|本期目录/Table of Contents|

[1]朱丽虹,蒋乐,汪洋.溶剂热法制备ZnO/竹炭及其光降解甲基橙性能[J].浙江理工大学学报,2016,35-36(自科6):826-831.
　ZHU Lihong,JIANG Le,WANG Yang.Preparation of ZnO/Bamboo Charcoal by Solvothermal Method and Its Photocatalytic Degradation Property on Methyl Orange[J].Journal of Zhejiang Sci-Tech University,2016,35-36(自科6):826-831.
点击复制

溶剂热法制备ZnO/竹炭及其光降解甲基橙性能()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第35-36卷
期数:
2016年自科6期
页码:
826-831
栏目:
出版日期:
2016-11-10

文章信息/Info

Title:
Preparation of ZnO/Bamboo Charcoal by Solvothermal Method and Its Photocatalytic Degradation Property on Methyl Orange
文章编号:
1673-3851 (2016) 06-0826-06
作者:
朱丽虹; 蒋乐; 汪洋
浙江理工大学，a．材料与纺织学院；b理学院，杭州 310018
Author(s):
ZHU Lihong; JIANG Le;  WANG Yang
a．College of Materials and Textiles；b．School of Science，Zhejiang  Sci-Tech University，Hangzhou 310018，China
关键词:
溶剂热法; ZnO/竹炭; 光催化; 甲基橙; 降解率
分类号:
O649.2
文献标志码:
A
摘要:
采用溶剂热法制备ZnO/竹炭复合材料。利用X射线衍射（XRD）、扫描电镜（SEM）、傅立叶变换红外(FT IR) 光谱、光致发光（PL）谱等技术对制备的光催化剂进行表征。以甲基橙为偶氮染料模型，研究二乙烯三胺（DETA）添加量（ V ）、焙烧温度（ T ）及循环次数（ n ）对ZnO/竹炭复合材料光催化降解甲基橙性能的影响。其实验结果表明：采用溶剂热法在竹炭表面负载的ZnO颗粒连续均匀。实验条件 V DETA =600 μL，焙烧温度 T =400 ℃， ZnO的光生电子和空穴复合率相对较低，该条件下制备的ZnO/竹炭复合材料紫外光照后对甲基橙的降解率可达到97.9%， 循环三次后对甲基橙的光降解率仍保持在94%以上。

参考文献/References:

［1］ 陈文渊.竹炭吸附水中有机污染物的研究［D］.福州:福建农林大学,2004.
［2］ WANG  X, WU Z, WANG Y, et al. Adsorptionphotodegradation of humic acid in water by using ZnO coupled TiO 2/bamboo charcoal under visible light irradiation［J］. Journal of Hazardous Materials,2013,262:16-24.
［3］ WU  C H, SHR J F, WU C F, et al. Synthesis and photocatalytic characterization of titaniasupported bamboo  charcoals by using solgel method［J］. Journal of Materials Processing Technology,2008,203(1):326-332.
［4］ 邵金璐,卢秀萍.纳米ZnO的应用研究进展［J］.浙江化工,2006,36(10):21-24.
［5］ ZHANG J, ZHAO D, WANG J, et al. Photocatalytic oxidation of dibenzothiophene using TiO2/bamboo charcoal［J］. Journal of Materials Science,2009,44(12):3112-3117.
［6］ YANG J L, AN S J, PARK W I, et al. Photocatalysis using ZnO thin films and nanoneedles grown by metalorganic chemical vapor deposition［J］. Advanced Materials,2004,16(18):1661-1664.
［7］ PALANISAMY S, CHEN S M, Sarawathi R. A novel nonenzymatic hydrogen peroxide sensor based on reduced graphene oxide/ZnO composite modified electrode［J］. Sensors and Actuators B: Chemical,2012,166:372-377.
［8］ SHEN X, MU D, CHEN S, et al. Enhanced electrochemical performance of ZnOloaded/porous carbon composite as anode materials for lithium ion batteries［J］. ACS Applied Materials & Interfaces,2013,5(8):3118-3125.
［9］ 刘德峥.微乳液技术制备纳米微粒的研究进展［J］.化工进展,2002,21(7):466-470.
［10］ 张峰振,吴超飞,胡芸,等.卤代有机污染物的光化学降解［J］.化学进展,2014,26(6):1079-1098.
［11］ 肖宗湖,张萌.ZnO薄膜结构缺陷与发光性能研究(一)［J］人工晶体学报,2006,35(6):1322-1327,1331.

备注/Memo

备注/Memo:
收稿日期： 2015-11-22
作者简介： 朱丽虹（1990-），女，浙江湖州人，硕士研究生，主要从事纳米TiO2制备及光催化应用方面的研究
通信作者： 汪洋，E-mail：wwyy2001@sina.com
更新日期/Last Update: 2016-11-18