DOPO衍生物/PA66复合材料的制备及性能分析()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第47-48卷
期数:
2022年自科第五期
页码:
678-686
栏目:
出版日期:
2022-09-10

文章信息/Info

Title:
Preparation and properties of DOPO derivative/PA66 composite
文章编号:
1673-3851 (2022) 09-0678-09
作者:
周杰睿; 王益文; 冯新星; 张华鹏
1.浙江理工大学浙江省纤维材料和加工技术研究重点实验室，杭州 310018；2.军事科学院系统工程研究院军需工程技术研究所，北京 100010
Author(s):
ZHOU Jierui; WANG Yiwen; FENG Xinxing; ZHANG Huapeng
1.Zhejiang Provincial Key Laboratory of Fiber Materials and Processing Technology, Zhejiang Sci-Tech University, Hangzhou 310018, China; 2.Institute of Military Engineering,  Institute of Systems Engineering, Academy of Military Sciences, Beijing 100010, China
关键词:
DOPO衍生物; 尼龙66; 复合材料; 阻燃; 共混改性; 磷系阻燃剂
分类号:
TB332；TQ323-6
文献标志码:
A
摘要:
为了实现阻燃尼龙66(PA66)的简易、高效制备，采用1,6-己二胺(HMDA)、衣康酸(ITA)、9,10-二氢-9-氧杂-10-磷杂菲-10-氧化物(DOPO)和氢氧化钙（Ca(OH) 2）为原材料，设计合成了一种具有高阻燃效率的DOPO衍生物阻燃剂；将其与PA66共混改性，得到DOPO衍生物/PA66复合材料。对DOPO衍生物/PA66复合材料进行极限氧指数和垂直燃烧试验，利用热重分析仪、锥形量热仪、电子万能试验机表征了复合材料的热稳定性、阻燃性能及力学性能。结果表明：DOPO衍生物能促进PA66成炭，残炭量随阻燃剂含量的增加会不断上升；当DOPO衍生物质量分数达到10%时，DOPO衍生物/PA66复合材料阻燃等级达到V-0级，LOI达到27.5%；随着阻燃剂添加量的增加，点燃时间会延后，最大热释放速率峰值和总热释放量会显著减少；当DOPO衍生物质量分数达到10%时，DOPO衍生物/PA66复合材料的拉伸强度下降了19.1%，断裂伸长率下降了9.0%。该结果可为合成新型高效率磷系阻燃剂及共混制备阻燃PA66提供参考。

参考文献/References:

［1］李双庆, 汤溢融, 杨永波. 阻燃尼龙研究进展［J］. 工程塑料应用, 2020, 48(2): 132-138.

［2］Jin W J, Cheng X W, He W L, et al. Flame retardant and antidripping modification of polyamide 6 fabric by guanidine sulfamate with enhanced durability［J］. Thermochimica Acta, 2021, 706: 179073.

［3］付晓婷, 李谦, 朱凯, 等. 包覆红磷阻燃增强PA66的性能研究［J］. 塑料工业, 2021, 49(9): 130-133.

［4］Jin X D, Sun J, Zhang J S, et al. Preparation of a novel intumescent flame retardant based on supramolecular interactions and its application in polyamide 11［J］. ACS Applied Materials & Interfaces, 2017, 9(29): 24964-24975.

［5］张日东, 陈勇伟, 周岚, 等. 2羧乙基苯基次膦酸的胺化处理及其在尼龙6中的阻燃应用［J］. 浙江理工大学学报（自然科学版）, 2015, 33(4): 447-451.

［6］Chen M J, Shao Z B, Wang X L, et al. Halogenfree flameretardant flexible polyurethane foam with a novel nitrogenphosphorus flame retardant［J］. Industrial & Engineering Chemistry Research, 2012, 51(29): 9769-9776.

［7］Liu W, Zhang S, Chen X S, et al. Thermal behavior and fire performance of nylon6, 6 fabric modified with acrylamide by photografting［J］. Polymer Degradation and Stability, 2010, 95(9): 1842-1848.

［8］韩红丽, 李巧玲, 崔丽丽. 尼龙66的无卤阻燃研究与进展［J］. 合成技术及应用, 2007,22(3): 34-37.

［9］王忠卫, 张荣科, 高军, 等. 羟甲基苯基次膦酸阻燃共聚酯的合成与性能［J］. 高分子材料科学与工程, 2008, 24(5): 24-27.

［10］Pondelak A, kapin A S, Knez N, et al. Improving the flame retardancy of wood using an ecofriendly mineralisation process［J］. Green Chemistry, 2021, 23(3): 1130-1135.

undefined

备注/Memo

备注/Memo:
收稿日期： 2022-01-10
网络出版日期：2022-04-05
基金项目： 国家自然科学基金青年基金项目（52003242)
作者简介： 周杰睿（1996-），男，湖北黄冈人，硕士研究生，主要从事尼龙66阻燃改性方面的研究
通信作者： 张华鹏，E-mail: roczhp@163.com
更新日期/Last Update: 2022-09-07