|本期目录/Table of Contents|

[1]朱善文,陈帅杰,王恩亮,等.聚磷酸铵/水性环氧形状记忆阻燃复合材料制备及其性能[J].浙江理工大学学报,2019,41-42(自科六):786-792.
 ZHU Shanwen,CHEN Shuaijie,WANG Enliang,et al.Preparation and properties of ammonium polyphosphate/waterborne  epoxy shape memory and flame retardant composites[J].Journal of Zhejiang Sci-Tech University,2019,41-42(自科六):786-792.
点击复制

聚磷酸铵/水性环氧形状记忆阻燃复合材料制备及其性能()
分享到:

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第41-42卷
期数:
2019年自科六期
页码:
786-792
栏目:
出版日期:
2019-10-31

文章信息/Info

Title:
Preparation and properties of ammonium polyphosphate/waterborne  epoxy shape memory and flame retardant composites
文章编号:
1673-3851 (2019) 11-0786-07
作者:
朱善文陈帅杰王恩亮黄云峰董余兵
浙江理工大学材料与纺织学院、丝绸学院,杭州 310018
Author(s):
ZHU Shanwen CHEN Shuaijie WANG Enliang HUANG Yunfeng DONG Yubing
Silk Institute, College of Materials and Textiles, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
水性环氧树脂聚磷酸铵形状记忆性能阻燃性能
分类号:
TB332
文献标志码:
A
摘要:
以水性环氧树脂(Waterborne epoxy, WEP)为基体,聚磷酸铵(Ammonium polyphosphate, APP)为阻燃剂,采用机械共混、冷冻干燥和热压成型工艺制备APP/WEP形状记忆阻燃复合材料,期望获得一种兼具优良形状记忆性能和阻燃性能的复合材料。通过SEM、TGA、DSC、TMA、万能试验机、极限氧指数测试仪分别对APP/WEP复合材料进行了表征与分析。结果表明:与WEP相比,APP/WEP复合材料的阻燃性能得到了显著提高。WEP的极限氧指(Limited oxygen index, LOI)为182%,当APP质量分数为200%时,APP/WEP复合材料的LOI值高达276%;另外,APP/WEP复合材料仍保持较好的形状记忆性能,即使APP质量分数增至500%时,其形状固定率和形状回复率仍分别高达905%和970%。因此,其复合材料是一种兼具阻燃和形状记忆多功能复合材料,该复合材料的制备工艺可为拓宽WEP及其复合材料的应用奠定材料基础和实验参考。

参考文献/References:

[1] 魏堃, 朱光明, 唐玉生, 等.热固性环氧树脂形状记忆聚合物的研究进展[J]. 高分子材料科学与工程, 2012, 28(8): 183-186.
[2] Jozsef K K, Sandor K K. Review of progress in shape memory epoxies and their composites[J]. Polymers, 2018, 10(1): 2-38.
[3] 王恩亮, 董余兵. 形状记忆聚合物复合材料研究进展[J]. 浙江理工大学学报, 2018, 39(1): 31-36.
[4] Cheng Y, Ben B Z, Xiao Y Y. Study on preparation and properties for epoxy shape memory polymer[J].Advanced Materials Research, 2013, 18(6): 463-466.
[5] Wang Y K, Tian W C, Liu X H, et al. Thermal sensitive shape memory behavior of epoxy composites reinforced with silicon carbide whiskers[J]. Applied Sciences, 2017, 7(1): 4-10.
[6] 郭何云, 王煦. 水性环氧树脂制备方法的研究进展[J]. 合成化学, 2017, 25(5): 457-460.
[7] 赵建国, 杨利娴, 陈晓珊, 等. 美国涂料行业VOC污染控制政策与技术研究[J]. 涂料工业, 2012, 42(2): 44-52.
[8] Dong Y, Ni Q Q, Fu Y. Preparation and characterization of waterborne epoxy shape memory composites containing silica[J].Composites Part A: Applied Science and Manufacturing, 2014, 72(12): 1-10.
[9] Dong Y, Ding J, Wang J, et al. Synthesis and properties of the vapourgrown carbon nanofiber/epoxy shapememory and conductive foams prepared via latex technology[J]. Composites Science and Technology, 2013, 76(34): 8-13.
[10]Dong Y, Ni Q Q, Li L, et al. Novel vaporgrown carbon nanofiber/epoxy shape memory nanocomposites prepared via latex technology[J]. Materials Letters, 2014, 132(25): 206-209.

备注/Memo

备注/Memo:
收稿日期:2018-10-29
网络出版日期: 2019-03-30
基金项目:国家自然科学基金项目(51703204,51473147)
作者简介:朱善文(1995-),男,安徽六安人,硕士研究生,主要从事形状记忆聚合物复合材料方面的研究
通信作者:董余兵,E-mail:dyb19831120@zstu.edu.cn
更新日期/Last Update: 2019-11-25