|本期目录/Table of Contents|

[1]石瑞瑞,王耐艳,张梦菲,等.氧化钌/纳米石墨复合电极材料的制备及电学性能研究[J].浙江理工大学学报,2015,33-34(自科2):174-177.
　SHI Rui rui,WANG Nai yan,ZHANG Meng fei,et al.Preparation of RuO 2/nano C Composite Electrode Material and Study on Its Electrical Properties[J].Journal of Zhejiang Sci-Tech University,2015,33-34(自科2):174-177.
点击复制

氧化钌/纳米石墨复合电极材料的制备及电学性能研究()
分享到：

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第33-34卷
期数:
2015年自科2期
页码:
174-177
栏目:
(自科)纺织与服装工程
出版日期:
2015-03-10

文章信息/Info

Title:
Preparation of RuO 2/nano C Composite Electrode Material and Study on Its Electrical Properties
文章编号:
1673-3851 (2015) 02-0174-04
作者:
石瑞瑞;  王耐艳;  张梦菲;  沈国锋;  周园;  张嘉楠
浙江理工大学材料工程中心, 杭州 310018
Author(s):
SHI Rui rui;  WANG Nai yan;  ZHANG Meng fei;  SHEN Guo feng;  ZHOU Yuan;  ZHANG Jianan
Material Engineering Center, Zhejiang Sci-Tech University, Hangzhou 310018, China
关键词:
氧化钌;  纳米石墨;  超级电容器;  电学性能
分类号:
TM53
文献标志码:
A
摘要:
以纳米石墨为基体,通过乙醇钌水解、过饱和非均相沉淀获得纳米级RuO 2,并包覆沉积于石墨表面,制备新型纳米RuO 2/nano C复合电极材料。X射线衍射(XRD)、透射电子显微镜(TEM)和能谱(EDS)分析表明:醇钌盐水解后生成的氧化钌主要是以非晶态RuO 2· x H 2O的形式包覆在纳米石墨上。循环伏安曲线测试表明:复合电〖JP2〗极材料在充放电过程中包含了碳双电层的储电机理和氧化钌氧化还原反应的储电机理,乙醇钌浓度为0.12 mol·L -1 的比容量为314 F·g -1。

参考文献/References:

［1］ 邵强, 林正峰, 刘庆琪, 等. 二氧化钌/石墨烯复合材料超级电容器的性能［J］. 微纳电子技术, 2013, 50(6): 347-359.
［2］ 王晓峰, 孔祥华, 刘庆国, 等. 氧化钌/活性炭超级电容器电极材料电化学特性［J］. 电子元件与材料, 2002, 21(3): 1-4.
［3］ Naoi K, Ishimoto S, Ogihara N, et al. Encapsulation of nanodot ruthenium oxide into KB for electrochemical capacitors［J］. J Electrochem Soc, 2009, 156(1): A52-A59.
［4］ Zheng J P, Cygan P J, Jow T R. Hydrous ruthenium oxide as an electrode material for electrochemical capacitors［J］. J Electrochem Soc, 1995, 142(8): 2699-2703.
［5］ 刘泓, 甘卫平, 郑峰, 等. 超级电容器用羧基氧化钌薄膜的充放电性能［J］. 粉末冶金材料科学与工程, 2011, 16(3): 431-436.
［6］ Cheng G H, Yang H, Liang H D, et al. Preparation of nanopowders TiO2 by hydrolysisprecipitation of Titanium alkoxide［J］. Rare Metal Materials and Engineering, 2010, 39(2): 69-72.
［7］ He  X J, Geng Y J, Oke S, et al. Electrochemical performance of RuO x /activated carbon black composite for supercapacitors［J］. Synthetic Metals, 2009, 159: 7-12
［8］ Mitra S, Lokesh K S, Sampath S. Exfoliated graphite ruthenium oxide composite electrodes for electrochemical supercapacitors［J］. Journal of Power Sources, 2008, 185: 1544-1549.
［9］ Kim H, Branko P N. Characterization of hydrous ruthenium oxide/carbon nanocomposite supercapacitors prepared by a colloidal method［J］. Journal of Power Sources, 2002, 104: 52-61.
［10］ 周颖, 姜磊, 阎景旺, 等. 石墨烯纸的制备及电容特性［J］. 高等学校化学学报, 2014, 35 (3): 619-625.
［11］ 孙旭东, 周明, 秦禄昌. 石墨烯结构与德拜温度因子的电子衍射分析［J］. 电子显微学报, 2013, 32(3): 206-210.
［12］ Liu, X M, Zhang X G. NiObased composite electrode with RuO2 for electrochemical capacitors［J］. Electrochimica Acta, 2004, 49(2): 229-232.

备注/Memo

备注/Memo:
收稿日期： 2014-05-23
基金项目： 浙江省新苗人才计划(2013R406051)
作者简介： 石瑞瑞(1989-),男,山东东营人,硕士研究生,主要从事超级电容器电极材料方面的研究
通信作者： 王耐艳,E-mail:wangnaiyan@zstu.edu.cn
更新日期/Last Update: 2015-03-23