|本期目录/Table of Contents|

[1]吴三定,王騊,郑晋生,等.真空活化法制备TiO-2可见光催化剂及其长效性研究[J].浙江理工大学学报,2016,35-36(自科6):814-819.
　WU Sanding,WANG Tao,ZHENG Jinsheng,et al.Preparation of TiO-2Visible light Catalyst by Vacuum Activation Method and Study on Its Longterm Efficiency[J].Journal of Zhejiang Sci-Tech University,2016,35-36(自科6):814-819.
点击复制

真空活化法制备TiO-2可见光催化剂及其长效性研究()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第35-36卷
期数:
2016年自科6期
页码:
814-819
栏目:
出版日期:
2016-11-10

文章信息/Info

Title:
Preparation of TiO-2Visible light Catalyst by Vacuum Activation Method and Study on Its Longterm Efficiency
文章编号:
1673-3851 (2016) 06-0814-06
作者:
吴三定; 王騊; 郑晋生; 俞烨; 王晟
1.浙江理工大学先进纺织材料与制备技术教育部重点实验室，杭州 310018；2.浙江宁波维科精华人丰家纺有限公司，浙江宁波 315821
Author(s):
WU Sanding;  WANG Tao;  ZHENG Jinsheng;  YU Ye;  WANG Sheng1
1. Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education, Zhejiang Sci-Tech University, Hangzhou 310018, China; 2.Zhengjiang Ningbo Weike Jinghua Renfeng Home Textile Co., Ltd, Ningbo 315821, China
关键词:
真空活化法; Ti 3+自掺杂TiO ; 可见光催化; 长效性
分类号:
O649.2
文献标志码:
A
摘要:
以商业TiO-2(Degussa P25)作为原料，采用简单的一步真空活化法制备了Ti 3+自掺杂TiO2可见光催化剂，并通过XRD、UV Vis、FT IR、XPS等手段对催化剂性能进行表征。随后，以甲基橙模拟目标污染物，在可见光下对Ti 3+自掺杂TiO-2的可见光催化性能以及长效性进行研究。结果表明：在可见光照射下，真空活化后的P25降解甲基橙的效率明显优于纯P25。循环测试结果表明：由于Ti 3+较活跃，容易被氧化，因此催化剂在可见光照射下长效性并不理想。但由于可以通过真空活化法反复对催化剂进行再生，这在一定程度上弥补了其可见光活性快速流失的缺憾。

参考文献/References:

［1］ LI X, XIONG R, WEI G. Preparation and photocatalytic activity of nanoglued Snvdoped TiO2［J］. Journal of hazardous materials,2009,164(2):587-591.
［2］ 童海霞,陈启元,胡慧萍,等.TiO2光催化活性向可见光区拓展的研究进展［J］.功能材料,2005,36(9):1307-1315.
［3］ LINSEBIGLER A, RUSU C, YATES J T. Absence of platinum enhancement of a photoreaction on TiO2CO photooxidation on Pt/TiO2(110)［J］. Journal of the American Chemical Society,1996,118(22):5284-5289.
［4］ SANCHEZ E, LOPEZ T, GOMEZ R, et al. Synthesis and characterization of solgel Pt/TiO2 catalyst［J］. Journal of Solid State Chemistry,1996,122(2):309-314.
［5］ JIMMY C. Synthesis of hierarchical nanoporous Fdoped TiO2 spheres with visible light photocatalytic activity［J］. Chemical Communications,2006(10):1115-1117.
［6］ ASAHI R, MORIKAWA T, OHWAKI T, et al. Visiblelight photocatalysis in nitrogendoped titanium oxides［J］. Science,2001,293(5528):269-271.
［7］ 刘欢,龚树萍,刘剑桥,等.钒掺杂二氧化钛薄膜制备与材料特性分析［J］.功能材料,2011,42(11):2017-2020
［8］ MORIKAWA T, ASAHI R, OHWAKI T, et al. Bandgap narrowing of titanium dioxide by nitrogen doping［J］. Japanese Journal of Applied Physics,2001,40(6A):L561.
［9］ XING M, WU Y, ZHANG J, et al. Effect of synergy on the visible light activity of B, N and Fe codoped TiO2 for the degradation of MO［J］. Nanoscale,2010,2(7):1233-1239.
［10］ XING M, ZHANG J, CHEN F. Photocatalytic performance of Ndoped TiO2 adsorbed with Fe 3+ ions under visible light by a redox treatment［J］. The Journal of Physical Chemistry C,2009,113(29):12848-12853.
［11］ LIU  G, ZHAO Y, SUN C, et al. Synergistic Effects of B/N Doping on the VisibleLight Photocatalytic Activity of Mesoporous TiO-2［J］. Angewandte Chemie International Edition,2008,47(24):4516-4520.

备注/Memo

备注/Memo:
收稿日期： 2016-01-19
基金项目： 国家自然科学基金项目（51372227，51471153）；浙江省自然科学基金项目（LY14E020011，2015C33008）;浙江理工大学“521人才培养计划”项目
作者简介： 吴三定（1992-），男，湖北鄂州人，硕士研究生，主要从事纳米材料方面的研究
通信作者： 王晟，E-mail: wangsheng571@hotmail.com
更新日期/Last Update: 2016-11-18