无溶剂聚醚氨基嵌段共聚硅油柔顺剂的制备及其在羊绒织物上的应用()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第45-46卷
期数:
2021年自科第二期
页码:
185-190
栏目:
出版日期:
2021-03-10

文章信息/Info

Title:
Preparation of solventfree polyether amino block copolymer silicone oil softener and its application on fleece fabrics
文章编号:
1673-3851 (2021) 03-0185-06
作者:
王娟; 任琳琳; 蒋吾伟; 邢亚杰; 李永强
浙江理工大学，a. 纺织科学与工程学院；b. 先进纺织材料与制备技术教育部重点实验室；c. 生态染整技术教育部工程研究中心，杭州 310018
Author(s):
WANG Juan a; b;  REN Linlin a; b;  JIANG Wuwei a; b;  XING Yajie a; b;  LI Yongqiang a; b; c
a. College of Textile Science and Engineering; b. Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education; c. Engineering Research Center for EcoDyeing and Finishing of Textiles, Ministry of Education, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
无溶剂; 聚醚氨基嵌段共聚硅油; 乳化性能; 柔顺剂; 羊绒织物; 应用性能
分类号:
TQ317-9
文献标志码:
A
摘要:
以自制端环氧聚醚硅油和聚醚胺D230为反应原料，在不添加溶剂的情况下制备聚醚氨基嵌段共聚硅油，并将其用于羊绒织物的后整理。研究反应温度、反应时间和反应物摩尔比对产物乳化性能的影响，通过傅里叶红外光谱、热重分析仪、纳米粒度仪和场发射扫描电子显微镜对聚醚氨基嵌段共聚硅油柔顺剂进行结构表征和形貌分析，并对其整理后羊绒织物的白度、亲水性及相对手感值进行测试，结果表明：无溶剂聚醚氨基嵌段共聚硅油的最佳合成工艺为：当反应温度为80 ℃，反应时间为6 h，自制端环氧聚醚硅油（Mw=8000）与聚醚胺D230摩尔比为1∶14时，所制聚醚氨基嵌段共聚硅油环氧值最低；乳液带有蓝光，平均粒径为5626 nm，粒径分散指数为0046；经聚醚氨基嵌段共聚硅油乳液整理后的羊绒织物的亲水性和柔软性提高，白度基本不变。该嵌段共聚硅油具有优异的综合性能，具有重要的实用价值。

参考文献/References:

［1］ zam A E, Spontak R J, Genzer J. Toward the development of a versatile functionalized silicone coating［J］. ACS Applied Materials & Interfaces, 2014, 6(24):22544-22552.
［2］ Wei Y, Zheng C, Chen P, et al. Synthesis of multiblock linear polyether functional amino silicone softener and its modification of surface properties on cotton fabrics［J］. Polymer Bulletin, 2019, 76(1): 447-467.
［3］ Jin Y F, Pu Q, Fan H. Synthesis of linear piperazine/polyether functional polysiloxane and its modification of surface properties on cotton fabrics［J］. ACS Applied Materials & Interfaces, 2015, 7(14): 7552-7558.
［4］ Choudhury A K R, Chatterjee B, Saha S, et al. Comparison of performances of macro, micro and nano silicone softeners［J］. Journal of the Textile Institute, 2012, 103(9): 1012-1023.
［5］ Mohamed A L, ErRafik M, Moller M. Suitability of Confocal Raman microscopy for monitoring the penetration of PDMS compounds into cotton fibres［J］. Carbohydrate Polymers, 2013, 96(1): 305-313.
［6］ Xu C S, Ouyang L, Liu H Y, et al. Synthesis of blocking polyether silicone oil and silicone blocking waterborne polyurethane and application to cashmere knitted fabric finishing［J］. Textile Research Journal, 2015, 85(19): 2040-2050.
［7］ 张强, 安秋凤, 李晓璐, 等. 亲水性聚醚氨基硅QPEAS硅乳的制备及应用［J］. 印染助剂, 2018, 35(6): 21-25.
［8］ Svensson A V, Johnson E S, Nylander T, et al. Surface deposition and phase behavior of oppositely charged polyionsurfactant ion complexes. 2. A means to deliver silicone oil to hydrophilic surfaces［J］. ACS Applied Materials & Interfaces, 2010, 2(1): 143-156.［9］ 徐成书, 吴梦婷, 任燕, 等. 线性聚醚嵌段氨基硅油的制备及其性能［J］. 纺织学报, 2019, 40(8): 89-94.
［10］ 刘锦凡, 汤金伟, 程文静, 等. 蓬松型聚醚嵌段硅油的制备及应用性能研究［J］. 化工管理, 2018(16): 49-52.

相似文献/References:

[1]裘珂俊,戚栋明,孙阳艺.中空介孔硅负载Karstedt催化剂对无溶剂有机硅树脂固化性能的影响[J].浙江理工大学学报,2023,49-50(自科四):516.
　QIU Kejun,QI Dongming,SUN Yangyi.Effect of hollow mesoporous silica loaded Karstedt catalyst on  the curing properties of solvent-free silicone resin[J].Journal of Zhejiang Sci-Tech University,2023,49-50(自科二):516.

备注/Memo

备注/Memo:
收稿日期：2020-11-16
网络出版日期：2021-01-05
基金项目：浙江省科技厅一般公益项目（LGG20E030007）；国家自然科学基金项目（51773181,51403189）
作者简介：王娟(1995-)，女，安徽安庆人，硕士研究生，主要从事绿色染整新技术方面的研究
通信作者：李永强，E-mail：yqqli@163.com
更新日期/Last Update: 2021-03-23