Title:
Preparation and properties of ammonium polyphosphate/waterborne  epoxy shape memory and flame retardant composites
文章编号:
1673-3851 (2019) 11-0786-07
作者:
朱善文; 陈帅杰; 王恩亮; 黄云峰; 董余兵
浙江理工大学材料与纺织学院、丝绸学院，杭州 310018
Author(s):
ZHU Shanwen;  CHEN Shuaijie;  WANG Enliang;  HUANG Yunfeng;  DONG Yubing
Silk Institute, College of Materials and Textiles, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
水性环氧树脂; 聚磷酸铵; 形状记忆性能; 阻燃性能
分类号:
TB332
文献标志码:
A
摘要:
以水性环氧树脂（Waterborne epoxy, WEP）为基体，聚磷酸铵（Ammonium polyphosphate, APP）为阻燃剂，采用机械共混、冷冻干燥和热压成型工艺制备APP/WEP形状记忆阻燃复合材料，期望获得一种兼具优良形状记忆性能和阻燃性能的复合材料。通过SEM、TGA、DSC、TMA、万能试验机、极限氧指数测试仪分别对APP/WEP复合材料进行了表征与分析。结果表明：与WEP相比，APP/WEP复合材料的阻燃性能得到了显著提高。WEP的极限氧指（Limited oxygen index, LOI）为182%，当APP质量分数为200%时，APP/WEP复合材料的LOI值高达276%；另外，APP/WEP复合材料仍保持较好的形状记忆性能，即使APP质量分数增至500%时，其形状固定率和形状回复率仍分别高达905%和970%。因此，其复合材料是一种兼具阻燃和形状记忆多功能复合材料，该复合材料的制备工艺可为拓宽WEP及其复合材料的应用奠定材料基础和实验参考。

参考文献/References:

［1］ 魏堃, 朱光明, 唐玉生, 等.热固性环氧树脂形状记忆聚合物的研究进展［J］. 高分子材料科学与工程, 2012, 28(8): 183-186.
［2］ Jozsef K K, Sandor K K. Review of progress in shape memory epoxies and their composites［J］. Polymers, 2018, 10(1): 2-38.
［3］ 王恩亮, 董余兵. 形状记忆聚合物复合材料研究进展［J］. 浙江理工大学学报, 2018, 39(1): 31-36.
［4］ Cheng Y, Ben B Z, Xiao Y Y. Study on preparation and properties for epoxy shape memory polymer［J］.Advanced Materials Research, 2013, 18(6): 463-466.
［5］ Wang Y K, Tian W C, Liu X H, et al. Thermal sensitive shape memory behavior of epoxy composites reinforced with silicon carbide whiskers［J］. Applied Sciences, 2017, 7(1): 4-10.
［6］ 郭何云, 王煦. 水性环氧树脂制备方法的研究进展［J］. 合成化学, 2017, 25(5): 457-460.
［7］ 赵建国, 杨利娴, 陈晓珊, 等. 美国涂料行业VOC污染控制政策与技术研究［J］. 涂料工业, 2012, 42(2): 44-52.
［8］ Dong Y, Ni Q Q, Fu Y. Preparation and characterization of waterborne epoxy shape memory composites containing silica［J］.Composites Part A: Applied Science and Manufacturing, 2014, 72(12): 1-10.
［9］ Dong Y, Ding J, Wang J, et al. Synthesis and properties of the vapourgrown carbon nanofiber/epoxy shapememory and conductive foams prepared via latex technology［J］. Composites Science and Technology, 2013, 76(34): 8-13.
［10］Dong Y, Ni Q Q, Li L, et al. Novel vaporgrown carbon nanofiber/epoxy shape memory nanocomposites prepared via latex technology［J］. Materials Letters, 2014, 132(25): 206-209.

相似文献/References:

[1]蔡菲,杲爽,孙锦涛,等.沉淀法改性聚磷酸铵及其在水性环氧树脂中的阻燃性能[J].浙江理工大学学报,2022,47-48(自科一):1.
　CAI Fei,GAO Shuang,SUN Jintao,et al.Precipitationmodified ammonium polyphosphate and its flame retardant properties in waterborne epoxy resin[J].Journal of Zhejiang Sci-Tech University,2022,47-48(自科六):1.

备注/Memo

备注/Memo:
收稿日期：2018-10-29
网络出版日期： 2019-03-30
基金项目：国家自然科学基金项目（51703204，51473147）
作者简介：朱善文（1995-），男，安徽六安人，硕士研究生，主要从事形状记忆聚合物复合材料方面的研究
通信作者：董余兵，E-mail:dyb19831120@zstu.edu.cn
更新日期/Last Update: 2019-11-25