　FANG Desheng,LIN Ping,WU Fengmin,et al.Photoelectric detection performance and stability of MAPbX3(X=I, Br, Cl) single crystal detectors under ultraviolet light[J].Journal of Zhejiang Sci-Tech University,2021,45-46(自科一):48-55.
点击复制

甲胺基铅卤钙钛矿单晶探测器在紫外光下的光电探测性能及稳定性()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第45-46卷
期数:
2021年自科第一期
页码:
48-55
栏目:
出版日期:
2021-01-16

文章信息/Info

Title:
Photoelectric detection performance and stability of MAPbX3(X=I, Br, Cl) single crystal detectors under ultraviolet light
文章编号:
1673-3851 (2021) 01-0048-08
作者:
方德胜; 林萍; 吴锋民; 崔灿
浙江理工大学理学院，杭州 310018
Author(s):
FANG Desheng;  LIN Ping;  WU Fengmin;  CUI Can
School of Science, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
甲胺基铅卤钙钛矿; 单晶; 光电探测器; 探测性能; 稳定性
分类号:
TN36
文献标志码:
A
摘要:
为了探究甲胺基铅卤钙钛矿MAPbX3(X=I, Br, Cl)单晶探测器的光电探测性能及稳定性，将利用逆温结晶法制备好的MAPbX3(X=I, Br, Cl)单晶蒸镀叉指电极，制作成单晶探测器器件，在365 nm和254 nm两种紫外光照射条件下，研究三种单晶器件在不同光强下的探测性能及稳定性。结果表明：在相同电压下，MAPbX3(X=I, Br, Cl)三种单晶器件的响应率、外量子效率及探测率都随着光强的升高而降低。MAPbI3稳定性较好，在两种波长下的光暗电流比均为49；MAPbBr3光暗电流比略佳，在365 nm及254 nm波长下分别达到122和51，然而其稳定性较差；MAPbCl3稳定性较好，但光暗电流比较低，分别为18和14。钙钛矿单晶探测器在365 nm及254 nm光照下的光电探测性能可为探测器器件设计及性能优化提供参考。

参考文献/References:

［1］ Monroy E, Omn s F, Calle F. Widebandgap semiconductor ultraviolet photodetectors［J］. Semiconductor Science and Technology, 2003, 18(4): R33-R51.
［2］ Ghezzi D, Antognazza M R, dal Maschio M, et al. A hybrid bioorganic interface for neuronal photoactivation［J］. Nature Communications, 2011, 2: 166.
［3］ Razeghi M, Rogalski A. Semiconductor ultraviolet detectors［J］. Journal of Applied Physics, 1996, 79(10): 7433-7473.
［4］ Manga K K, Wang J Z, Lin M, et al. Highperformance broadband photodetector using solutionprocessible PbSeTiO2graphene hybrids［J］. Advanced Materials, 2012, 24(13): 1697-1702.
［5］ Zhang H B, Zhang X J, Liu C, et al. Highresponsivity, highdetectivity, ultrafast topological insulator Bi2Se3/silicon heterostructure broadband photodetectors［J］. ACS Nano, 2016, 10(5): 5113-5122.
［6］ 朱晓秀, 葛咏, 李建军, 等. 量子点增强硅基探测成像器件的研究进展［J］. 中国光学， 2020, 13(1): 62-74.
［7］ Barone P W, Baik S, Heller D A, et al. Nearinfrared optical sensors based on singlewalled carbon nanotubes［J］. Nature Materials, 2004, 4(1): 86-92.
［8］ 陶泽军, 霍婷婷, 尹欢, 等. 基于碳管/石墨烯/GaAs双异质结自驱动的近红外光电探测器［J］. 半导体光电, 2020, 41(2): 164-168.
［9］ Jin Y Z, Wang J P, Sun B Q, et al. Solutionprocessed ultraviolet photodetectors based on colloidal ZnO nanoparticles［J］. Nano Letters, 2008, 8(6): 1649-1653.
［10］ Bie Y Q, Liao Z M, Zhang H Z, et al. Selfpowered, ultrafast, visibleblind UV detection and optical logical operation based on ZnO/GaN nanoscale pn junctions［J］. Advanced Materials, 2011, 23(5): 649-653.

备注/Memo

备注/Memo:
收稿日期：2020-06-15
网络出版日期：2020-09-03
基金项目：国家自然科学基金项目（11804300）；浙江省自然科学基金项目（LQ18A040005）
作者简介：方德胜（1993-），男，河南濮阳人，硕士研究生，主要从事甲胺基铅卤钙钛矿单晶制备及探测器光电性能方面的研究
通信作者：崔灿，E-mail: cancui@zstu.edu.cn
更新日期/Last Update: 2021-01-21