|本期目录/Table of Contents|

[1]张永飞,吴光杰,康硕,等.YxGd(1-x)BO3:Eu3+荧光粉的制备及其荧光性能[J].浙江理工大学学报,2021,45-46(自科四):445-452.
　ZHANG Yongfei,WU Guangjie,KANG Shuo,et al.Preparation and fluorescence properties ofYxGd(1-x)BO3:Eu3+phosphors[J].Journal of Zhejiang Sci-Tech University,2021,45-46(自科四):445-452.
点击复制

YxGd(1-x)BO3:Eu3+荧光粉的制备及其荧光性能()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第45-46卷
期数:
2021年自科第四期
页码:
445-452
栏目:
出版日期:
2021-07-10

文章信息/Info

Title:
Preparation and fluorescence properties ofYxGd(1-x)BO3:Eu3+phosphors
文章编号:
1673-3851 (2021) 07-0445-08
作者:
张永飞; 吴光杰; 康硕; 喻志奎; 王龙成
浙江理工大学材料科学与工程学院，杭州 310018
Author(s):
ZHANG Yongfei;  WU Guangjie;  KANG Shuo;  YU Zhikui;  WANG Longcheng
School of Materials Science & Engineering, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
YxGd(1-x)BO3:Eu3+; K+掺杂; 发光强度; 量子效率; 荧光粉
分类号:
TB34
文献标志码:
A
摘要:
采用水热法制备复合基质YxGd(1-x)BO3:Eu3+荧光粉，以提升红色荧光粉的发光强度和量子效率。研究不同x值对YxGd(1-x)BO3:Eu3+荧光粉形貌、发光性能与物相结构的影响，并在最佳的x取值下进行K+离子掺杂制备出不同K+离子掺杂量的YxGd(1-x)BO3:Eu3+荧光粉。采用X射线衍射仪、场发射扫描电子显微镜和荧光光谱仪等对样品进行表征。结果表明：当x为06时，YxGd(1-x)BO3:Eu3+荧光粉的发光性能最好，发光强度与YBO3:Eu3+和GdBO3:Eu3+荧光粉相比分别提高了39-47%和75-77%，量子效率与YBO3:Eu 3+和GdBO3:Eu 3+荧光粉相比分别提高了60-53%和93-11%；当K+的掺杂量为1%时，Y 06Gd04BO3:Eu 3+: K+荧光粉的发光性能最好，掺杂后发光强度提高了55-73%，量子效率提高了49-83%。该研究表明适量的K+离子的掺入可以改善YxGd(1-x)BO3:Eu3+荧光粉的光致发光性能。

参考文献/References:

［1］ 吴亚茹, 曹兴忠, 李玉晓, 等. 稀土铕离子掺杂聚合物基荧光材料的研究进展［J］. 材料导报, 2015, 29(9):141-145.
［2］ Koparkar K A, Bajaj N S, Omanwar S K. Effect of partially replacement of Gd 3+ ions on fluorescence properties of YBO3: Eu 3+ phosphor synthesized via precipitation method［J］. Optical Materials, 2015, 39: 74-80.
［3］ 杨智,任敏.稀土硼酸盐的结构及其真空紫外（VUV）荧光性质［J］.高等学校化学学报,2000,21(9):1339-1343.
［4］ Becker P. Borate materials in nonlinear optics［J］. Advanced Materials, 1998, 10(13): 979-992.
［5］ Dubey V, Kaur J, Agrawal S, et al. Effect of Eu 3+ concentration on photoluminescence and thermoluminescence behavior of YBO3: Eu 3+ phosphor［J］. Superlattices and Microstructures, 2014, 67: 156-171.
［6］ Kim D S, Lee R Y. Synthesis and photoluminescence properties of (Y, Gd)BO3: Eu phosphor prepared by ultrasonic spray［J］. Journal of Materials Science, 2000, 35(19): 4777-4782.
［7］ Priya R, Pandey O P, Dhoble S J. Review on the synthesis, structural and photophysical properties of Gd2O3 phosphors for various luminescent applications［J］. Optics & Laser Technology, 2021, 135: 106663.
［8］ 李群, 张文军, 张永飞, 等. YxGd(1-x)BO3:Eu3+荧光粉的制备及其荧光性能［J］. 浙江理工大学学报(自然科学版), 2020, 43(3): 315-321.
［9］ 廖苑滨. 碱土元素与铕共掺杂钒酸钇发光材料的制备及性能研究［D］. 南昌: 南昌大学, 2014: 12-33.
［10］ 郑贤火. 非稀土金属离子掺杂对氧化钇粉末荧光性能的影响［D］. 杭州: 浙江理工大学, 2016: 22-48.

备注/Memo

备注/Memo:
收稿日期：2020-12-28
网络出版日期：2021-03-31
基金项目：浙江省基础工艺研究计划项目(LGG20E02001)
作者简介：张永飞(1990-)，男，安徽亳州人，硕士研究生，主要从事稀土发光材料方面的研究
通信作者：王龙成，E-mail：wlongcheng@zstu.edu.cn
更新日期/Last Update: 2021-09-13