 ZHOU Chuankai,YU Bin,SUN Hui,et al.Preparation of TiO-2-Ag Mesoporous Microspheres by GelsolMethod and Analysis of Its Antibacterial Property[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科4):485-490.
点击复制

溶胶凝胶法制备 TiO-2-Ag的介孔微球及其抗菌性能研究()
分享到:

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第37-38卷
期数:
2017年自科4期
页码:
485-490
栏目:
出版日期:
2017-07-10

文章信息/Info

Title:
Preparation of TiO-2-Ag Mesoporous Microspheres by GelsolMethod and Analysis of Its Antibacterial Property
文章编号:
1673-3851 (2017) 04-0485-06
作者:
周传凯于斌孙辉朱斐超
浙江理工大学,a.材料与纺织学院;b.“产业用纺织材料制备技术”浙江省重点实验室,杭州 310018
Author(s):
ZHOU Chuankai YU Bin SUN Hui ZHU Feichao
a.College of Materials and Textiles; b.Key Laboratory of Preparation ofIndustrial Textile Materials, Ministry of Education, Zhejiang Sci-TechUniversity, Hangzhou 310018, China
关键词:
溶胶凝胶法煅烧温度TiO-2-Ag介孔微球抗菌性
分类号:
TQ134.1
文献标志码:
A
摘要:
以钛酸丁酯和硝酸银分别作为钛源、银源,聚乙二醇系为扩孔剂,采用溶胶凝胶法制备TiO-2-Ag介孔微球。通过调节煅烧温度优化煅烧工艺,并通过热场发射扫描电子显微镜(EDS/EBSD)、X射线衍射仪(XRD)、傅里叶红外光谱仪(FTIR)及比表面积及孔体积测量仪(BET)等对所得产物的形貌、晶体结构、化学组成和比表面积等进行分析。采用震荡法来评定TiO-2-Ag介孔微球的抗菌性。研究表明:采用溶胶凝胶法制备的TiO-2-Ag介孔微球,其Ag粒子在TiO-2表面均匀分布;在煅烧温度为500℃下添加扩孔剂,能有效提高TiO-2-Ag介孔微球的比表面积,增大TiO-2-Ag吸附能力;TiO-2-Ag介孔微球具有良好的抗菌性能。

参考文献/References:

[1] WANG Y, XUE X, YANG H. Modification of the antibacterial activity of Zn/TiO-2, nanomaterials through different anions doped[J]. Vacuum,2014,101(3):193-199.
[2] 朱燕峰,张娟,张义永,等.溶胶凝胶法制备改性TiO2纳米薄膜及其防腐蚀性能[J].物理化学学报,2012,28(2):393-398.
[3] LU Y, SUN J, ZHANG B. Preparation and lubricating properties of a new antibacterial emulsion containing nano-TiO-2 for cold rolling strips[J]. China Petroleum Processing & Petrochemical Technology,2016,18(3):110-118.
[4] TODAN L, DASCALESCU T, PREDA S, et al. Porous nanosized oxide powders in the MgO-TiO-2, binary system obtained by solgel method[J]. Ceramics International,2014,40(10):15693-15701.
[5] CAI H, MU W, LIU W, et al. Solgel synthesis highly porous titanium dioxide microspheres with cellulose nanofibrilsbased aerogel templates[J]. Inorganic Chemistry Communications,2015,51(51):71-74.
[6] 郭立雪,费成斌,李波,等.Ag@TiO2纳米颗粒等离激元效应增强钙钛矿太阳能薄膜电池性能[J].硅酸盐学报,2016,44(10):1393-1400.
[7] 孙娜,赵祥,肖正刚.Ag-TiO-2空心复合微球制备及其光催化性能[J].功能材料,2015,46(2):2115-2119.

相似文献/References:

[1]张春山,丁新波,韩建,等.PVC建筑膜材用纳米SiO2粒径的可控性及其羰基化研究[J].浙江理工大学学报,2013,30(03):312.
 ZHANG Chun shan,DING Xin bo,HAN Jian,et al.Controllability of Particle Size of Nano SiO2 for PVC Architectural Membrane Material[J].Journal of Zhejiang Sci-Tech University,2013,30(自科4):312.
[2]吴震弘,汪洋,冯佩,等.TiO 2薄膜的制备及其对304不锈钢防腐性能的研究[J].浙江理工大学学报,2014,31-32(自科2):179.
 WU Zhen hong,WANG Yang,FENG Pei,et al.Preparation of TiO 2 Thin Films and Study of Its Corrosion Resistance Performance for 304 Stainless Steel[J].Journal of Zhejiang Sci-Tech University,2014,31-32(自科4):179.
[3]蒋乐,魏琪,周彬,等.Gd掺杂和Gd/N共掺杂TiO-2光催化剂的制备及其光催化性能研究[J].浙江理工大学学报,2017,37-38(自科1):152.
 JIANG Le,WEI Qi,Zhou Bin,et al.Preparation of Gddoped and Gd/Ncodoped TiO-2 Photocatalyst and Its Photocatalytic Performance Research[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科4):152.
[4]李智慧,张立,刘涛,等.中空生物玻璃形貌结构及其活性研究[J].浙江理工大学学报,2017,37-38(自科5):737.
 LI Zhihui,ZHANG Li,LIU Tao,et al.Synthesis and Bioactivity of Hollow Bioactive Glass Nanospheres[J].Journal of Zhejiang Sci-Tech University,2017,37-38(自科4):737.
[5]鞠凤宇,刘涛,张丽香,等.介孔镂空生物玻璃微球调控及形成机制[J].浙江理工大学学报,2018,39-40(自科2):171.
 JU Fengyu,LIU Tao,ZHANG Lixiang,et al.Control and formation mechanism of mesoporous hollow bioactive glass nanospheres[J].Journal of Zhejiang Sci-Tech University,2018,39-40(自科4):171.
[6]汪文华,雷彩虹,余媛,等.基于Zn 2+与Mo 6+共掺杂TiO2复合粒子的抗菌PVDF平板膜制备及其性能分析[J].浙江理工大学学报,2022,47-48(自科四):524.
 WANG Wenhua,LEI Caihong,YU Yuan,et al.Preparation of antibacterial PVDF flat membrane based on Zn 2+与Mo 6+ codoped TiO2 composite particles and its property analysis[J].Journal of Zhejiang Sci-Tech University,2022,47-48(自科4):524.

备注/Memo

备注/Memo:
收稿日期: 2016-11-02
网络出版日期: 2017-03-28
基金项目: 国家自然科学基金项目(1201682-A);浙江省公益性技术运用研究计划项目(2017C33077)
作者简介: 周传凯(1991-),男,湖北孝感人,硕士研究生,主要从事熔喷非织造材料方面的研究
通信作者: 孙辉,E-mail:51878123@qq.com
更新日期/Last Update: 2017-09-25