新型P、N协效阻燃剂的制备及其在PA66中的应用()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第47-48卷
期数:
2022年自科第六期
页码:
806-813
栏目:
出版日期:
2022-11-10

文章信息/Info

Title:
Preparation of new P N synergistic flame retardant and  its application in PA66
文章编号:
1673-3851 (2022) 11-0806-08
作者:
王益文; 周杰睿; 冯新星; 张华鹏
1.浙江理工大学浙江省纤维材料和加工技术研究重点实验室，杭州 310018；2.军事科学院系统工程研究院军需工程技术研究所，北京 100010
Author(s):
WANG Yiwen; ZHOU Jierui; FENG Xinxing; ZHANG Huapeng
1.Zhejiang Provincial Key Laboratory of Fiber Materials and Manufacturing Technology, Zhejiang Sci-Tech University, Hangzhou 310018, China; 2.Institute of Military Engineering, Institute of Systems Engineering,Academy of Military Sciences, Beijing 100010, China
关键词:
植酸; 自组装法; 阻燃剂; PA66; 复合材料; 协效阻燃
分类号:
TS195-644
文献标志码:
A
摘要:
为获得适用于聚酰胺66（PA66）的协效型阻燃剂，以植酸（Phytic acid，PA）和三聚氰胺（Melamine，MEL）为原料，采用超分子自组装法制备一种P、N协效型阻燃剂三聚氰胺植酸盐（Melaminephytate，MPA），再将MPA与PA66熔融共混制备成复合材料，通过垂直燃烧仪、极限氧指数仪、锥形量热仪、电子万能试验机等对其阻燃性能、力学性能进行表征，并提出该阻燃剂可能的阻燃机理。结果表明：MPA可提升PA66的阻燃性能，当PA66/MPA复合材料中MPA质量分数达到8%时，垂直燃烧等级达到UL94 V 0级，极限氧指数大于27%，热释放速率峰值和烟雾释放总量显著降低；随着阻燃剂MPA含量的提升，PA66/MPA复合材料的力学性能有所下降，当MPA质量分数达到8%时，拉伸强度与断裂伸长率分别下降27.4%和24.1%；MPA可能的阻燃机理为P、N协效阻燃，二者同时在凝聚相和气相发挥作用，从而提升PA66的阻燃性能。该结果可为工程应用中协效化阻燃PA66的制备提供一定参考。

参考文献/References:

［ 1 ］ Bai Y P, Huang L, Huang T, et al. Synthesis and characterization of a water-soluble nylon copolyamide ［ J ］ . Polymer, 2013, 54(16): 4171-4176.

［ 2 ］ Luo D, Duan W F, Liu Y, et al. Melamine cyanurate surface treated by nylon of low molecular weight to prepare flame-retardant polyamide 66 with high flowability ［ J ］ . Fire and Materials, 2019, 43(3): 323-331.

［ 3 ］李占冲 , 孟凡涛 , 魏春城 , 等 . 无卤阻燃聚乙烯的研究进展［ J ］ . 塑料工业 ,2022,50(1): 1-5,19.

［ 4 ］ Milbrath M O G, Wenger Y, Chang C W, et al. Apparent half-lives of dioxins, furans, and polychlorinated biphenyls as a function of age, body fat, smoking status, and breast-feeding ［ J ］ . Environmental Health Perspectives, 2009, 117(3): 417-425 .

［ 5 ］ Renner R. Government Watch: In US, flame retardants will be voluntarily phased out ［ J ］ . Environmental Science & Technology, 2004, 38(1): 14-15.

［ 6 ］郑骏驰 , 舒帮建 , 孙兆懿 , 等 . 阻燃 PA6 复合材料研究进展［ J ］ . 工程塑料应用 , 2019, 47(11): 149-155.

［ 7 ］ Qian X D, Song L, Yuan B H, et al. Organic/inorganic flame retardants containing phosphorus, nitrogen and silicon: preparation and their performance on the flame retardancy of epoxy resins as a novel intumescent flame retardant system ［ J ］ . Materials Chemistry and Physics, 2014, 143(3): 1243-1252.

［ 8 ］ Li J F, Jiang W. Synthesis of a novel P-N flame retardant for preparing flame retardant and durable cotton fabric ［ J ］ . Industrial Crops and Products, 2021, 174: 114205.

［ 9 ］ Tao W, Hu X, Sun J H, et al. Effects of P-N flame retardants based on cytosine on flame retardancy and mechanical properties of polyamide 6 ［ J ］ . Polymer Degradation and Stability, 2020, 174: 109092.

［ 10 ］赵智垒 , 张金凯 , 张乃恩 , 等 . 一种含磷、氮的新型阻燃剂的合成及其在聚丙烯中的应用［ J ］ . 化工新型材料 , 2018, 46(7): 258-261.

undefined

备注/Memo

备注/Memo:
收稿日期： 2022-01-11
网络出版日期：2022-05-09
基金项目： 国家自然科学基金青年基金项目（52003242)
作者简介： 王益文（1997-），男，江西上饶人，硕士研究生，主要从事聚合物阻燃方面的研究。
通信作者： 张华鹏，E-mail：roczhp@163.com
更新日期/Last Update: 2022-11-07