[1]曾红春,杨静静,张晨纯,等.电化学沉积法制备Gd 2O 3∶Eu 3+薄膜的发光特性研究[J].浙江理工大学学报,2013,30(03):308-311.
 ZENG Hong chun,YANG Jing jing,ZHANG Chen chun,et al.Study on Characteristics of Luminescence of Gd 2O 3∶Eu 3+ Thin Film Prepared with Electrochemical Deposition Method[J].Journal of Zhejiang Sci-Tech University,2013,30(03):308-311.
点击复制

电化学沉积法制备Gd 2O 3∶Eu 3+薄膜的发光特性研究()
分享到:

浙江理工大学学报[ISSN:1673-3851/CN:33-1338/TS]

卷:
第30卷
期数:
2013年03期
页码:
308-311
栏目:
(自科)纺织与服装工程
出版日期:
2013-05-10

文章信息/Info

Title:
Study on Characteristics of Luminescence of Gd 2O 3∶Eu 3+ Thin Film Prepared with Electrochemical Deposition Method
文章编号:
16733851 (2013) 03030804
作者:
曾红春 杨静静 张晨纯 张雪 石瑞瑞
浙江理工大学材料工程中心, 杭州 310018
Author(s):
ZENG Hongchun YANG Jingjing ZHANG Chenchun ZHANG Xue SHI Ruirui
College of Materials and Textiles, Zhejiang SciTech University, Hangzhou 310018, China
关键词:
Gd 2O 3∶Eu 3+薄膜 稀土掺杂 电化学沉积 发光特性
分类号:
TB34
文献标志码:
A
摘要:
采用电化学沉积法制备Gd 2O 3∶Eu 3+荧光薄膜,通过调节Eu 3+ 离子掺杂浓度来探究具有最佳发光效果的薄膜,利用XRD、SEM,PL光谱和EDS测试分析该种材料的物相构成及表面形貌。结果显示:电化学沉积法制备的薄膜结晶效果好,具有立方晶体结构,掺杂离子Eu 3+离子均匀地分布在薄膜中;制备出的荧光薄膜有良好的发光强度,当Gd(NO 3) 3·6H2O与Eu(NO 3) 3·6H 2O的体积比为10∶1时发光强度最大,但当Eu 3+离子掺杂浓度过大时,会出现荧光淬灭现象,电化学沉积法可以制备出具有良好发光性能的荧光薄膜。

参考文献/References:

[1] Hiwo J G, Park S H, Jang J E. Synthesis and modification of red oxide phosphors for low voltage excitation[J]. Journal of Vacuum Science and Technology B: Microelectronics and Nanometer Structures, 2000, 18: 1101-1105.[2] Schmechel  R, Kennedy M, Seggern H V, et al. Luminescence properties of nanocrystalline Y 2O 3∶Eu 3+  in different host materials[J]. J Appl Phys, 2001, 89(3): 1679-1686.
[3] Wakefield G, Holland E, Dobson P J. Luminescence properties of nanocrystalline Y 2O 3∶Eu 3+[J]. Adv Mater, 2001, 13(20): 1557-1560.
[4] Bartk A P O, Peyser L A, Dickson R M, et al. Observation of dipolar emission patterns from isolated Eu 3+ : Y 2O 3 doped nanocrystals new evidence for single ion luminescence[J]. Chem Phys Lett, 2002, 358(6): 459-465.
[5] Scholl  M S, Trimmer J R, Luminescence of YAG: Tm, Tb[J]. J Electrochem Soc, 1986, 133(3): 643-648.
[6] Sivakumar V, Varadaraju U V. Intense redemitting phosphors for white light emitting diodes[J]. J Electrochem Soc, 2005, 152(10): H168-H171.
[7] 李德杰. 大屏幕场助热电子发射平板显示[J]. 真空电子技术, 2002(6): 1-5.
[8] Lin J, Saenger D U, Mennig M, et al. Sol gel deposition and characterization of Mn 2+-doped silicate phosphor films[J]. Thin Solid Films, 2000, 360(1/2): 39-45.
[9] Hirata G A, Mckittrick J. Physical properties of Y 2O 3∶Eu 3+ luminescent films grown by MOCVD and laser ablation[J]. Appl Surf, 1997, 113/114: 509-514.
[10]Cho K G, Kumar D. Luminescence behavior of pulsed deposited Eu 3+: Y2O3 thin film phosphors on sapphire substrates[J]. Appl Phys Lett, 1998, 73(21): 3058-3060.
[11] Esparza A, Garcia M, Falcony C. Structural and photoluminescent characteristics of yttriumaluminum oxide films doped with Tb, Eu or Ce[J]. Thin Solid Films, 1998, 325: 14-18.
[12] 刘行仁. 显示器用的荧光粉的进展[J]. 液晶与显示, 1996(3): 61-64.
[13] 符连社, 张洪杰, 邵 华. 溶胶—凝胶法稀土光学材料研究进展[J]. 稀土, 1998, 19(2): 49, 53.
[14] Tang W, Cameron D C. Electroluminescent zinc sulphide devices produced by solgel processing[J]. Thin Solid Films, 1996, 280: 221-226.
[15] Qi Z, Shi C, ZhangW. Local structure and luminescence of nanocrystalline Y2O3∶Eu[J]. Appl Phys Lett, 2002, 81(8): 2857-2859.

相似文献/References:

[1]史凌云,廖娜,贾红,等. 电化学沉积法制备稀土掺杂氧化钇荧光薄膜的发光性能[J].浙江理工大学学报,2011,28(04):563.
 SHI Ling yun,LIAO Na,JIA Hong,et al. Study on the Photoluminescence Properties of Y2O3: Ln(Ln=Er3+, Ce3+, Sm3+, Pr3+) Thin Film Phosphors Prepared by ElectroDeposition Method[J].Journal of Zhejiang Sci-Tech University,2011,28(03):563.

备注/Memo

备注/Memo:
收稿日期: 2012-12-03
作者简介: 曾红春(1984-),男,江西宁都人,硕士研究生,主要从事稀土发光材料研究。
更新日期/Last Update: