Title:
Comfort control of cotton fabrics containing  crosslinking thermosensitive microgels
文章编号:
1673-3851 (2019) 05-0292-08
作者:
范娜钟齐王际平
浙江理工大学,a.材料与纺织学院;b.先进纺织材料与制备技术教育部重点实验室,杭州 310018
Author(s):
FAN Na ZHONG Qi WANG Jiping
a.College of Materials and Textiles; b.Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
温敏微凝胶智能纺织品透湿性舒适度调控
分类号:
TS195
文献标志码:
A
摘要:
以N 异丙基丙烯酰胺(NIPAM)、聚乙二醇甲醚甲基丙烯酸酯(OEGMA 300)和聚(乙二醇)甲基丙烯酸酯(EGMA)为单体,通过自由基乳液聚合的方法合成聚(N异丙基丙烯酰胺 co 聚(乙二醇)甲醚甲基丙烯酸酯 co聚(乙二醇)甲基丙烯酸酯)温敏微凝胶(P(NIPAM co OEGMA 300 co EGMA));利用傅立叶变换红外光谱(FTIRATR)、紫外可见分光光度计(UV Vis)、动态光散射(DLS)、场发射扫描电子显微镜(FESEM)和视频接触角(CA)对P(NIPAM co OEGMA 300 co EGMA)进行表征;采用P(NIPAM co OEGMA 300 co EGMA)制备智能纺织品,通过扫描电子显微镜、智能白度测试仪、智能风格仪、多功能电子织物强力机等对织物的性能进行表征。结果表明,经过P(NIPAM co OEGMA 300 co EGMA)微凝胶整理后的棉织物柔软度下降,透湿性可以通过外界环境温度进行调节。

参考文献/References:

[1] Berndt I, Richtering W. Doubly temperature sensitive coreshell microgels[J]. Macromolecules, 2003, 36(23): 8780-8785.
[2] Tauer K, Gau D, Schulze S, et al. Thermal property changes of poly(Nisopropyl acrylamide) microgel particles and block copolymers[J]. Colloid and Polymer Science, 2009, 287(3):299-312.
[3] Zhong Q, Chen Y Y, Guan S L, et al. Smart cleaning cotton fabrics crosslinked with thermoresponsive and flexible poly(2(2methoxyethoxy) ethoxyethyl methacrylatecoethylene glycol methacrylate)[J]. Rsc Advances, 2015, 5(48):38382-38390.
[4] Debord J D, Lyon L A, Synthesis and characterization of pHresponsive copolymer microgels with tunable volume phase transition temperatures[J]. Langmuir, 2003, 19(18):7662-7664.
[5] Richter A, Paschew G, Klatt S, et al. Review on hydrogelbased pH sensors and microsensors[J]. Sensors, 2008, 8(1):561-581.
[6] Suzuki A, Tanaka T. Phase transition in polymer gels induced by visible light[J]. Nature, 1990, 346(6282):345-347.
[7] 罗宣干, 王坦. N异丙基丙烯酰胺系温度敏感聚合物和水凝胶的研究进展[J]. 化学通报, 1996(4):10-15.
[8] 张胜兰, 沈新元, 杨庆,等. 热敏水凝胶的研究进展[J]. 河南师范大学学报:自然科学版, 2000, 28(1):4246.
[9] Oya T, Nikodem T, Aliakbar J, et al. Influence of the length and grafting density of PNIPAM chains on the colloidal and optical properties of quantum dot/PNIPAM assemblies[J]. Nanotechnology, 2011, 22(26):265701-265706.
[10] Guan Y, Zhang Y J. PNIPAM microgels for biomedical applications: From dispersed particles to 3D assemblies[J]. Soft Matter, 2011, 7(14):6375-6384.

备注/Memo

备注/Memo:
收稿日期:2018-11-23
网络出版日期: 2018-12-29
基金项目:国家自然科学基金项目(51403186,51611130312)
作者简介:范娜(1993-),女,陕西渭南,硕士研究生,主要从事温敏微凝胶及智能纺织品方面的研究
通信作者:钟齐,E-mail:qi.zhong@zstu.edu.cn
更新日期/Last Update: 2019-05-29