Title:
Preparation and electrochemical performance of metal sulfide loaded with carbon network
文章编号:
1673-3851 (2019) 05-0327-06
作者:
王健杨天鹏金达莱王耐艳
浙江理工大学材料与纺织学院、丝绸学院,杭州 310018
Author(s):
WANG Jian YANG Tianpeng JIN Dalai WANG Naiyan
Silk Institute, College of Materials and Textiles, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
NiS2CoSNiCo2S4活性炭纤维网状体复合材料电化学性能
分类号:
TB332
文献标志码:
A
摘要:
采用水热法在活性炭纤维网状体(Carbon network,CNW)表面分别负载NiS2、CoS和NiCo2S4。通过X射线衍射仪、场发射式扫描电子显微镜对复合体系进行结构表征,结果表明:NiCo2S4呈现纳米棒状,单根纳米棒的长度约为800 nm,直径约为50 nm。电化学性能测试结果显示:相较于CNW/ NiS2和CNW/CoS,CNW/NiCo2S4复合电极表现出更为优越的电化学性能,其比电容达到994.2 F/g(电流密度为5 mA/cm2)。经1000次充放电循环后仍保持87.4%的电容。

参考文献/References:

[1] 叶灵,黄正宏,沈万慈,等.石墨质多孔炭在不同电解液中的电化学性能研究[J]. 新型炭材料, 2018,33(1):53-60.
[2] Ma L, Liu R, Niu H, et al. Flexible and freestanding electrode based on polypyrrole/graphene/bacterial cellulose paper for supercapacitor[J]. Composites Science & Technology, 2016, 137:87-93.
[3] Wang G, Zhang L, Zhang J. A review of electrode materials for electrochemical supercapacitors[J]. Chemical Society Reviews, 2012, 41(2):797-828.
[4] 宋世姣.玉米皮基多孔碳材料的制备及超级电容器性能研究[D]. 哈尔滨:黑龙江大学, 2017:1-8.
[5] 周新民,孙晖.新型储能元件综述:超级电容及其应用[J]. 变频器世界, 2009(6):28-30.
[6] Kena Chen. Graphenebased materials for flexible energy storage devices[J]. Energy Chemistry, 2018,27(1):12-24.
[7] Kim J, Kim F, Huang J. Seeing graphenebased sheets[J]. Materials Today, 2010, 13(3):28-38.
[8] Kaempgen M, Chan C K, Ma J, et al. Printable Thin Film supercapacitors using singlewalled carbon nanotubes[J]. Nano Letters, 2015, 9(5):1872.
[9] Ktz R,Carlen M. Principles and applications of electrochemical capacitors[J]. Electrochimica Acta, 2000, 45(15):2483-2498.
[10] Li X, Zheng F, Zhou D F, Luo Y M, et al. Stable RuO2based ternary composite electrode of sandwiched for electrochemical capacitors[J]. Electrochimica Acta, 2018, 289(11):292-310

备注/Memo

备注/Memo:
收稿日期: 2018-09-19
网络出版日期: 2018-11-02
作者简介: 王健(1994-),男,安徽铜陵人,硕士研究生,主要从事电极材料方面的研究
通信作者: 金达莱,E-mail:jindl@zstu.edu.cn
更新日期/Last Update: 2019-05-29