Ni ZrO 2纳米复合涂层的制备及其耐磨耐蚀性能研究()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第33-34卷
期数:
2015年自科3期
页码:
336-339
栏目:
(自科)纺织与服装工程
出版日期:
2015-05-10

文章信息/Info

Title:
Preparation of Ni ZrO 2 Nano composite Coating and Study on Its Performance of Wear and Corrosion Resistance
文章编号:
1673-3851 (2015) 03-0336-04
作者:
裴旭;  易剑;  王騊
1. 浙江理工大学材料与纺织学院, 杭州 310018; 2. 台州学院机械工程学院, 浙江台州 318000
Author(s):
PEI Xu;  YI Jian;  WANG Tao
1. School of Materials and Textiles, Zhejiang Sci-Tech University, Hangzhou 310018, China;2. College of Mechanical Engineering, Taizhou University, Taizhou 318000, China
关键词:
纳米氧化锆;  45号钢;  电火花沉积;  激光熔覆;  复合涂层;  耐磨耐蚀
分类号:
TB304
文献标志码:
A
摘要:
采用电火花沉积和激光熔覆技术在45号钢基体表面沉积制备Ni ZrO 2复合涂层。通过研究涂层的显微硬度分布、耐磨和防腐性能发现:在900 W功率下,电火花沉积的Ni基过渡层质量较好,过渡层厚度达到了 110 μm 左右,且与基体冶金结合具有较高的结合力。利用激光熔覆技术在Ni基过渡层上熔覆纳米ZrO 2粉体( 3Y TZP ),纳米ZrO 2涂层平均厚度约为20 μm。Ni ZrO 2纳米复合涂层的表面平均硬度为934.19HV0.1,最高硬度可达1 145HV0.1,相对于基体,硬度提高了3.8倍。摩擦磨损和腐蚀试验发现复合涂层的耐磨性能和耐蚀性能较基体都有明显的提升。

参考文献/References:

［1］ Nikolenko S V, Pyachin S A. Burkov A A. Formation of electrospark coatings of the VK8 hard alloy with the Al 2O 3 additive［J］. Russian Journal of NonFerrous Metals, 2011, 52(1): 56-61.
［2］ Ouyang J H, Nowotny S, Richter A, et al. Laser cladding of yttria partially stabilized ZrO 2(YPSZ) ceramic coatings on aluminum alloys［J］. Ceramics International, 2001, 27(1): 15-24.
［3］ Ouyang J H, Sasaki S. Microstructure and tribological characteristics of ZrO 2 Y 2O 3 ceramic coatings deposited by laserassisted plasma hybrid spraying［J］. Tribology International, 2002, 35(4): 255-264.
［4］ 王英姿, 陶文宏, 吴波. 评价氧化铝陶瓷性能与显微结构的关系［J］. 实验技术与管理, 2002, 19(4): 51-53
［5］ Wang Jiansheng, Meng Huimin, Yu Hongying, et al. Characterization and wear behavior of WC 0 8 Co coating on cast steel rolls by electrospark deposition［J］. International Journal of Minerals, Metallurgy and Materials, 2009, 16(6): 707-713.
［6］ Norbert R, Konrad B. Performance properties of  electro spark  deposited carbideceramic coatings modified by laser beam［J］. Physics Procedia, 2010, 5(A): 417-423.
［7］ 高玉新, 赵成, 易剑. 电火花沉积NiCr合金涂层的组织及性能［J］. 材料工程, 2012(3): 74-78.
［8］ 王建升. 电火花沉积工艺及沉积层性能的研究［J］. 表面技术, 2005, 34(1): 27-30.

备注/Memo

备注/Memo:
收稿日期： 2014-09-04
作者简介： 裴旭(1990-),男,河南洛阳人,硕士研究生,主要从事新型功能材料方面的研究
通信作者： 易剑,E-mail:yj7979@tzc.edu.cn
更新日期/Last Update: 2015-05-08