基于无机盐诱导的可控聚集制备纳米多孔结构减反射涂膜()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第39-40卷
期数:
2018年自科5期
页码:
566-572
栏目:
出版日期:
2018-08-31

文章信息/Info

Title:
Nanoporous antireflection coating prepared by controlled aggregation based on inorganic salt induction
文章编号:
1673-3851 (2018) 09-0566-07
作者:
李文波; 赵强强; 沈一峰; 杨雷
浙江理工大学，a.材料与纺织学院；b.先进纺织材料与制备技术教育部重点实验室，杭州 310018
Author(s):
LI Wenbo; ZHAO Qiangqiang; SHEN Yifeng; YANG Lei
a.College of Materials and Textiles; b.Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
可控聚集; 纳米多孔; 乳胶膜; 减反射; Zeta电位
分类号:
O632.12
文献标志码:
A
摘要:
纳米多孔膜是一种重要的减反射膜，目前制备方法存在步骤繁琐、条件苛刻以及效率低等不足，如何简便、高效地制备减反射性能优良的纳米多孔涂膜具有很大的挑战性。文章提出以无机盐可控地诱导成膜过程中乳胶粒聚集，一步制备纳米多孔结构减反射涂膜的设想。在以胶乳制备多孔结构减反射时，分别考察了氯化铵（NH 4Cl，酸式盐）、氯化钠（NaCl，中性盐）和碳酸氢铵（NH 4HCO 3，碱式盐）为致孔剂时，涂膜的结构及减反射性能。研究表明：为达到实验的目的，与NH 4Cl和NaCl相比，NH 4HCO 3更适宜作为纳米多孔膜的致孔剂；胶乳中加入NH 4HCO 3后，乳液分散稳定性提高；被涂覆于基材表面后，乳液中NH 4HCO 3的浓度随着水分的蒸发不断增高，引起乳胶粒子聚集、堆积形成多孔结构；之后，在100 ℃干燥涂膜时，NH 4HCO 3又可通过热分解而被去除；以NH 4HCO 3为致孔剂时，涂膜具有纳米多孔结构，对入射光散射小，单面涂膜玻璃增透率提高3.6%，增透效率明显高于采用NaCl或NH 4Cl所制的涂膜。

参考文献/References:

［1］ Guo Z, Zhao H, Zhao W, et al. Highquality hollow closedpore silica antireflection coatings based on styreneacrylate emulsion@ organicinorganic silica precursor［J］. ACS Applied Materials & Interfaces,2016,8(18):11796-11805.
［2］ Buskens P, Burghoorn M, Mourad M C D, et al. Antireflective coatings for glass and transparent polymers［J］. Langmuir,2016,32(27):6781-6793.
［3］ Ren T, He J. Substrateversatile approach to robust  antireflective and superhydrophobic coatings with excellent selfcleaning property in varied environments［J］. ACS Applied Materials & Interfaces，2017,9(39):34367-34376.
［4］ Ji L, Hsu H Y, Li X, et al. Localized dielectric breakdown and antireflection coating in metaloxidesemiconductor photoelectrodes［J］. Nature Materials,2017,16(1):127-131.
［5］ Poitras D, Dobrowolski J A. Toward perfect antireflection coatings. 2. theory［J］. Applied Optics,2004,43(6):1286-1295.
［6］ Mizoshita N, Ishii M, Kato N, et al. Hierarchical nanoporous silica films for wear resistant antireflection coatings［J］. ACS Applied Materials & Interfaces,2015,7(34):19424-19430.
［7］ Kaminski P M, Lisco F, Walls J M. Multilayer broadband antireflective coatings for more efficient thin film CdTe solar cells［J］. IEEE Journal of Photovoltaics,2014,4(1):452-456.
［8］ Ji S, Song K, Nguyen T B, et al. Optimal moth eye nanostructure array on transparent glass towards broadband antireflection［J］. ACS Applied Materials & Interfaces,2013,5(21):10731-10737.
［9］ Macleod H A. Thinfilm Optical Filter［M］.4th ed. Boca Raton: CRC Press,2010:73-104.
［10］ Mattox D M. Handbook Of Physical Vapor Deposition (PVD) Processing［M］. 2nd ed. Norwich NY:William Andrew,2010:545-552.

备注/Memo

备注/Memo:
收稿日期： 2018-1-19
网络出版日期： 2018-04-04
基金项目： 国家自然科学基金项目(21606206)；浙江省自然科学基金项目(LY18E030008，LY15E030013，LY12E03008)；浙江省公益技术应用研究项目(2016C31074，2017C31033)
作者简介： 李文波(1991-)，男，湖北仙桃人，硕士研究生，主要从事新型染整化学品及绿色合成技术方面的研究
通信作者： 杨雷，E-mail：yanglei@zstu.edu.cn
更新日期/Last Update: 2018-09-12