|本期目录/Table of Contents|

[1]张春山,丁新波,韩建,等.PVC建筑膜材用纳米SiO2粒径的可控性及其羰基化研究[J].浙江理工大学学报,2013,30(03):312-315.
　ZHANG Chun shan,DING Xin bo,HAN Jian,et al.Controllability of Particle Size of Nano SiO2 for PVC Architectural Membrane Material[J].Journal of Zhejiang Sci-Tech University,2013,30(03):312-315.
点击复制

PVC建筑膜材用纳米SiO2粒径的可控性及其羰基化研究()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第30卷
期数:
2013年03期
页码:
312-315
栏目:
(自科)纺织与服装工程
出版日期:
2013-05-10

文章信息/Info

Title:
Controllability of Particle Size of Nano SiO2 for PVC Architectural Membrane Material
文章编号:
1673 3851 (2013) 03 0312 04
作者:
张春山;  丁新波;  韩建;  于斌;  徐国平
浙江理工大学, a. 材料与纺织学院; b. 先进纺织材料与制备技术教育部重点实验室, 杭州 310018
Author(s):
ZHANG Chun shan ;  DING Xin bo ;  HAN Jian ;  YU Bin ;  XU Guo ping 
a. School of Materials and Textiles; b. Key Laboratory of Advanced Textile Materials and Manufacturing  Technology, Ministry of Education, Zhejiang SciTech University, Hangzhou 310018, China
关键词:
溶胶凝胶法;  纳米;  SiO2;  粒径; 羟基含量;  硅烷偶联剂
分类号:
TU532.61
文献标志码:
A
摘要:
为研制PVC建筑膜材用纳米SiO2粉体,采用溶胶凝胶法制备粉体，并用有机无机杂化法进行改性,以降低粉体亲水性。激光粒径仪分析表明,随 n (NH-3·H -2O)∶ n (TEOS)摩尔比的增大,二氧化硅粒径增大;热重分析表明，随 n (NH-3·H-2O)∶ n(TEOS)摩尔比的增大,羟基含量先增加后减少,至1∶1时达到峰值;红外分析表明,硅烷偶联剂KH570与纳米SiO2粉体发生反应,引入了羰基基团,同时羟基数量减少。

参考文献/References:

［1］ 李明亮, 丁新波, 韩建, 等. PVC膜材涂层的热稳定性和表面形貌研究［J］. 浙江理工大学学报, 2011, 28(5): 700-704.
［2］ 曲爱兰, 文秀芳, 皮丕辉, 等. 复合SiO2粒子涂膜表面结构及超疏水性能［J］. 无机化学学报, 2007, 10(23): 1711-1716.
［3］ 王庆军, 陈庆民. 超疏水表面的制备技术及其应用［J］. 高分子材料科学与工程, 2005, 21(2): 6-10.
［4］ 赵存挺, 冯新星, 吴芳, 等. 单分散纳米二氧化硅微球的制备及羧基化改性［J］. 功能材料, 2009, 11(40): 1942-1945.
［5］ 戚栋明, 包永忠, 黄志明, 等. 纳米SiO 2粒子锚固偶氮引发剂及接枝聚甲基丙烯酸甲酯［J］. 高分子学报, 2004, 6(3): 415-418.
［6］ Pilotek S, Schmidt H K. Wettability of microstructured hydrophobic solgel coatings［J］. Journal of Solgel Science and Technology, 2003(26): 789-792.
［7］ 赵丽, 余家国, 程蓓, 等. 单分散二氧化硅球形颗粒的制备与形成机理［J］. 化学学报, 2003, 4(61): 562-566.
［8］ Ochi M, Takahashi R, Terauchi A . Phase structure and mechanical and adhesion properties of epoxy/silica hybrids ［J］. Polymer, 2001(42): 5151-5158.
［9］ Liu Qiuping, Gao Lingxiang, Gao Ziwei, et al. Preparation and characterization of polyimide/Silica nanocomposite spheres［J］. Journal of Shaanxi Normal University, 2007, 3(35): 65-68
［10］ Shrtcllffe N J, Mchale G, Newton M I. Intrinsically superhydrophobic organosilica solgel foams［J］. Langmuir, 2003, 19(14): 5626-5631.
［11］ Abraham Marmur. The lotus effect: superbydrophobicity and metastability［J］. Langmuir, 2004, 20(9): 3517-3519.
［12］ 宋震宇, 霍瑞亭, 周劲勋, 等. 改性SiO2在防污自洁表面处理中的应用［J］. 涂料工业, 2009, 39(3): 6-9

