|本期目录/Table of Contents|

[1]魏秋云,沈崇斌,孔哲,等.含不饱和金属位点的金属有机骨架材料对烟道气中SO-2的吸附与分离行为的分子模拟研究[J].浙江理工大学学报,2018,39-40(自科2):232-241.
　WEI Qiuyun,SHEN Chongbin,KONG Zhe,et al.Molecular simulation study on adsorption and separation of SO-2 in flue gas by metal organic frameworks with unsaturated metal sites[J].Journal of Zhejiang Sci-Tech University,2018,39-40(自科2):232-241.
点击复制

含不饱和金属位点的金属有机骨架材料对烟道气中SO-2的吸附与分离行为的分子模拟研究()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第39-40卷
期数:
2018年自科2期
页码:
232-241
栏目:
出版日期:
2018-03-31

文章信息/Info

Title:
Molecular simulation study on adsorption and separation of SO-2 in flue gas by metal organic frameworks with unsaturated metal sites
文章编号:
1673-3851 (2018) 03-0232-10
作者:
魏秋云; 沈崇斌; 孔哲; 张丽
1.浙江理工大学理学院，杭州 310018；2.北京师范大学附属杭州中学，杭州 310002；3.杭州电子科技大学材料与环境工程学院，杭州 310018
Author(s):
WEI Qiuyun;  SHEN Chongbin;  KONG Zhe;  ZHANG Li
1.School of Sciences, Zhejiang Sci-Tech University, Hangzhou 310018, China;2.Hangzhou Middle School Affiliated to Beijing Normal University, Hangzhou 310002, China; 3.College of Materials & Environmental Engineering, Hangzhou Dianzi University, Hangzhou 310018, China
关键词:
金属有机骨架材料; 烟道气; 吸附/分离; 分子模拟
分类号:
O647.32
文献标志码:
A
摘要:
MOFs（Metal organic frameworks）材料因具有较高的比表面积和孔隙率、可调的孔道以及良好的热稳定性和化学稳定性等优势，被认为是用于硫化物吸附与分离最有前途的新型多孔材料。采用分子模拟方法研究了含不饱和金属位点的MOFs材料对烟道气中SO2的吸附与分离行为，揭示影响吸附/分离性能的因素，研究结果表明：低压下，SO2在MOFs材料中的吸附性能取决于SO2与MOFs材料之间的相互作用，MOFs材料与SO2之间的相互作用越强，吸附性能越好；高压下，SO2在MOFs材料中的吸附性能由材料的比表面积、孔体积决定。金属离子与有机配体构成的角度越大，烟道气中SO2与MDOBDCs材料（金属离子MⅡ（Co、Ni、Mg等）和2,5二羟基1,4对苯二甲酸（2,5dioxido1,4benzenedicarboxylate，DOBDC）配体配位形成的微孔材料）中的不饱和金属位点之间接触概率越大，MDOBDCs材料与烟道气中SO2之间的相互作用越强，其对烟道气中SO2的分离性能越佳。烟道气中N2在不同金属离子的MDOBDCs材料中吸附量相当，不同金属离子对烟道气分离性能差异主要由CO2与SO2在不同MDOBDCs中竞争效应不同所致。ZnDOBDC是可用于烟道气中VSA过程SO2分离的备选材料。

参考文献/References:

［1］ 薛菲,石劲松.烟气脱硫技术现状与发展建议［J］.江苏化工,2001,29(2):32-35.
［2］ Davini P. SO2 and NOx adsorption properties of activated carbons obtained from a pitch containing iron derivatives［J］. Carbon,2001,39(14):2173-2179.
［3］ Deng H, Yi H, Tang X, et al. Adsorption equilibrium for sulfur dioxide, nitric oxide, carbon dioxide, nitrogen on 13X and 5A zeolites［J］. Chemical Engineering Journal,2012,188:77-85.
［4］ Ridha F N, Manovic V, Macchi A, et al. The effect of SO2 on CO2 capture by CaObased pellets prepared with a kaolin derived Al(OH)3 binder［J］. Applied Energy,2012,92:415-420.
［5］ Lu H, Smirniotis P G. Calcium oxide doped sorbents for CO2 uptake in the presence of SO2 at high temperatures［J］. Industrial & Engineering Chemistry Research,2009,48(11):5454-5459.
［6］ Sun P, Grace J R, Lim C J, et al. Removal of CO2 by calciumbased sorbents in the presence of SO2［J］. Energy & Fuels,2007,21(1):163-170.
［7］ Peterson G W, Karwacki C J, Feaver W B, et al. Zirconium hydroxide as a reactive substrate for the removal of sulfur dioxide［J］. Industrial & Engineering Chemistry Research,2009,48(4):1694-1698.
［8］ Seredych M, Bandosz T J. Effects of surface features on adsorption of SO2 on graphite oxide/Zr(OH)4 composites［J］. The Journal of Physical Chemistry C,2010,114(34):14552-14560.
［9］ Seredych M, Mabayoje O, Bandosz T J. Involvement of water and visible light in the enhancement in SO2 adsorption at ambient conditions on the surface of zinc(hydr) oxide/graphite oxide composites［J］. Chemical Engineering Journal,2013,223:442-453.

备注/Memo

备注/Memo:
收稿日期： 2017-03-15
网络出版日期： 2017-06-21
作者简介： 魏秋云(1989-)，女，河南周口人，硕士研究生，主要从事分子模拟方面的研究
通信作者： 张丽，E-mail：yazi5@163.com
更新日期/Last Update: 2018-03-16