 ZHANG Lixiang,LIU Tao,REN Xu,et al.Preparation and controlled doping of copper substituted hollow bioactive glass nanospheres[J].Journal of Zhejiang Sci-Tech University,2019,41-42(自科四):433-439.
点击复制

掺铜中空生物玻璃纳米球的制备及可控掺杂()
分享到:

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第41-42卷
期数:
2019年自科四期
页码:
433-439
栏目:
出版日期:
2019-06-20

文章信息/Info

Title:
Preparation and controlled doping of copper substituted hollow bioactive glass nanospheres
文章编号:
1673-3851 (2019) 07-0433-07
作者:
张丽香刘涛任旭陈颖睿丁新波
浙江理工大学,a.材料与纺织学院;b.科技与艺术学院,杭州 310018
Author(s):
ZHANG Lixiang LIU Tao REN Xu CHEN Yingrui DING Xinbo
a. College of Materials and Textiles; b. Keyi College, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
中空生物玻璃纳米球溶胶凝胶法制备可控掺杂
分类号:
TQ127-2
文献标志码:
A
摘要:
通过研究铜元素掺杂对中空生物玻璃纳米球形貌结构的影响,进一步探究中空生物玻璃铜掺杂与药物缓释性能的关系,以获得具有一定抗菌作用和药物控释性能的骨组织工程支架。以聚丙烯酸(Polyacrylic acid,PAA)为模板剂,以硅源、磷源、钙源及铜源为无机盐前驱体,结合采用溶胶凝胶法制备掺铜中空生物玻璃纳米球(Copper substituted hollow bioactive glass, CuHBGNs),改变CaO、CuO组分的原料添加量来调控所得掺铜中空生物玻璃纳米球的掺杂量;采用SEM、TEM、EDS、FTIR、XRD、TGA及N2吸附脱附等测试表征掺铜中空生物玻璃纳米球的形貌结构、元素组成及热稳定性。结果表明:在生物玻璃体系中引入不同摩尔比的CaO、CuO组分能实现掺铜中空生物玻璃纳米球的可控掺杂,所制备纳米球样品外观形貌及结构基本不变,粒径、孔径均可调。溶胶凝胶法准备的可控掺铜中空生物玻璃在药物输送和骨组织修复领域具有广阔的应用前景。

参考文献/References:

[1] Jiang P, Lin H, Xing R, et al. Synthesis of multifunctional macroporousmesoporous TiO2bioglasses for bone tissue engineering[J]. Journal of Solgel Science and Technology, 2012, 61(2): 421-428.
[2] 轩肖娜, 朱海霖, 陈建勇. 丝素蛋白/纳米生物玻璃复合多孔支架的结构与性能[J]. 功能材料, 2013, 44(2): 226-231.
[3] Hench L L. Bioceramics: From concept to clinic[J]. Journal of the American Ceramic Society, 1991, 74(7): 1487-1510.
[4] Du X, He J. Spherical silica micro/nanomaterials with hierarchical structures: Synthesis and applications[J]. Nanoscale, 2011, 3(10): 3984-4002.
[5] Wang F, Tang Y, Zhang B, et al. Preparation of novel magnetic hollow mesoporous silica microspheres and their efficient adsorption[J]. Journal of Colloid and Interface Sscience, 2012, 386(1): 129-134.
[6] Yang Y H, Liu C H, Liang Y H, et al. Hollow mesoporous hydroxyapatite nanoparticles (hmHANPs) with enhanced drug loading and pHresponsive release properties for intracellular drug delivery[J]. Journal of Materials Chemistry B, 2013, 1(19): 2447-2450.
[7] Wu C, Chang J, Xiao Y. Mesoporous bioactive glasses as drug delivery and bone tissue regeneration platforms[J]. Therapeutic Delivery, 2011, 2(9): 1189-1198.
[8] Pappas G S, Bilalis P, Kordas G C. Synthesis and characterization of SiO2CaOP2O5 hollow nanospheres for biomedical applications[J]. Materials Letters, 2012, 67(1): 273-276.
[9] Li B, Luo W, Wang Y, et al. Bioactive SiO2CaOP2O5 hollow nanospheres for drug delivery[J]. Journal of NonCrystalline Solids, 2016, 447: 98-103.
[10] Wu C, Zhou Y, Xu M, et al. Coppercontaining mesoporous bioactive glass scaffolds with multifunctional properties of angiogenesis capacity, osteostimulation and antibacterial activity[J]. Biomaterials, 2013, 34(2): 422-433.

备注/Memo

备注/Memo:
收稿日期: 2018-09-28
网络出版日期: 2018-12-01
基金项目:浙江理工大学纺织科学与工程一流学科(A)研究生创新基金项目(11110131201716);浙江省自然科学基金项目(LY16E020012);浙江理工大学科研启动基金项目(15012081Y);浙江理工大学科技与艺术学院面上项目(KY2017010)
作者简介:张丽香(1992-),女,湖南岳阳人,硕士研究生,主要从事现代纺织技术及新产品开发方面的研究
通信作者:丁新波,E-mail:dxblt@zstu.edu.cn
更新日期/Last Update: 2019-09-16