[1]叶逢春,郭绍义,汪伦. 恒流阳极氧化0Cr25Al5的组织及抗氧化机理[J].浙江理工大学学报,2011,28(05):767-771.
　YE Feng chun,GUO Shao yi,WANG Lun. The Organization and Antioxidation Mechanism of the 0Cr25Al5 Anodic Oxide Film by Constant Current Anodic Oxidation[J].Journal of Zhejiang Sci-Tech University,2011,28(05):767-771.
点击复制

 恒流阳极氧化0Cr25Al5的组织及抗氧化机理()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第28卷
期数:
2011年05期
页码:
767-771
栏目:
出版日期:
2011-10-30

文章信息/Info

Title:
 The Organization and Antioxidation Mechanism of the 0Cr25Al5 Anodic Oxide Film by Constant Current Anodic Oxidation
文章编号:
16733851 (2011) 05076705
作者:
 叶逢春;  郭绍义;  汪伦
 浙江理工大学机械与自动控制学院， 杭州 310018
Author(s):
 YE Fengchun;  GUO Shaoyi;  WANG Lun
 School of Machinery & Automation, Zhejiang SciTech University, Hangzhou 310018, China
关键词:
 ; 阳极氧化;  铁铬铝;  抗氧化;  表面绝缘
分类号:
TG174.451
文献标志码:
A
摘要:
    采用恒流阳极氧化法，在铁铬铝表面制备抗氧化绝缘膜。对0Cr25Al5分别进行恒流0.2 A/dm2、0.4 A/dm2阳极氧化50 min，通过X射线衍射仪(XRD)、扫描电镜(SEM)等分析测试手段观测了氧化膜的显微组织并进行表面形貌分析，探讨不同电流密度对阳极氧化膜表面形貌的影响。结果表明：恒流0.4 A/dm2阳极氧化时，绝缘膜层主要由Al2O3和Cr3O4组成，其表面致密平整，裂纹较少，显著地提高了铁铬铝合金表面抗氧化及绝缘性能。

参考文献/References:

 ［1］王振东, 宫元生. 电热合金［M］. 北京: 化学工业出版社, 2006: 1328.
［2］ 武英, 谢建刚, 曾克里, 等. FeCrAl电热合金的研究进展［J］. 有色金属, 1999, 51(4): 8386.
［3］ 胡平, 蒙继龙, 黄文波. FeCrAl电热合金液浸原位生成绝缘膜的研究［J］. 材料与表面处理, 2001(5): 3436.
［4］ Lee W, Schwirn K, Strinhart M, et al. Structural engineering of nanoporous anodic aluminium oxide by pulse anodization of aluminium［J］. Nature Nanotechnology, 2008, （3）: 234239.
［5］ 周健儿, 李家科, 江伟辉. FeCrAl合金表面高温抗氧化陶瓷涂层的制备［J］. 硅酸盐学报, 2005, 33(9): 189193.
［6］ 吕建琴, 陈代伟, 赵甫良. 铝及铝合金铬酸阳极氧化工艺研究［J］. 涂料涂装与电镀, 2006, 4(6): 3140.
［7］ 刘妍. FeCrAl电热合金的研制与稀土对合金氧化行为的影响［D］. 哈尔滨: 哈尔滨工业大学, 2005.
［8］ 郭等柱, 侯士敏, 薛增泉, 等. 铝表面条纹状准有序结构的AFM研究［J］. 物理化学学报, 2001, 17(11): 961965.
［9］ 郭鹤桐, 王为. 铝阳极氧化的回顾与展望［J］. 材料保护, 2000, 33(1): 4345.
［10］ 刘红雯, 郭海明, 王业亮, 等. 阳极氧化铝模板表面自组织条纹的形成［J］. 物理学报, 2004, 53(2): 656660.
［11］ Shimizu K, Kobayashi K, Thompson G E, et al. Development of porous anodic films on aluminium［J］. Philosophical Magazine A, 1992, 66(4): 300308.
［12］ Stott F H, Wood G C, Stringer J. The influence of alloying elements on the development and maintenance of protective scales［J］. Oxid Metal, 1995, 44(12): 113143.