相似文献/References:

[1]吴震弘,汪洋,冯佩,等.TiO 2薄膜的制备及其对304不锈钢防腐性能的研究[J].浙江理工大学学报,2014,31-32(自科2):179.
　WU Zhen hong,WANG Yang,FENG Pei,et al.Preparation of TiO 2 Thin Films and Study of Its Corrosion Resistance Performance for 304 Stainless Steel[J].Journal of Zhejiang Sci-Tech University,2014,31-32(03):179.
[2]蒋乐,魏琪,周彬,等.Gd掺杂和Gd/N共掺杂TiO-2光催化剂的制备及其光催化性能研究[J].浙江理工大学学报,2017,37-38(自科1):152.
　JIANG Le,WEI Qi,Zhou Bin,et al.Preparation of Gddoped and Gd/Ncodoped TiO-2 Photocatalyst and Its Photocatalytic Performance Research[J].Journal of Zhejiang Sci-Tech University,2017,37-38(03):152.
[3]周传凯,于斌,孙辉,等.溶胶凝胶法制备 TiO-2-Ag的介孔微球及其抗菌性能研究[J].浙江理工大学学报,2017,37-38(自科4):485.
　ZHOU Chuankai,YU Bin,SUN Hui,et al.Preparation of TiO-2-Ag Mesoporous Microspheres by GelsolMethod and Analysis of Its Antibacterial Property[J].Journal of Zhejiang Sci-Tech University,2017,37-38(03):485.
[4]李智慧,张立,刘涛,等.中空生物玻璃形貌结构及其活性研究[J].浙江理工大学学报,2017,37-38(自科5):737.
　LI Zhihui,ZHANG Li,LIU Tao,et al.Synthesis and Bioactivity of Hollow Bioactive Glass Nanospheres[J].Journal of Zhejiang Sci-Tech University,2017,37-38(03):737.
[5]鞠凤宇,刘涛,张丽香,等.介孔镂空生物玻璃微球调控及形成机制[J].浙江理工大学学报,2018,39-40(自科2):171.
　JU Fengyu,LIU Tao,ZHANG Lixiang,et al.Control and formation mechanism of mesoporous hollow bioactive glass nanospheres[J].Journal of Zhejiang Sci-Tech University,2018,39-40(03):171.
[6]汪文华,雷彩虹,余媛,等.基于Zn 2+与Mo 6+共掺杂TiO2复合粒子的抗菌PVDF平板膜制备及其性能分析[J].浙江理工大学学报,2022,47-48(自科四):524.
　WANG Wenhua,LEI Caihong,YU Yuan,et al.Preparation of antibacterial PVDF flat membrane based on Zn 2+与Mo 6+ codoped TiO2 composite particles and its property analysis[J].Journal of Zhejiang Sci-Tech University,2022,47-48(03):524.

备注/Memo

备注/Memo:
收稿日期： 2012-11-22
基金项目： 浙江省重点科技创新团队(2011r50003)
作者简介： 张春山(1987-),男,河南郑州人,硕士研究生,主要从事产业用纺织材料的开发和应用研究。
通信作者： 韩建,电子邮箱:hanjian8@zstu.edu.cn
更新日期/Last Update: