|本期目录/Table of Contents|

[1]陈俊超,周文进,孙娟,等.油相溶剂对PIP/TMC复合纳滤膜结构和性能的影响[J].浙江理工大学学报,2020,43-44(自科三):301-307.
　CHEN Junchao,ZHOU Wenjin,SUN Juan,et al.Effects of oil phase solvent on structure and properties of PIP/TMC composite nanofiltration membranes[J].Journal of Zhejiang Sci-Tech University,2020,43-44(自科三):301-307.
点击复制

油相溶剂对PIP/TMC复合纳滤膜结构和性能的影响()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第43-44卷
期数:
2020年自科三期
页码:
301-307
栏目:
出版日期:
2020-06-09

文章信息/Info

Title:
Effects of oil phase solvent on structure and properties of PIP/TMC composite nanofiltration membranes
文章编号:
1673-3851 (2020) 05-0301-07
作者:
陈俊超; 周文进; 孙娟; 唐红艳
浙江理工大学，a.浙江省纤维材料和加工技术研究重点实验室; b.纺织纤维材料与加工技术国家地方联合工程实验室，杭州 310018
Author(s):
CHEN Junchao;  ZHOU Wenjin;  SUN Juan;  TANG Hongyan
a. Zhejiang Provincial Key Laboratory of Fiber Materials and Processing Technology; b. National Engineering Lab for Textile Fiber Materials and Processing Technology, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
聚四氟乙烯; 复合纳滤膜; 混合溶剂; 界面聚合; 结构和性能
分类号:
TQ 028-8
文献标志码:
A
摘要:
以亲水改性后的聚四氟乙烯（PTFE）平板膜作基膜，采用不同配比的正己烷和环己烷作为油相溶剂，哌嗪（PIP）和均苯三甲酰氯（TMC）分别作为水相单体和油相单体，通过界面聚合的方法在亲水PTFE平板膜上制备得到一系列的聚酰胺复合纳滤膜。研究正己烷和环己烷的配比对PIP/TMC复合纳滤膜的表面化学组成和微观形貌的变化规律影响；并通过优化制膜条件，制备出性能良好的PIP/TMC复合纳滤膜。结果表明：随着混合油相溶剂中环己烷含量的增加，油相溶剂和水相间界面张力逐渐增大，PIP/TMC复合纳滤膜截留率逐渐下降、渗透通量逐渐上升；当混合油相溶剂中环己烷和正己烷配比为25∶75，PIP的浓度为1-5 wt%以及TMC的浓度为0-4 wt%时，PIP/TMC复合纳滤膜的性能达到最佳，截留率为94-72%，渗透通量为3-5 L/(m 2·h)。

参考文献/References:

［1］ Fu F F, Zhou B Q, Ouyang Z J, et al. Multifunctional cholesterolmodified dendrimers for targeted drug delivery to cancer cells expressing folate receptors［J］. Chinese Journal of Polymer Science, 2019, 37(2): 129-135.
［2］ Wang S C, Wang L Z. Recent progress of tungstenand molybdenumbased semiconductor materials for solarhydrogen production［J］. Tungsten, 2019(1): 19-45.
［3］ Terra N M, Madrona G S, Ferreira F B, et al. High performance of asymmetric alumina hollow fiber membranes for the clarification of genipap (genipa Americana L.) fruit extract［J］. Food and Bioprocess Technology, 2019, 12(1): 27-38.
［4］ 张志箭, 徐安厚, 赵孔银, 等. 聚羟基丁酸酯纳米纤维支撑海藻酸钙纳滤膜制备及抗污染性能［J］. 高分子材料科学与工程, 2017, 33(7): 179-183.
［5］ 金中茜, 王峰, 陈建勇. 小分子醇对PES/CDA膜结构和性能的影响［J］. 浙江理工大学学报(自然科学版), 2019, 41(3): 341-346.
［6］ Wang Q, Zhang G S, Li Z S, et al. Preparation and properties of polyamide/titania composite nanofiltration membrane by interfacial polymerization［J］. Desalination, 2014, 352: 38-44.
［7］ 张芯. 高压电场强化法制备荷电聚醚酰亚胺纳滤膜及其性能研究［J］. 塑料工业, 2019,47(5): 28-32.
［8］ JinW Q, Toutianoush A, Tieke B. Use of polyelectrolyte layerbylayer assemblies as nanofiltration and reverse osmosis membranes［J］. Langmuir, 2003,19(7):2550-2553.
［9］ Ghosh A K, Jeong B, Huang X F, et al. Impacts of reaction and curing conditions on polyamide composite reverse osmosis membrane properties［J］. Journal of Membrane Science, 2008, 311(1): 34-45.
［10］ Gohil J M, Suresh A K. Development of high flux thinfilm composite membrane for water desalination: A statistical study using response surface methodology［J］. Desalination & Water Treatment, 2014, 52(28/29/30): 5219-5228.

相似文献/References:

[1]王峰,朱海霖,郭玉海. 聚四氟乙烯微孔膜亲水性与抗污性的关系研究[J].浙江理工大学学报,2012,29(05):641.
　WANG Feng,ZHU Hai lin,GUO Yu hai. Relationship between the Hydrophilicity and Antifouling Performance of Polytetrafluoroethylene (PTFE) Microporous Membrane[J].Journal of Zhejiang Sci-Tech University,2012,29(自科三):641.
[2]张毅,卫傅翔,唐红艳.PI/PTFE复合膜的制备及其分离性能的研究[J].浙江理工大学学报,2017,37-38(自科5):635.
　ZHANG Yi,WEI Fuxiang,TANG Hongyan.Study on the Preparation of Polyimide/PolytetrafluoroethyleneComposite Membrane and Its Separation Property[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科三):635.
[3]黄宁欣,陈俊超,唐红艳.PDMS对PEI/TMC复合纳滤膜结构和性能的影响[J].浙江理工大学学报,2020,43-44(自科四):506.
　HUANG Ningxin,CHEN Junchao,TANG Hongyan.Effect of PDMS on structure and performance of PEI/TMC composite nanofiltration membranes[J].Journal of Zhejiang Sci-Tech University,2020,43-44(自科三):506.
[4]陈慕荣,刘雪强,张华鹏,等.离心纺丝法制备PTFE/PVA复合微/纳米纤维膜[J].浙江理工大学学报,2020,43-44(自科五):625.
　CHEN Murong,LIU Xueqiang,ZHANG Huapeng,et al.Preparation of PTFE / PVA composite micro/nano fiber membrane by centrifugal spinning[J].Journal of Zhejiang Sci-Tech University,2020,43-44(自科三):625.
[5]王安拓,李祥龙,侯腾,等.不同结构聚四氟乙烯微纳米纤维的制备[J].浙江理工大学学报,2021,45-46(自科六):758.
　WANG Antuo,LI Xianglong,HOU Teng,et al.Preparation of PTFE micronano fibers with different structures[J].Journal of Zhejiang Sci-Tech University,2021,45-46(自科三):758.

备注/Memo

备注/Memo:
收稿日期：2019-10-24
网络出版日期：2020-01-02
基金项目：浙江省自然科学基金项目（LY19B060016）
作者简介：陈俊超（1994-），男，浙江东阳人，硕士研究生，主要从事膜分离改性方面的研究
通信作者：唐红艳，E-mail：hytang2004@163.com
更新日期/Last Update: 2020-06-10