[1]陈静,祝洪良,刘一夫,等.基于超声喷雾热解法制备的球形YAG:Eu 3+  荧光粉性能表征[J].浙江理工大学学报,2020,43-44(自科五):595-601.
　CHEN Jing,ZHU Hongliang,LIU Yifu,et al.Performance characterization of spherical YAG:Eu 3+ phosphors prepared by ultrasonic spray pyrolysis[J].Journal of Zhejiang Sci-Tech University,2020,43-44(自科五):595-601.
点击复制

基于超声喷雾热解法制备的球形YAG:Eu 3+  荧光粉性能表征()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第43-44卷
期数:
2020年自科五期
页码:
595-601
栏目:
出版日期:
2020-09-18

文章信息/Info

Title:
Performance characterization of spherical YAG:Eu 3+ phosphors prepared by ultrasonic spray pyrolysis
文章编号:
1673-3851 (2020) 05-0595-07
作者:
陈静; 祝洪良; 刘一夫; 李雪
浙江理工大学材料科学与工程学院，杭州 310018
Author(s):
CHEN Jing;  ZHU Hongliang;  LIU Yifu;  LI Xue
School of Materials Science and Engineering, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
YAG:Eu 3+ ; 荧光粉; 超声喷雾热解法; 发光性能
分类号:
TB34
文献标志码:
A
摘要:
为实现球形YAG:Eu 3+荧光粉的大规模生产，提出通过超声喷雾热解法制备尺寸均匀的球形YAG:Eu 3+荧光粉。先将含有三种金属离子（Y、Al和Eu）的硝酸盐配置成前驱体溶液，然后利用超声高频谐振器将前驱体溶液转为雾滴，再将前驱体雾滴在管式炉中快速蒸发、脱水，聚拢成球形固体前驱体，最后在900 ℃的管式炉中原位晶化转为YAG:Eu 3+荧光粉。采用X射线衍射（XRD）、扫描电子显微镜（SEM）和能量色散X射线光谱（EDS）对产物的物相、形貌和成分进行分析。结果表明：制备所得产物是纯立方结构的YAG:Eu 3+ 荧光粉，呈现出规则的球形形貌，尺寸分布范围窄（100～300 μm），平均直径为1-59～255 μm；荧光粉直径会随着前驱体摩尔浓度的升高而增大；发光光谱显示，球形YAG:Eu 3+荧光粉在紫外光的激发下，在594 nm和615 nm处表现出典型的红光发射。文章采用的超声喷雾热解法具有连续、可控、产物均匀规律等特点，有望在球形YAG:Eu 3+荧光粉的生产中得到实际应用。

参考文献/References:

［1］ Game D N, Ingale N B, Omanwar S K. Converted white light emitting diodes from Ce3+ doping of alkali earth sulfide phosphors［J］. Materials Discovery, 2016, 4:1-7.
［2］ Kurrey M S, Tiwari A, Khokhar M S K, et al.Thermoluminescence investigations of sol–gel derived and γirradiated rare earth (Eu and Nd) doped YAG nanophosphors［J］. Journal of Luminescence, 2015, 164:94-98.
［3］ Zhang R, Lin H, Yu Y L, et al. A newgeneration color converter for highpower white LED: transparent Ce3+: YAG phosphoringlass［J］. Laser & Photonics Reviews, 2014, 8(1): 158-164.
［4］ Yi X Z, Zhou S M, Chen C, et al. Fabrication of Ce: YAG, Ce, Cr: YAG and Ce: YAG/Ce, Cr: YAG duallayered composite phosphor ceramics for the application of white LEDs［J］. Ceramics International, 2014, 40(5): 7043-7047.
［5］ Mczka M, Bednarkiewicz A, MendozaMendoza E, et al. Lowtemperature synthesis, phonon and luminescence properties of Eu doped Y3Al5O12 (YAG) nanopowders［J］. Materials Chemistry and Physics, 2014, 143(3): 1039-1047.
［6］ Kolesnikov I E, Tolstikova D V, Kurochkin A V, et al. Eu3+ concentration effect on luminescence properties of YAG:Eu3+ nanoparticles［J］. Optical Materials, 2014, 37: 306-310.
［7］ Zhou Y H, Lin J, Wang S B, et al. Preparation of Y3Al5O 12: Eu phosphors by citric–gel method and their luminescent properties［J］. Optical Materials, 2002, 20(1): 13-20.
［8］ Song Z, Liao J, Ding X L, et al. Synthesis of YAG phosphor particles with excellent morphology by solid state reaction［J］. Journal of Crystal Growth, 2013, 365: 24-28.
［9］ Ikesue A, Furusato I, Kamata K. Fabrication of polycrystal line, transparent YAG ceramics by a solidstate reaction method［J］. Journal of the American Ceramic Society, 1995, 78(1): 225-228.
［10］ 黎学明, 向星, 杨文静, 等. 化学共沉淀法合成YAG∶Eu 3+ 红色荧光粉及其光致发光性质［J］. 半导体光电, 2010, 31(1): 71-74.

相似文献/References:

[1]马非凡,郑贤火,廖世才,等.钾离子对GdBO-3:Tb-3+ 发光性能的影响[J].浙江理工大学学报,2017,37-38(自科4):506.
　MA Feifan,ZHENG Xianhuo,LIAO Shicai,et al.Effect of K+ Doping on Luminescent Property of GdBO-3:Tb-3+ Powder[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科五):506.
[2]刘一夫,祝洪良,李雪,等.球状YVO4:Eu3+/SiO2复合结构材料的喷雾干燥法制备及其发光性能[J].浙江理工大学学报,2020,43-44(自科二):189.
　LIU Yifu,ZHU Hongliang,LI Xue,et al.Preparation and photoluminscence properties of spherical YVO 4:Eu 3+ /SiO 2 composites by spray drying[J].Journal of Zhejiang Sci-Tech University,2020,43-44(自科五):189.
[3]李群,张文军,张永飞,等.GdxY(2-x)O3:Eu3+荧光粉的制备及其荧光性能[J].浙江理工大学学报,2020,43-44(自科三):315.
　LI Qun,ZHANG Wenjun,ZHANG Yongfei,et al.Preparation and fluorescence properties of GdxY(2-x)O3:Eu3+ phosphors[J].Journal of Zhejiang Sci-Tech University,2020,43-44(自科五):315.
[4]张永飞,吴光杰,康硕,等.YxGd(1-x)BO3:Eu3+荧光粉的制备及其荧光性能[J].浙江理工大学学报,2021,45-46(自科四):445.
　ZHANG Yongfei,WU Guangjie,KANG Shuo,et al.Preparation and fluorescence properties ofYxGd(1-x)BO3:Eu3+phosphors[J].Journal of Zhejiang Sci-Tech University,2021,45-46(自科五):445.

备注/Memo

备注/Memo:
收稿日期：2020-03-27
网络出版日期：2020-06-03
基金项目：国家自然科学基金项目（51872262）；浙江省自然科学基金项目（LY18B010008）
作者简介：陈静（1994-），女，四川德阳人，硕士研究生，主要从事锂离子材料制备方面的研究
通信作者：祝洪良，E-mail: zhuhl@zstu.edu.cn
更新日期/Last Update: 2020-09-15