[1]Carrington M TAKAWIRA,虞雅伦,庄广清,等.二氧化硅气凝胶的常压低温快速制备和表征[J].浙江理工大学学报,2016,35-36(自科2):178-181.
　Carrington M TAKAWIRA,YU Yalun,ZHUANG Guangqing,et al.Fast Preparation of Inorganic Silica Aerogels Under Ambient  Pressure and Low Temperature and Its Representation[J].Journal of Zhejiang Sci-Tech University,2016,35-36(自科2):178-181.
点击复制

二氧化硅气凝胶的常压低温快速制备和表征()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第35-36卷
期数:
2016年自科2期
页码:
178-181
栏目:
出版日期:
2016-03-10

文章信息/Info

Title:
Fast Preparation of Inorganic Silica Aerogels Under Ambient  Pressure and Low Temperature and Its Representation
文章编号:
1673-3851 (2016) 02-0178-04
作者:
Carrington M TAKAWIRA; 虞雅伦; 庄广清;  黄益; 邵建中
浙江理工大学,a.生态染整技术教育部工程研究中心；b.先进纺织材料与制备技术教育部重点实验室，杭州 310018
Author(s):
Carrington M TAKAWIRA;  YU Yalun;  ZHUANG Guangqing;  HUANG Yi;  SHAO Jianzhong
a.Engineering Research Center for Eco Dyeing and Finishing of Textiles, Ministry of Education; b. Key Laboratory of Advanced Textile and Manufactwring Technology, Ministry of Education, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
气凝胶; 溶胶凝胶; 溶剂置换; 表面改性
分类号:
TQ127.2
文献标志码:
A
摘要:
二氧化硅气凝胶凭借其极高的孔隙率和低导热性能已成为近年的热门研究材料之一。文章在常压低温条件下以正硅酸四乙酯为硅源，异丙醇和正己烷溶液为溶剂，通过低表面能溶剂置换以及粒子表面改性的方法快速制备无机气凝胶材料，并采用FESEM、HRTEM、FTIRATR光谱及X射线衍射分析等手段对所制备气凝胶材料的表观形貌、化学结构以及结晶性能进行表征。研究表明: 制得的二氧化硅气凝胶表面连有疏水的Si—CH 3基团、存在丰富的介孔结构，粒子和孔隙的尺寸较小，是一种孔隙率高、轻质、且热稳定性较高的微晶纳米材料，具有广泛的应用前景。

参考文献/References:

［1］ PIERRE A C, PAJONK G M. Chemistry of aerogels and their applications［J］. Chemical Reviews, 2002, 102 (11): 4243-4266.
［2］ 姚连增, 李小毛, 蔡维理, 等. SiO2气凝胶的制备与表征［J］. 硅酸盐学报, 1998, 26(3): 319-323.
［3］ 李伟, 王霞瑜, 张平,等. 快速溶胶凝胶法制备SiO2气凝胶的研究［J］. 湘潭大学自然科学学报, 2002, 24(1): 64-67.
［4］ 刘朝辉, 苏勋家, 侯根良, 等. 二氧化硅气凝胶的制备和表征［J］. 无机盐工业, 2006, 38(7): 25-27.
［5］ LU X, CAPS R, FRICKE J, et al. Correlation between structure and thermal conductivity of organic aerogels［J］. Journal of NonCrystalline Solids, 1995, 188(3): 226-234.
［6］ CAPADONA L A, MEADOR M A B, ALUNNI A, et al. Flexible, lowdensity polymer crosslinked silica aerogels［J］. Polymer, 2006, 47(16): 5754-5761.
［7］ KIM M T. Deposition behavior of hexamethydisiloxane films based on the FTIR analysis of Si—O—Si and Si—CH3 bonds［J］. Thin Solid Films, 1997, 311(12): 157-163.
［8］ 胡银, 张和平, 黄冬梅, 等. 柔韧性块体疏水二氧化硅气凝胶的制备及表征［J］. 硅酸盐学报, 2013, (8): 1037-1041.
［9］ 刘洋, 张毅, 李东旭. 常压干燥制备疏水性SiO2气凝胶［J］. 功能材料, 2015(5): 5132-5135.
［10］ LI L, YALCIN B, NGUYEN B N, et al. Flexible nanofiber reinforced aerogel (xerogel) synthesis, manufacture, and characterization［J］. ACS Applied Materials & Interfaces, 2009, 1(11): 2491-2501.

相似文献/References:

[1]朱莹,刘涛,丁新波,等.氧化纤维素气凝胶的制备及其吸附性能[J].浙江理工大学学报,2020,43-44(自科六):806.
　ZHU Ying,LIU Tao,DING Xinbo,et al.Preparation and adsorption properties of oxidized cellulose aerogels[J].Journal of Zhejiang Sci-Tech University,2020,43-44(自科2):806.
[2]郭秦铭,崔金萍,陈明星,等.CA/MoS2复合物的制备及其去除六价铬的性能[J].浙江理工大学学报,2021,45-46(自科二):212.
　GUO Qinming,CUI Jinping,CHEN Mingxing,et al.Preparation of CA/MoS2 composite and its removal of hexavalent chromium[J].Journal of Zhejiang Sci-Tech University,2021,45-46(自科2):212.
[3]葛文斌,冯新星,张华鹏.TEMPO介导氧化纤维素模板Zr/Si气凝胶的合成和测试[J].浙江理工大学学报,2021,45-46(自科四):437.
　GE Wenbin,FENG Xinxing,ZHANG Huapeng.Synthesis and test of Zr/Si hybrid aerogel from  TEMPOoxidized cellulose templates[J].Journal of Zhejiang Sci-Tech University,2021,45-46(自科2):437.
[4]黄俊文,唐峰,李营战,等.MXene/CNF复合气凝胶的制备及其光热转换性能[J].浙江理工大学学报,2021,45-46(自科六):744.
　HUANG Junwena,TANG Fenga,LI Yingzhanb,et al.Preparation of MXene/CNF composite aerogel and its photothermal conversion property[J].Journal of Zhejiang Sci-Tech University,2021,45-46(自科2):744.
[5]关炳月,刘涛,丁新波,等.羧化纤维素气凝胶的制备及其对亚甲基蓝染料的吸附性能[J].浙江理工大学学报,2022,47-48(自科二):166.
　GUAN Bingyue,LIU Tao,DING Xinbo,et al.Preparation of carboxylated cellulose aerogel and its adsorption  properties for methylene blue dye[J].Journal of Zhejiang Sci-Tech University,2022,47-48(自科2):166.
[6]王文召,陈雪飞,杜磊.对位芳纶气凝胶的制备及其孔结构调控[J].浙江理工大学学报,2022,47-48(自科五):635.
　WANG Wenzhao,CHEN Xuefei,DU Lei.Preparation of para aramid aerogel and its  pore structure regulation[J].Journal of Zhejiang Sci-Tech University,2022,47-48(自科2):635.

备注/Memo

备注/Memo:
收稿日期： 2015-06-06
作者简介： Carrington M. TAKAWIRA（1988-），男，津巴布韦人，硕士研究生，主要从事气凝胶制备方面的研究
通信作者： 邵建中，E-mail：jshao@zstu.edu.cn
更新日期/Last Update: 2016-06-01