|本期目录/Table of Contents|

[1]李华彬,唐红艳,郭玉海.PA/PTFE复合纳滤膜的制备及表征[J].浙江理工大学学报,2017,37-38(自科1):14-17.
　LI Huabin,TANG Hongyan,GUO Yuhai.Synthesis and Characterization of PA/PTFE CompositeNanofiltration Membrane[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科1):14-17.
点击复制

PA/PTFE复合纳滤膜的制备及表征()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第37-38卷
期数:
2017年自科1期
页码:
14-17
栏目:
出版日期:
2017-01-10

文章信息/Info

Title:
Synthesis and Characterization of PA/PTFE CompositeNanofiltration Membrane
文章编号:
1673-3851 (2017) 01-0014-04
作者:
李华彬; 唐红艳; 郭玉海
浙江理工大学，a.材料与纺织学院；b.“纺织纤维材料与加工技术”国家地方联合工程实验室；c.浙江省重点实验室“纤维材料和加工技术研究实验室”，杭州 310018
Author(s):
LI Huabin ;  TANG Hongyan ;  GUO Yuhai
a.College of Materials and Textiles; b.National Local Joint Engineering Laboratory of Textile Fiber Material and Processing Technology; c.The Key Research Laboratory of Fiber Materials and Processing Technology of Zhejiang Province, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
间苯二胺; 均苯三甲酰氯; 聚四氟乙烯微孔膜; 界面聚合; 纳滤
分类号:
TQ028.8
文献标志码:
A
摘要:
以聚四氟乙烯（PTFE）微孔膜为基膜，间苯二胺（MPD）为水相单体，均苯三甲酰氯（TMC）为油相单体，采用界面聚合的方法制备了聚酰胺（PA）/ PTFE复合纳滤膜。用红外光谱（FTIR）和扫描电子显微镜（SEM）对复合纳滤膜化学结构和微观形貌进行分析，探讨单体浓度、聚合时间、热处理条件对膜结构性能的影响。结果表明，在操作压力0.5 MPa下，所制备的复合纳滤膜对1 g/L Na2SO4溶液的脱除率为95 %以上。

参考文献/References:

［1］ CADOTTE J E. Novel water softening membranes［P］. US Pat：4812270,1989-03-14.
［2］ SCHAEP J, VAN DER BRUGGEN B, VANDECASTEELE C, et al. Influence of ion size and charge in nanofiltration［J］. Separation and Purification Technology,1998,14(1)：155-162.
［3］ 俞三传,高从堦,张建飞.复合纳滤膜及其应用［J］.水处理技术,1997,23(3)：139.
［4］ WANG T, YANG Y, ZHENG J, et al. A novel highly permeable positively charged nanofiltration membrane based on a nanoporous hypercrosslinked polyamide barrier layer ［J］. Journal of Membrane Science,2013,448：180-189.
［5］ AN Q F, SUN W D, ZHAO Q, et al. Study on a novel nanofiltration membrane prepared by interfacial polymerization with zwitterionic amine monomers ［J］. Journal of Membrane Science,2013,431：171-179.
［6］ LIU M, YAO G, CHENG Q, et al. Acid stable thinfilm composite membrane for nanofiltration prepared from naphthalene1, 3, 6trisulfonylchloride (NTSC) and piperazine (PIP) ［J］. Journal of Membrane Science,2012,415：122-131.
［7］ XIE W, GEISE G M, FREEMAN B D, et al. Polyamide interfacial composite membranes prepared from mphenylene diamine, trimesoyl chloride and a new disulfonated diamine［J］. Journal of Membrane Science,2012,403：152-161.
［8］ MEIHONG L, SANCHUAN Y, YONG Z, et al. Study on the thinfilm composite nanofiltration membrane for the removal of sulfate from concentrated salt aqueous：Preparation and performance［J］. Journal of Membrane Science,2008,310(1)：289-295.
［9］ SAHA N K, JOSHI S V. Performance evaluation of thin film composite polyamide nanofiltration membrane with variation in monomer type［J］. Journal of Membrane Science, 2009, 342(1)：60-69.

备注/Memo

备注/Memo:
收稿日期： 2015-11-02
网络出版日期： 2016-12-09
基金项目： 国家科技支撑计划项目（2013BAC01B01）；浙江省自然科学基金项目（LY15B060010）；浙江理工大学521 人才培养计划，浙江省高校重中之重学科优秀基金、开放基金项目（2014KF05，2014YXQN03）
作者简介： 李华彬(1990-)，男，广西博白人，硕士研究生，主要从事聚四氟乙烯膜改性方面的研究
通信作者： 郭玉海，E-mail:gyh@zstu.edu.cn
更新日期/Last Update: 2017-02-28