　ZHU Ying,LIU Tao,DING Xinbo,et al.Preparation and adsorption properties of oxidized cellulose aerogels[J].Journal of Zhejiang Sci-Tech University,2020,43-44(自科六):806-814.
点击复制

氧化纤维素气凝胶的制备及其吸附性能()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第43-44卷
期数:
2020年自科六期
页码:
806-814
栏目:
出版日期:
2020-11-27

文章信息/Info

Title:
Preparation and adsorption properties of oxidized cellulose aerogels
文章编号:
1673-3851 (2020) 11-0806-09
作者:
朱莹; 刘涛; 丁新波; 王莉; 郑洁
浙江理工大学，a. 纺织科学与工程学院(国际丝绸学院）；b. 科技与艺术学院，杭州 310018
Author(s):
ZHU Ying;  LIU Tao;  DING Xinbo;  WANG Li;  ZHENG Jie
a. College of Textile Science and Engineering (International Institute of Silk);  b. Keyi College, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
微晶纤维素; 高碘酸钠; 二醛纤维素; 气凝胶; 重金属吸附
分类号:
TQ352-4
文献标志码:
A
摘要:
以微晶纤维素为原材料制备二醛纤维素，然后通过冻干燥法获得氧化纤维素气凝胶，并探究氧化纤维素气凝胶去除重金属离子的能力。分析氧化时间对纤维素醛基含量的影响，利用扫描电子显微镜、红外光谱仪、热重分析仪等仪器对制备所得气凝胶的形貌和结构进行表征，优化影响气凝胶吸附性能的时间、溶液浓度和pH值等条件。结果表明：氧化纤维素醛基含量会随氧化时间在一定范围内的增加而增加，超过8 h时，醛基含量反而会下降；氧化改性6 h后的氧化纤维素气凝胶性能较优，轻质且具有高度多孔性，孔隙率高于9493%；合成的氧化纤维素气凝胶材料的吸附量在一定范围内随时间、初始浓度和pH的增加而增加，并在pH为45时最高，3600 min后达到吸附平衡，吸附量高达183401 mg/g，明显高于纤维素气凝胶，体现出优越的吸附性能，可作为一种高效吸附剂。

参考文献/References:

［1］ Hayati B, Maleki A, Najafi F, et al. Heavy metal adsorption using PAMAM/CNT nanocomposite from aqueous solution in batch and continuous fixed bed systems［J］. Chemical Engineering Journal, 2018, 346: 258-270.
［2］ Zhang J J, Shao J G, Jin Q Z, et al. Sludgebased biochar activation to enhance Pb(II) adsorption［J］. Fuel, 2019, 252: 101-108.
［3］ Venkateswarlu S, Panda A, Kim E, et al. Biopolymercoated magnetite nanoparticles and metalorganic framework ternary composites for cooperative Pb(II) adsorption［J］. ACS Applied Nano Materials, 2018, 1(8): 4198-4210.
［4］ Sharma M, Singh J, Hazra S, et al. Adsorption of heavy metal ions by mesoporous ZnO and TiO2@ZnO monoliths: Adsorption and kinetic studies［J］. Microchemical Journal, 2019,145:105-112.
［5］ Saleh T A, Gupta V K. Column with CNT/magnesium oxide composite for lead(II) removal from water［J］. Environ Pollut Res Int, 2012, 19(4):1224-1228.
［6］ Rol F, Belgacem M N, Gandini A, et al. Recent advances in surfacemodified cellulose nanofibrils［J］. Progress in Polymer Science, 2019, 88: 241-264.
［7］ 李宗红, 潘远凤, 肖惠宁, 等. 改性纤维素对重金属吸附的研究进展［J］. 金属世界, 2019(1): 36-41.
［8］ Carlsson D O, Lindh J, Nyholm L, et al. Cooxidantfree TEMPOmediated oxidation of highly crystalline nanocellulose in water［J］. Rsc Advances, 2014, 4(94): 52289-52298
［9］ Zhao D Y, Tian Y Y, Jing X F, et al. PAF1@cellulose nanofibril composite aerogel for highlyefficient removal of bisphenol A［J］. Journal of Materials Chemistry A, 2019, 7(1): 157-164.
［10］ Sheng C, Zhou Y M, Lu J N, et al. Preparation and characterization of chitosan based hydrogels chemical crosslinked by oxidized cellulose nanowhiskers［J］. Polymer Composites, 2019, 40(6): 2432-2440.

相似文献/References:

[1]朱亚娟,汪进前,盖燕芳,等.氧化纤维素负载二氧化钛的制备工艺研究[J].浙江理工大学学报,2016,35-36(自科5):668.
　ZHU Yajuan,WANG Jinqian,GE Yanfang,et al.Study on Preparation Technology of Oxycellulose Coated with Titanium Dioxide[J].Journal of Zhejiang Sci-Tech University,2016,35-36(自科六):668.
[2]关炳月,刘涛,丁新波,等.羧化纤维素气凝胶的制备及其对亚甲基蓝染料的吸附性能[J].浙江理工大学学报,2022,47-48(自科二):166.
　GUAN Bingyue,LIU Tao,DING Xinbo,et al.Preparation of carboxylated cellulose aerogel and its adsorption  properties for methylene blue dye[J].Journal of Zhejiang Sci-Tech University,2022,47-48(自科六):166.

备注/Memo

备注/Memo:
收稿日期：2020-07-28
网络出版日期：2020-09-03
基金项目：国家自然科学基金项目（31900964）；浙江理工大学研究生优秀学位论文培育基金项目（2019M24）
作者简介：朱莹（1996-），女，浙江杭州人，硕士研究生，主要从事高技术纤维制品开发方面的研究
通信作者：刘涛，E-mail:maggie_liu310@163.com
更新日期/Last Update: 2020-11-05