|本期目录/Table of Contents|

[1]薛飞,朱流,王金芳,等.化学活化诱导碳化钨化学镀镍铜磷三元合金的研究[J].浙江理工大学学报,2015,33-34(自科5):635-638.
　XUE Fei,ZHU Liu,WANG Jin fang,et al.Investigation on Ni Cu P Ternary Alloy by Wolfram Carbide ChemicalPlating Induced by Chemical Activation[J].Journal of Zhejiang Sci-Tech University,2015,33-34(自科5):635-638.
点击复制

化学活化诱导碳化钨化学镀镍铜磷三元合金的研究()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第33-34卷
期数:
2015年自科5期
页码:
635-638
栏目:
出版日期:
2015-09-10

文章信息/Info

Title:
Investigation on Ni Cu P Ternary Alloy by Wolfram Carbide ChemicalPlating Induced by Chemical Activation
文章编号:
1673-3851 (2015) 05-0635-04
作者:
薛飞;  朱流;  王金芳;  涂志标;  陈光良
1. 浙江理工大学材料与纺织学院, 杭州 310018; 2. 台州学院机械工程学院, 浙江 台州 318000
Author(s):
XUE Fei;  ZHU Liu;  WANG Jinfang;  TU Zhibiao;  CHEN Guangliang
1. School of Materials and Textiles, Zhejiang Sci-Tech University, Hangzhou 310018, China,2. College of Mechanical Engineering, Taizhou University, Taizhou 318000, China
关键词:
化学活化;  Ni Cu P;  碳化钨粉体;  化学镀
分类号:
TB333
文献标志码:
A
摘要:
采用化学活化直接对WC陶瓷粉体进行预处理,并结合低温超声辅助化学镀制备Ni Cu P三元合金包覆WC复合粉体。通过场发射扫描电子显微镜(FE SEM)和能谱仪(EDS)研究原始WC粉体、化学活化预处理WC粉体以及包覆的复合粉体表面形貌及对应的微观区域元素分布,探讨化学活化机理以及Ni Cu P三元合金沉积机理。结果表明:预处理后WC陶瓷粉体表面新生微观缺陷的化学表面,形成Ni Cu P三元合金沉积的活化中心,且Cu优先在活化中心沉积形成合金镀层内表面,Ni、P元素沉积则贯穿化学镀过程。

参考文献/References:

［1］ 姜晓霞, 沈伟. 化学镀理论及实践［M］. 北京: 国防工业出版社, 2001: 4.
［2］ 肖鑫, 秦灏, 郭贤烙, 等. 化学镀镍铜磷三元合金工艺的研究［J］. 电镀与涂饰, 2003, 22(1): 15-18.
［3］ Xu Y F, Zheng X J, Hu X G, et al. Preparation of the electroless NiP and NiCuP coatings on enginecylinder and their tribological behaviors under biooillubricated conditions［J］. Surface & CoatingsTechnology, 2014, 258: 790-796.
［4］ Abdel A A, Shehata A M. Electroless Ni Cu P plating onto open cell stainless steel foam［J］. Applied Surface Science, 2009, 255: 6652-6655.
［5］ Farzin G, Soheil G, Hassan A P. Structural and oxidation behavior of atmospheric heat treated plasma sprayed WCCo coatings［J］. Vacuum, 2013, 94: 64-68.
［6］ Espallargas N, Berget J, Guilemany J M, et al. Cr 3C 2 NiCr and WCNi thermal spray coatings as alternatives to hard chromium for erosioncorrosion resistance［J］. Surface & Coatings Technology, 2008, 202: 1405-1417.
［7］ Ishikawa Y, Kuroda S, Kawakita J, et al. Sliding wear properties of HVOF sprayed WC 20%Cr 3C 2 7%Ni cermet coatings［J］. Surface & Coatings Technology, 2007, 201: 4718-4727.
［8］ 朱流. 金属陶瓷复合粉体制备与机理及其应用研究［D］. 杭州: 浙江大学, 2006: 1-2.
［9］ 刘君, 吕珺, 王建民, 等. 粉体化学镀的研究及应用进展［J］. 金属功能材料, 2005, 12(4): 35-38.
［10］ 李宁, 袁国伟, 黎德育. 化学镀镍基合金理论与技术［M］. 哈尔滨: 哈尔滨工业大学出版社, 2000: 21-22

相似文献/References:

[1]胡普奇,朱曜峰.丝胶蛋白基多孔碳的制备及其吸波性能研究[J].浙江理工大学学报,2024,51-52(自科一):21.
　HU Puqi,ZHU Yaofeng.Preparation of silk sericin based porous carbon and  its microwave absorption property[J].Journal of Zhejiang Sci-Tech University,2024,51-52(自科5):21.

备注/Memo

备注/Memo:
收稿日期： 2014-11-14
基金项目： 浙江省自然科学基金项目(LY12E2003)
作者简介： 薛飞(1989-),男,安徽安庆人,硕士研究生,主要从事新型功能材料方面的研究
通信作者： 朱流,Email:zhuliu@tzc.edu.cn
更新日期/Last Update: 2015-09-11