NiCo 2 S4&KB复合材料的制备及其电化学性能()
分享到:

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第43-44卷
期数:
2020年自科三期
页码:
322-331
栏目:
出版日期:
2020-06-09

文章信息/Info

Title:
Preparation and electrochemical property of  NiCo 2 S4&KB composite materials
文章编号:
1673-3851 (2020) 05-0322-10
作者:
朱仁霞张茜马丹阳蔡玉荣
浙江理工大学材料科学与工程学院,杭州 310018
Author(s):
ZHU Renxia ZHANG Qian MA Danyang CAI Yurong
College of Material Science and Engineering, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
NiCo 2S 4&KB复合材料正极材料锂硫电池科琴黑电化学性能
分类号:
TM912
文献标志码:
A
摘要:
针对锂硫电池中活性物质硫和Li2S/Li2S2导电性差,充放电过程中硫的体积膨胀、中间产物多硫化物离子易溶于电解液等问题,以科琴黑(KB)、六水合硝酸镍(Ni(NO3)2·6H2O)、六水合硝酸钴(Co(NO3)2·6H2O)和尿素为原料,经水热和热熔过程制备出均匀分散的NiCo2S4&KB/S正极材料,并将该正极材料应用于锂硫电池电化学性能研究。结果表明:经过05 M硫化钠处理的NiCo2S4&KB/S电极表现出优异的电化学性能;在低电流密度下(02 C),初始放电比容量为1278 mAh/g,循环100圈后其比容量仍保持在984 mAh/g,库伦效率达到9420%;在50 C的高电流密度下,首圈放电比容量为437 mAh/g,200圈后容量仍能达到331 mAh/g,平均每圈衰减率为012%。该复合材料为锂硫电池的正极材料的设计与制备提供一种新的思路和方法。

参考文献/References:

[1] 宋永华, 阳岳希, 胡泽春. 电动汽车电池的现状及发展趋势[J]. 电网技术, 2011, 35(4): 1-7.
[2] Fang R P, Zhao S Y, Sun Z H, et al. More reliable lithiumsulfur batteries: Status, solutions and prospects[J]. Advanced Materials, 2017, 29(48): 1606823.
[3] Li Z, Huang Y M, Yuan L X, et al. Status and prospects in sulfurcarbon composites as cathode materials for rechargeable lithiumsulfur batteries[J]. Carbon, 2015, 92: 41-63.
[4] Hu J J, Li G R, Gao X P. Current status, problems and challenges in lithiumsulfur batteries[J]. Journal of Inorganic Materials, 2013, 28(11): 1181-1186.
[5] Mikhaylik Y V, Kovalev I, Schock R, et al. High energy rechargeable LiS cells for EV application: Status, remaining problems and solutions[J]. ECS Transactions, 2010, 25(35): 23-34.
[6] Scrosati B, Garche J. Lithium batteries: Status, prospects and future[J]. Journal of Power Sources, 2010, 195(9): 2419-2430.
[7] He J R, Manthiram A. A review on the status and challenges of electrocatalysts in lithiumsulfur batteries[J]. Energy Storage Materials, 2019, 20: 55-70.
[8] 林山, 朱仁霞, 马丹阳, 蔡玉荣,等. MOFs改性玻璃纤维膜的制备及其在锂硫电池隔膜中的应用[J]. 浙江理工大学学报(自然科学版), 2019, 41(5): 615-622.
[9] 蔡周阳, 李玉姣, 林山,等. 氮掺杂介孔碳/硫复合材料的制备及其用作锂硫电池正极材料的研究[J]. 浙江理工大学学报(自然科学版), 2018, 39(5): 551-559.
[10] Evers S, Nazar L F. New approaches for high energy density lithiumsulfur battery cathodes[J]. Accounts of Chemical Research, 2012, 46(5): 1135-1143.

备注/Memo

备注/Memo:
收稿日期:2019-11-02
网络出版日期:2020-01-02
基金项目:浙江理工大学基本科研业务费项目(2019Y006)
作者简介:朱仁霞(1993-),女,江西上饶人,硕士研究生,主要从事锂硫电池正极方面的研究
通信作者:蔡玉荣,E-mail:caiyr@zstu.edu.cn
更新日期/Last Update: 2020-06-10