|本期目录/Table of Contents|

[1]张阳,高尚,王耐艳.硼掺杂对Ca-2Si-5N-8:Eu-2+荧光粉发光性能的影响[J].浙江理工大学学报,2018,39-40(自科1):57-61.
　ZHANG Yang,GAO Shang,WANG Naiyan.Effect of boron doping on luminescent properties of Ca-2Si-5N-8: Eu2+ phosphors[J].Journal of Zhejiang Sci-Tech University,2018,39-40(自科1):57-61.
点击复制

硼掺杂对Ca-2Si-5N-8:Eu-2+荧光粉发光性能的影响()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第39-40卷
期数:
2018年自科1期
页码:
57-61
栏目:
出版日期:
2017-12-31

文章信息/Info

Title:
Effect of boron doping on luminescent properties of Ca-2Si-5N-8: Eu2+ phosphors
文章编号:
1673-3851 (2018) 01-0057-05
作者:
张阳; 高尚; 王耐艳
浙江理工大学材料工程中心，杭州 310018
Author(s):
ZHANG Yang;  GAO Shang;  WANG Naiyan
Materials Engineering Center, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
Ca-2Si-5N-8:Eu-2+; BN; 掺杂; 发光性能
分类号:
TB34
文献标志码:
A
摘要:
采用氨热法，以金属Ca、Eu、非晶Si以及硼烷氨为原料，液氨为介质均与混合，经1230 ℃保温5 h合成h-BN包覆的Ca-2Si-5N-8:Eu-2+红色荧光粉。X射线衍射（XRD）测试结果表明：是否掺杂硼并没有改变Ca-2Si-5N-8晶体结构，但掺杂硼的产物除存在Ca-2Si-5N-8主相外，还包含BN相；透射电子显微镜（TEM）分析结果得到：BN相呈透明状包覆在Ca-2Si-5N-8外表面，并与Ca-2Si-5N-8相呈共格相界；荧光光谱（PL）测试结果表明：硼掺杂Ca-2Si-5N-8:Eu-2+荧光粉的发光强度提高了约1.1倍，发射光谱红移20 nm，其激发峰在465 nm，发射峰位于590 nm，硼掺杂有助于提高Ca-2Si-5N-8:Eu 2+荧光粉的发光性能。

参考文献/References:

［1］ 洪广言,庄卫东.稀土发光材料［M］.北京:冶金工业出版社,2016：39-43.
［2］ 周伟杰,高林辉,王广发.Gd2Zr2O7:Eu 3+红色荧光粉的制备及发光性能的研究［J］.浙江理工大学学报,2017,37(2):197-201.
［3］ Wang Q, Dong Y, Shao Q, et al. The effect of Li3N flux on properties of Sr2Si5N8: Eu2+, phosphor［J］. Materials & Design,2016,95(35):618-622.
［4］ Lin H C, Yang C Y, Das S, et al. Redemission improvement of Eu2+-Mn2+ codoped Sr2Si5N8 phosphors for white lightemitting diodes［J］. Ceramics International,2014,40(8):12139-12147.
［5］ Wei X D, Cai L Y, Lu F C, et al. Structure and luminescence of Ca2Si5N8:Eu2+ phosphor for warm white lightemitting diodes［J］. Chinese Physics B,2009,18(8):3555-3562.
［6］ Lin J, Huang Y, Mi J, et al. BNcoated Ca1-xSixS:Eu solidsolution nanowires with tunable red light emission［J］. Nanotechnology,2013,24(40):405701-405705.
［7］ Yeh C W, Chen W T, Liu R S, et al. Origin of thermal degradation of Sr2-xSi5N8:Eux phosphors in air for lightemitting diodes［J］. Journal of the American Chemical Society,2012,134(34):14108-14117.
［8］ Schlieper T, Schnick W. ChemInform abstract: Nitrido  Silicates. Part 1. High temperature synthesis and crystal  structure of Ca2Si5N8［J］. Cheminform,1995,26(41):1037-1041.
［9］ Li J, Lei B, Qin J, et al. Temperaturedependent emission  spectra of Ca2Si5N8: Eu2+, Tm3+ phosphor and its afterglow  properties［J］. Journal of the American Ceramic Society,2013,96(3):873-878.

［10］ 张梦菲，刘凡,张阳,等.液相混合辅助低温制备Ca2Si5N8: Eu2+荧光粉［J］.浙江理工大学学报,2016,35(7):554-558.

备注/Memo

备注/Memo:
收稿日期： 2017-06-23
网络出版日期： 2017-11-09
作者简介： 张阳(1991-)，男，安徽萧县人，硕士研究生，主要从事稀土发光材料方面的研究
通信作者： 王耐艳，E-mail:wangnaiyan@zstu.edu.cn
更新日期/Last Update: 2018-03-12