海藻酸钙/聚 (N 异丙基丙烯酰胺) 互穿网络水凝胶的药物释放及抗菌性能()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第39-40卷
期数:
2018年自科6期
页码:
715-722
栏目:
出版日期:
2018-11-10

文章信息/Info

Title:
Drug release and antibacterial property of drug loaded alginate Ca 2+ /poly(Nisopropylacrylamide) interpenetrating network hydrogels
文章编号:
1673-3851 (2018) 11-0715-08
作者:
李冰; 徐艺洲; 魏巍; 王际平
浙江理工大学，a.生态染整技术教育部工程研究中心；b.先进纺织材料与制备技术教育部重点实验室，杭州 310018
Author(s):
LI Bing;  XU Yizhou;  WEI Wei;  WANG Jiping
a.Engineering Research Center for EcoDyeing & Finishing of Textiles, Ministry of Education;b.Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education, Zhejiang SciTech University, Hangzhou 310018, China
关键词:
温敏水凝胶; 海藻酸钠; 聚(N 异丙基丙烯酰胺); 药物释放; 抗菌性能
分类号:
O648.1
文献标志码:
A
摘要:
以海藻酸钠（Sodium alginate, SA）和N异丙基丙烯酰胺（Nisopropylacrylamide, NIPAAm）为原料，采用氧化还原自由基聚合和物理交联的方法合成海藻酸钙/聚(N异丙基丙烯酰胺)互穿网络结构水凝胶（AlginateCa 2+/PNIPAAm IPN hydrogel）。利用红外光谱仪（FTIR）、差示扫描量热仪（DSC）以及扫描电子显微镜（SEM）对制备的水凝胶材料进行理化性质表征；以SA/NIPAAm比例、药物浓度、载药方式和介质温度为实验变量，研究水凝胶的盐酸四环素释放行为，并以抑菌圈表征其抗菌性能。结果表明：N异丙基丙烯酰胺比例越高，药物累积释放率越低；药物浓度越高，药物累积释放率也略有下降；采用直接包埋的方法可有效的延长药物缓释的时间，具有良好的药物释放性能；在37 ℃的介质温度下，药物的累积释放率远大于25 ℃，并且具有良好的抗菌效果。制备所得水凝胶在创伤敷料应用方面将具有良好的前景。

参考文献/References:

［1］ Kabiri K, Omidian H, ZohuriaanMehr M J, et al. Superabsorbent hydrogel composites and nanocomposites: A review［J］. Polymer Composites,2011,32(2):277-289.
［2］ Murakami K, Aoki H, Nakamura S, et al. Hydrogel blends of chitin/chitosan, fucoidan and alginate as healingimpaired wound dressings［J］. Biomaterials,2010,31(1):83-90.
［3］ Burdick J A, Prestwich G D. Hyaluronic acid hydrogels for biomedical applications［J］. Advanced Materials,2011,23(12):H41-H56.
［4］ 柯林楠,冯晓明,王春仁.医用敷料研究的现状与进展［J］.中国组织工程研究,2010,14(3):521-524.
［5］ Sun J, Tan H. Alginatebased biomaterials for regenerative  medicine applications［J］. Materials,2013,6(4):1285-1309.
［6］ 刘晓华,王晓工,刘德山.快速响应的温敏性聚(N异丙基丙烯酰胺)水凝胶I.以CaCO3为成孔剂制备方法、表征及动力学研究［J］.高分子学报,2002,1(3):354-357.
［7］ Zhang X Z, Wu D Q, Chu C C. Synthesis, characterization 〖JP〗and controlled drug release of thermosensitive IPNPNIPAAm hydrogels［J］. Biomaterials,2004,25(17):3793-3805.
［8］ 丁曼,王华林,姜绍通.载盐酸四环素壳聚糖缓释膜的制备［J］.中国组织工程研究,2012,16(38):7121-7125.
［9］ 周雯婷,郭吟竹,李兴茂,等.键合型抗菌水凝胶敷料的制备及性能［J］.化工新型材料,2016,44(6):226-229.
［10］ 程祥胜.双重响应性微凝胶及其复合物的合成与性能研究［D］.青岛:青岛大学,2010.

相似文献/References:

[1]张星云,周灵青,鄂玉萍,等.海带发泡缓冲材料的制备及性能研究[J].浙江理工大学学报,2015,33-34(自科6):781.
　ZHANG Xing yun,ZHOU Ling qing,E Yu ping,et al.Preparation of Laminaria Japonica Foamed Cushioning  Material and the Research on Its Properties[J].Journal of Zhejiang Sci-Tech University,2015,33-34(自科6):781.
[2]赵许亮,赵奇才,陈维国.应用有机/无机复合糊料的涤纶分散染料印花热固色研究[J].浙江理工大学学报,2016,35-36(自科4):504.
　ZHAO Xuliang,ZHAO Qicai,CHEN Weiguo.Study on Thermal Fixation of Polyester with Disperse Dye by Applying Organic/Inorganic Composite Paste[J].Journal of Zhejiang Sci-Tech University,2016,35-36(自科6):504.
[3]张立,刘涛,张丽香,等.PEO/SA生物活性玻璃支架的制备和生物活性研究[J].浙江理工大学学报,2018,39-40(自科3):299.
　ZHANG Li,LIU Tao,ZHANG Lixiang,et al.Preparation and bioactivity of bioactive glass scaffold based on PEO/SA[J].Journal of Zhejiang Sci-Tech University,2018,39-40(自科6):299.
[4]刘玉,徐国平,祝佳琼.PLA/PVA/SA复合纱线的制备与表征[J].浙江理工大学学报,2019,41-42(自科六):723.
　LIU Yu,XU Guoping,ZHU Jiaqiong.Preparation and characterization of PLA/PVA/SA composite yarns[J].Journal of Zhejiang Sci-Tech University,2019,41-42(自科6):723.
[5]任旭,刘涛,朱莹,等.丝素/海藻酸钠载药复合支架的药物缓释行为及其活性[J].浙江理工大学学报,2020,43-44(自科二):209.
　REN Xu,LIU Tao,ZHU Ying,et al.Drug sustained release properties and bioactivity of silk fibroin/sodium alginate drugloaded composite scaffold[J].Journal of Zhejiang Sci-Tech University,2020,43-44(自科6):209.

备注/Memo

备注/Memo:
收稿日期： 2018-03-05
网络出版日期： 2018-05-07
作者简介： 李冰（1989-），男，浙江诸暨人，博士研究生，主要从事温敏响应性水凝胶方面的研究
通信作者： 王际平，E-mail：jpwang@zstu.edu.cn
更新日期/Last Update: 2018-11-09