粗糙，TEM图表明ATH粒子分布在APP的表面；通过FTIR、XRD测试证明包覆在APP表面的为ATH粒子，TGA测试表明ATH@APP的残炭量显著升高；将改性后的APP与WEP结合后发现，表面粗糙度的提高有效提高了APP在聚合物基体中的相容度，燃烧测试也表明改性APP/WEP样条可以产生更厚更稳定的炭化层，以抑制进一步的燃烧，证实了沉淀法改性的APP可以有效提高WEP阻燃性能。

参考文献/References:

［1］ Chen X X, Shen J H, Wan M, et al. Comparative study on flame retardancy of multiple solid super acidscontaining epoxy resin composites［J］. Materials Today Communications, 2020, 25: 101436.
［2］ Shi X H, Xu Y J, Long J W, et al. Layerbylayer assembled flameretardant architecture toward highperformance carbon fiber composite［J］. Chemical Engineering Journal, 2018, 353: 550-558.
［3］ 高喜平, 李小童, 齐晨晨, 等. 纳米无机粒子协同聚磷酸铵阻燃高分材料的研究进展［J］. 化工新型材料, 2019, 47(5): 27-31.
［4］ He X, Zhang W, Yi D, et al. Flame retardancy of ammonium polyphosphatemontmorillonite nanocompounds on epoxy resin［J］. Journal of Fire Sciences. 2016, 34(3): 212-225.
［5］ Liu Y, He J, Yang R. The effects of aluminum hydroxide and ammonium polyphosphate on the flame retardancy and mechanical property of polyisocyanuratepolyurethane foams［J］. Journal of Fire Sciences. 2015, 33(6): 459-472.
［6］ 郭振宇, 宁培森, 丁著明. 聚磷酸铵改性及其应用［J］. 塑料助剂, 2018(4): 21-26.
［7］ 邓钧豪, 杨进, 洪浩源, 等. 复合改性聚磷酸铵增强滤纸阻燃性［J］. 造纸科学与技术, 2019, 38(2): 62-65.
［8］ Tian D B, He Y J, Wang T T, et al. Study on the hydrophobic modification of ammonium polyphosphate and its application in flame retardant polypropylene［J］. Materials Science Forum, 2016, 852: 726-732.
［9］ Pan Y T, Luo Z L, Wang B B. Crosslinking modification of ammonium polyphosphate via ionic exchange and selfassembly for enhancing the fire safety properties of polypropylene［J］. Polymers, 2020, 12(11): 2761.
［10］Kang X, Liu Y, Chen N, et al. Influence of modified ammonium polyphosphate on the fire behavior and mechanical properties of polyformaldehyde［J］. Journal of Applied Polymer Science, 2020,138(14): 50156.

相似文献/References:

[1]朱善文,陈帅杰,王恩亮,等.聚磷酸铵/水性环氧形状记忆阻燃复合材料制备及其性能[J].浙江理工大学学报,2019,41-42(自科六):786.
　ZHU Shanwen,CHEN Shuaijie,WANG Enliang,et al.Preparation and properties of ammonium polyphosphate/waterborne  epoxy shape memory and flame retardant composites[J].Journal of Zhejiang Sci-Tech University,2019,41-42(自科一):786.

备注/Memo

备注/Memo:
收稿日期：2021-03-06
网络出版日期：2021-04-27
基金项目：国家自然科学基金项目(52003243)
作者简介：蔡菲(1995-)，女，江苏盐城人，硕士研究生，主要从事阻燃复合材料方面的研究
通信作者：傅雅琴，E-mail：fyq01@zstu.edu.cn
更新日期/Last Update: 2022-03-08