[1]陈一明,周岚,冯新星,等.聚酰胺6型弹性体的热稳定性研究[J].浙江理工大学学报,2017,37-38(自科5):642-646.
 CHEN Yiming,ZHOU Lan,FENG Xinxing,et al.Study on Thermal Stability of Polyamide 6 Elastomer[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科5):642-646.
点击复制

聚酰胺6型弹性体的热稳定性研究()
分享到:

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第37-38卷
期数:
2017年自科5期
页码:
642-646
栏目:
出版日期:
2017-08-30

文章信息/Info

Title:
Study on Thermal Stability of Polyamide 6 Elastomer
文章编号:
1673-3851 (2017) 05-0642-05
作者:
陈一明周岚冯新星陈建勇
1. 浙江理工大学,a. 纤维材料和加工技术研究重点实验室;b. 生态染整技术教育部工程研究中心,杭州310018;2.中国人民解放军总后勤部军需装备研究所,北京 100082
Author(s):
CHEN Yiming ZHOU Lan FENG Xinxing CHEN Jianyong
1a. Zhejiang Provincial Key Laboratory of Fiber Materials and Manufacturing Technology;1b. Engineering Research Center for EcoDyeing and Finishing of Textiles, Ministry of Education,Zhejiang Sci-Tech University, Hangzhou 310018, China; 2.The Quartermaster Research Institute of the General Logistics Department of the PLA, Beijing 100082, China
关键词:
聚酰胺嵌段共聚物软硬段配比热稳定性
分类号:
TQ342
文献标志码:
A
摘要:
以己内酰胺为硬单体进行水解开环聚合合成封端预聚体聚己内酰胺(PA6),再加入聚乙二醇(PEG)软段合成聚酰胺嵌段共聚物(PA6-b-PEG)。通过FTIR、XRD、TG和DSC分析其结构并表征其热性能,研究嵌段聚合物的热稳定性与软段含量及分子量的关系。结果表明:在不同的软段和硬段配比中,随着软段的加入,PA6-b-PEG嵌段共聚物的热稳定性升高,当配比为20∶80时,其热稳定性达到最佳;使用不同分子量的PEG合成的PA6-b-PEG的热失重相差无几,且合成的共聚物的弹性表现出较宽的使用温度范围。

参考文献/References:

[1] 汪卫斌,张正华,徐伟箭.聚酰胺类热塑性弹性体的合成与发展现状[J].化工新型材料,2003,31(11):23-25
[2] 代芳,吕召胜,王金立.2014年我国热塑性工程塑料研究进展[J].工程塑料应用,2015,43(3):123-132
[3] GILL R, MAZHAR M, SIDDIQ M. Structural characterization and thermal behaviour of block copolymers of polydimethylsiloxane and polyamide having trichlorogermyl pendant groups[J]. Polymer International,2010,59(12):1598-1605.
[4] 邱贤亮,游德军,岑兰,等.聚酰胺类热塑性弹性体的研究进展[J].橡胶工业,2012,59(3):187-191
[5] 李凤娇,周阳,黄启谷,等.聚酰胺的制备方法与改性[J].塑料,2014,43(4):72-74
[6] 何建辉,宋新,冯美平,等.世界聚酰胺纤维产业链现状及发展趋势[J].合成纤维工业,2013,36(3):38-43
[7] 文彦飞.尼龙6系热塑性弹性体[J].化工新型材料,2000(5):11-13.
[8] 张英伟,王文志,杨克俭,等.多嵌段共聚聚酰胺弹性体的制备及性能研究[J].塑料工业,2013,41(2):16-19.

相似文献/References:

[1]王爱瑞,邵英,易玲敏,等.PMTFPS-b-PMMA/PMMA共混聚合物膜的表面性质[J].浙江理工大学学报,2017,37-38(自科6):804.
 WANG Airui,SHAO Ying,YI Lingmin,et al.Surface Properties of PMTFPS-b-PMMA/PMMA Polymer Blend Films[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科5):804.
[2]糜磊,钟齐,王际平.无规和嵌段聚丙烯酸酯类温敏共聚物的转变行为研究[J].浙江理工大学学报,2018,39-40(自科3):278.
 MI Lei,ZHONG Qi,WANG Jiping.Study on transformation behavior of random and block polyacrylate thermosensitive copolymers[J].Journal of Zhejiang Sci-Tech University,2018,39-40(自科5):278.
[3]李姝雨,何书恒,曹志海,等.二次界面聚合法制备聚酰胺-银-纳米粒子复合纳滤膜[J].浙江理工大学学报,2023,49-50(自科四):500.
 LI Shuyu,HE Shuheng,CAO Zhihai,et al.Preparation of polyamide-Ag nanoparticle composite nanofiltration membranes via secondary interfacial polymerization[J].Journal of Zhejiang Sci-Tech University,2023,49-50(自科5):500.

备注/Memo

备注/Memo:
收稿日期: 2016-11-13
网络出版日期: 2017-01-19
基金项目: 中国人民解放军总后军需一般项目(2011BAE05B)
作者简介: 陈一明(1989-),男,江西南昌人,硕士研究生,主要从事聚酰胺弹性体热性能方面的研究
通信作者: 冯新星,E-mail:xinxingfeng@hotmail.com
更新日期/Last Update: 2017-09-26