|本期目录/Table of Contents|

[1]邢亚杰,蒋吾伟,张洪晶,等.等离子体接枝聚合制备非对称润湿性Janus棉织物的研究[J].浙江理工大学学报,2022,47-48(自科四):467-473.
 XING Yajie,JIANG Wuwei,ZHANG Hongjing,et al.Study on fabrication of asymmetric wettability Janus cotton fabric by plasma graft polymerization[J].Journal of Zhejiang Sci-Tech University,2022,47-48(自科四):467-473.
点击复制

等离子体接枝聚合制备非对称润湿性Janus棉织物的研究()
分享到:

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第47-48卷
期数:
2022年自科第四期
页码:
467-473
栏目:
出版日期:
2022-09-30

文章信息/Info

Title:
Study on fabrication of asymmetric wettability Janus cotton fabric by plasma graft polymerization
文章编号:
1673-3851 (2022) 07-0467-07
作者:
邢亚杰蒋吾伟张洪晶周克虞啸天李永强
浙江理工大学,a.纺织科学与工程学院(国际丝绸学院);b.生态染整技术教育部工程研究中心;c.先进纺织材料与制备技术教育部重点实验室,杭州 310018
Author(s):
XING Yajie JIANG Wuwei ZHANG Hongjing ZHOU Ke YU Xiaotian LI Yongqiang
a.College of Textile Science and Engineering (International Institute of Silk); b.Engineering Research Center for Eco-Dyeing & Finishing of Textiles, Ministry of Education; c.Key Laboratory on Advanced Textiles and Manufacturing and Preparation Technology, Ministry of Education, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
等离子体接枝聚合非对称润湿性超疏水Janus棉织物八甲基环四硅氧烷
分类号:
TS195-6
文献标志码:
A
摘要:
具有非对称润湿性的Janus材料通常通过构造化学梯度或形态梯度来设计和制备,存在工艺复杂、改性剂含氟和耐久性差等问题。为寻求简单、环保的制备方法,采用等离子体诱导接枝聚合八甲基环四硅氧烷(D4)到棉织物一侧,制得一侧具有超疏水性、另一侧具有亲水性的Jauns棉织物,并应用场发射扫描电子显微镜(FESEM)、红外光谱仪(FT IR)及视频接触角测试仪等对纤维表面形貌、表面基团变化及表面润湿性能进行表征。结果表明:当等离子体处理功率为80 W,处理时间为8 min时,制备的Janus棉织物超疏水面水接触角为152.1°,另一面保持亲水性,经过10次循环洗涤,超疏水面接触角仍可达150.3°,具有良好的耐洗性。所制备的Janus棉织物仍有较好的手感值,不影响穿着舒适性。该文结果为Janus材料制备和棉织物的功能化应用提供数据参考。

参考文献/References:

1 ] 王树涛 . 猪笼草口缘超湿滑的揭密 :JiangTaylor 毛细升与液体定向输运[ J . 化学进展 , 2017, 29(1): 34.

2 Zheng Y, Bai H, Huang Z, et al. Directional water collection on wetted spider silk J . Nature, 2010, 463(7281): 640643.
3 Zeng X, Qian L, Yuan X, et al. Inspired by stenocara beetles: from water collection to highefficiency waterinoil emulsion separation J . ACS Nano, 2017, 11(1): 760769.
4 Zhang H C, Hou X, Zeng L, et al. Bioinspired artificial single ion pump J . Journal of the American Chemical Society, 2013, 135(43): 1610216110.
5 Cai Y H, Chen D Y, Li N J, et al. A facile method to fabricate a doublelayer stainless steel mesh
for effective separation of waterinoil emulsions with high flux J . Journal of Materials Chemistry A, 2016, 4(48): 1881518821.
6 Wang Z J, Wang Y, Liu G J, Rapid and efficient separation of oil from oilinwater emulsions using a Janus cotton fabric J . Angewandte Chemie, 2016, 55(4): 12911294.
7 ] 李维斌,张程,刘军 . 超疏水棉织物制备及其在油水过滤分离中应用[ J . 纺织学报 , 2021, 42(8): 109114.
8 Wu M B, Yang H C, Wang J J, et al. Janus membranes with opposing surface wettability enabling oiltowater and watertooil emulsification J . Acs Applied Materials & Interfaces, 2017, 9(6): 50625066.
9 Chi H, Xu Z, Wei Z, et al. Fabrics with novel airoil amphibious, spontaneous oneway watertransport capability for oil/water separation J . Acs Applied Materials & Interfaces, 2021, 13(24): 2915029157.
10 Tian X L, Jin H, Sainio J, et al. Droplet and fluid gating by biomimetic janus membranes J . Advanced Functional Materials, 2014, 24(38): 60236028.

undefined

相似文献/References:

[1]张晓龙,郑丽霞,王騊,等. 等离子体制备亲水性聚乙烯薄膜及其性能研究[J].浙江理工大学学报,2012,29(06):795.
 ZHANG Xiao long,ZHENG Li xia,WANG Tao,et al. Characterization of Hydrophilic Polyethylene FilmPrepared by Plasma Treatment[J].Journal of Zhejiang Sci-Tech University,2012,29(自科四):795.
[2]郑丽霞,王騊,陈光良,等.低温等离子体法制备超亲水PE薄膜及其性能研究[J].浙江理工大学学报,2013,30(04):482.
 ZHENG Lixia,WANG Tao,CHEN Guangliang,et al.Research on Preparation of Superhydrophilic PE Film with low temperature Plasma Method and Its Properties[J].Journal of Zhejiang Sci-Tech University,2013,30(自科四):482.

备注/Memo

备注/Memo:
收稿日期:2022-01-06
网络出版日期:2022-03-18
基金项目:国家自然科学基金项目(52103068);浙江省科技厅一般公益项目(LGG20E030007)
作者简介:邢亚杰(1997-),女,吉林白山人,硕士研究生,主要从功能纺织品方面的研究
通信作者:李永强,E-mail:yqqli@163.com
更新日期/Last Update: 2022-09-06