相似文献/References:

[1]陈智杰a,赵晓丽a,徐畅b,等. 有机颜料微胶囊在涂料染色中的应用及其染色效果分析[J].浙江理工大学学报,2013,30(01):1.
　CHEN Zhi jiea,ZHAO Xiao lia,XU Changb,et al. Application of Organic Pigment Microcapsule in Pigment Dyeingand Its Dyeing Results[J].Journal of Zhejiang Sci-Tech University,2013,30(05):1.
[2]詹永娟,谢维斌,姜晓云,等. 织物液态水传递性能的自动检测技术及应用[J].浙江理工大学学报,2013,30(01):6.
　ZHAN Yong juan,XIE Wei bin,JIANG Xiao yun,et al. Technology and Application of the Automatic Detection inTesting Liquid Transport Properties of Textiles[J].Journal of Zhejiang Sci-Tech University,2013,30(05):6.
[3]孙麒. 基于极大似然估计的织物图像分割[J].浙江理工大学学报,2013,30(01):12.
　SUN Qi. Textile Image Segmentation Based on theMaximum Likelihood Algorithm[J].Journal of Zhejiang Sci-Tech University,2013,30(05):12.
[4]巫静a,田彦杰b,汪澜a,等. 基于SVM理论的涤纶织物分散染料上染率模型研究[J].浙江理工大学学报,2013,30(01):21.
　WU Jinga,TIAN Yan jieb,WANG Lana,et al. Research on Modeling of DyeUptake Rate for Disperse Dyes onPolyester Fibers Based on SVM[J].Journal of Zhejiang Sci-Tech University,2013,30(05):21.
[5]周昊,徐英莲,齐素梅.微孔结构改性涤纶/棉混纺针织物服用性能的研究[J].浙江理工大学学报,2013,30(01):21.
　ZHAO Hao,XU Ying lian,QI Su mei. Research on Using Knitted Blend Fabric of Modified Polyesterby Cellular Structure and Cotton for Wearing[J].Journal of Zhejiang Sci-Tech University,2013,30(05):21.
[6]孙佳英,李艳清,章斐燕,等. 纺织结构复合材料铺层顺序设计与力学性能分析[J].浙江理工大学学报,2013,30(01):27.
　SUN Jia ying,LI Yan qing,ZHANG Fei yan,et al. Study on Layer Sequence Design and Mechanical Propertiesof Textile Structure Composites[J].Journal of Zhejiang Sci-Tech University,2013,30(05):27.
[7]丁源维,王騊,姚菊明,等. 静电纺制备TiO2/PVA复合纳米纤维及其光催化性能研究[J].浙江理工大学学报,2013,30(01):31.
　DING Yuan wei,WANG Tao,YAO Ju ming,et al. Photocatalytic Performance Investigation of TiO2/PVANanofibers Prepared by Electrospinning[J].Journal of Zhejiang Sci-Tech University,2013,30(05):31.
[8]章梦洁,伍仲,方园. 涤棉混纺织物阻燃性能的实验分析[J].浙江理工大学学报,2013,30(01):36.
　ZHANG Meng jie,WU Zhong,FANG Yang. Experimental Study on the PolyesterCotton BlendedFabrics Flame Retardancy[J].Journal of Zhejiang Sci-Tech University,2013,30(05):36.
[9]胡觉亮a,孔云鹏b,韩曙光a,等. 基于随机需求的服装供应链回购契约研究[J].浙江理工大学学报,2013,30(01):40.
　HU Jue lianga,KONG Yun pengb,HAN Shu guanga,et al. Study on Repurchase Contract in a Fashion Chainwith the Stochastic Demand[J].Journal of Zhejiang Sci-Tech University,2013,30(05):40.
[10]毛雯,阎玉秀. 针织服装供应商评价指标体系构建与权重确定[J].浙江理工大学学报,2013,30(01):46.
　MAO Wen,YAN Yu xiu. Building Evaluation Index System for Knitting Clothing Suppliersand Determining the Weight[J].Journal of Zhejiang Sci-Tech University,2013,30(05):46.

备注/Memo

备注/Memo:
 收稿日期： 2010-10-15
作者简介： 叶逢春(1988-)，男，江西上饶人，硕士研究生，主要从事摩擦学与表面处理方面的研究。
更新日期/Last Update: