Title:
Preparation of Au Nanoparticles by Magnetron Sputtering and Study on Its Localized Surface Plasmon Resonance
文章编号:
1673-3851 (2015) 06-0882-05
作者:
董大银; 潘傲秋; 李培刚; 沈静琴; 王顺利; 李超荣
浙江理工大学光电材料与器件中心，杭州310018
Author(s):
DONG Dayin;  PAN Aoqiu;  LI Peigang;  SHEN Jingqin;  WANG Shunli;  LI Chaorong
Center for Optoelectronics Materials and Devices, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
Au薄膜; 局域表面等离激元共振; 热退火; 表面形貌
分类号:
O531,O433.4
文献标志码:
A
摘要:
通过磁控溅射的方法在石英衬底上沉积了Au薄膜，经过热退火处理形成了不同表面形貌和尺寸的Au纳米颗粒。通过XRD、AFM和紫外可见光谱研究了薄膜的质量、表面形貌、尺寸和光谱特性,分析了不同表面形貌和尺寸的Au纳米颗粒对局域表面等离激元共振的影响。研究表明：随着退火温度的升高，Au薄膜由各向异性的蠕虫状结构逐渐变成规则的纳米颗粒，退火温度越高，Au纳米颗粒越接近于圆形，颗粒间距越大，导致局域表面等离激元共振峰位发生蓝移，半峰宽变窄；另外溅射时间对Au纳米颗粒的影响也很大，随着溅射时间的增加，颗粒尺寸变大，变得不再均匀，局域表面等离激元共振峰发生红移、宽化和向长波段上扬。

参考文献/References:

［1］ Raether H. Surface Plasmons on Smooth and Rough Surfaces and on Gratings［M］. Berlin: Springer, 1988:1-3.
［2］ Barnes W L, Dereux A, Ebbesen T W. Surface plasmon subwavelength optics ［J］. Nature, 2003, 424: 824-830.
［3］ Wei H, Ratchford D, Li X Q, et al. Propagating surface plasmon induced photon emission from quantum dots［J］. Nano Lett, 2009, 9(12): 4168-4171.
［4］ Tong L M, Wei H, Zhang S P, et al. Optical properties of single coupled plasmonic nanoparticles［J］. Phys Chem Chem Phys, 2013, 15(12): 4100-4109.
［5］ Hutter E, Fendler J H. Exploitation of localized surface plasmon resonance［J］. Adv Mater, 2004, 16(19): 1685-1706.
［6］ Ito Y, Matsuda K, Kanemitsu Y. Mechanism of photoluminescence enhancement in single semiconductor nanocrystals on metal surfaces［J］. Phys Rev B, 2007, 75(3): 033309.
［7］ Xiao S, Gong H M, Su X R,  et al . Two  and threephoton luminescence of au nanoparticles and resonant energy transfer from cdse quantum dots［J］.Phys Chem C, 2007, 111(28): 10185-10189.
［8］ Atwater H A, Polman A. Plasmonic for improved photovoltaic devices［J］. Nature Materials, 2010, 9(3): 205-213.
［9］ 刘燕楠, 邹祖全, 刘燕青, 等. 肺正常组织与癌变组织的表面增强拉曼光谱［J］. 光谱学与光谱分析. 2007, 27(10): 2045-2048.
［10］ Kang A, Yoo S M, Yoon I, et al. Patterned multiplex pathogen dna detection by au particleonwire sers sensor［J］. Nano Lett, 2010, 10(4): 1189-1193.
［11］ Pillai S, Catchpole K R, Trupke T, et al. Enhanced emission from thin Si based LEDs using surface plasmons［J］. Appl Phys Lett, 2006, 88(16): 161102.
［12］ Brown M D, Suteewong T, Kumar R S S S, et al. Plasmonic dyesensitized solar cells using coreshell metalinsulator nanoparticles［J］. Nano Lett, 2011, 11(2): 438-445.
［13］ Sun H T, Yu M P, Wang G K, et al. Temperaturedependent morphology evolution and surface plasmon absorption of ultrathin gold island films［J］. J Phys Chem C, 2012, 116(16): 9000-9008.
［14］ 于威, 刘玉梅, 戴万雷, 等. 热退火诱导纳米银膜形貌变化对表面等离激元共振特性的影响［J］. 光谱学与光谱分析, 2013, 33(4): 906-910.
［15］ Yeh D M, Huang C F, Chen C Y, et al. Localized surface plasmoninduced emission enhancement of a green lightemitting diode［J］. Nanotechnology, 2008, 19(34): 345201.

备注/Memo

备注/Memo:
收稿日期：2014-11-26
基金项目：国家自然科学基金项目（61274017）；浙江省大学生科技创新活动计划（2014R406083）；浙江理工大学521人才计划；浙江省钱江人才计划（QJD1202004）；浙江省科技厅公益性技术应用研究计划项目（2014C37073）
作者简介：董大银（1989-），男，安徽宣城人，硕士研究生，主要从事纳米材料与器件方面的研究
通信作者：李超荣，E-mail：crli@zstu.edu.cn
更新日期/Last Update: 2015-11-19